Method for manufacturing a laminated layered printed wiring board using a sulfuroxy acid and an oxiding treatment of the metallic wiring patterns to insure the integrity of the laminate product
Assignee: MC GEAN-ROHCO Inc
•
Filing: 1986-06-02
•
Granted: 1987-10-27
•
Expires: 2006-06-02
Abstract
Abstract A sulfuroxy acid reducing agent composition can be used to treat the metallic conductive pathways formed in or on the surface of printed wiring boards in order to assure that the copper pathways are firmly and securely bonded to laminate layers of layered printed wiring board articles. The sulfuroxy acid reducing agent treatment promotes the rapid formation of a uniform metal oxide layer on the printed wiring board conductive pathways, when the printed circuit boards are exposed to an oxiding agent, which insures that the compositions used in forming the printed wiring board laminates do not interact with the active copper metal preventing delamination.
Inventors
- 👤 Greg D. Garlough
- 👤 Kurt E. Heikkila
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:51
CPC Classifications
C; C23; C23C; C23C22/00; C23C22/05; C23C22/60; C23C22/63; H; H05; H05K; H05K3/00; H05K3/38; H05K3/382; H05K3/385; H05K2203/00; H05K2203/03; H05K2203/0315; H05K3/02; H05K3/022; H05K3/025; H05K3/10; H05K3/20; H05K3/46; H05K3/4611
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
133 words
A method for the manufacture of laminated or layered printed wiring boards that resist delamination caused by an interaction between a metal pattern and a printed wiring board substrate during manufacture and use which comprises: (a) preparing a metallic foil printed circuit pattern; (b) contacting at least one surface of the metallic printed circuit pattern with an aqueous solution of an effective concentration of a sulfuroxy acid compound to promote the rapid formation of a uniform metal oxide coating, forming a sulfuroxy acid treated metal pattern; (c) contacting the sulfuroxy acid treated metal pattern with an effective amount of an aqueous oxiding agent to form a uniform metal oxide conversion coating on the metallic wiring pattern; and (d) laminating the metallic pattern with the metal oxide coating with at least one substrate layer.
Claim 2
Independent Claim
133 words
A method for the manufacture of laminated or layered printed wiring boards that resist delamination caused by an interaction between a metal pattern and a printed wiring board substrate during manufacture and use which comprises: (a) preparing a metallic foil printed circuit pattern; (b) contacting at least one surface of the metallic printed circuit pattern with an aqueous solution of an effective concentration of a sulfuroxy acid compound to promote the rapid formation of a uniform metal oxide coating, forming a sulfuroxy acid treated metal pattern; (c) contacting the sulfuroxy acid treated metal pattern with an effective amount of an aqueous oxiding agent to form a uniform metal oxide conversion coating on the metallic wiring pattern; and (d) laminating the metallic pattern with the metal oxide coating with at least one substrate layer.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein the sulfuroxy acid compound comprises a thiosulfate compound, a dithionite compound, a trithionate compound, a tetrathionate compound, or mixtures thereof.
Claim 4
Dependent Claim
25 words
The method of claim 2 wherein the thiosulfate compound comprises an alkali metal thiosulfate at a concentration of about 5 to 750 grams per liter.
Claim 5
Dependent Claim
24 words
The method of claim 3 wherein the alkali metal thiosulfate comprises sodium thiosulfate at a concentration of about 10 to 200 grams per liter.
Claim 6
Dependent Claim
14 words
The method of claim 1 wherein the metallic wiring patterns comprise copper wiring patterns.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein the oxiding agent comprises an aqueous solution of an alkali metal chlorite and an alkali metal hydroxide.
Claim 8
Dependent Claim
33 words
The method of claim 5 wherein prior to contacting the copper printed wiring pattern with the sulfuroxy acid compound, a chemical etchant is used to remove the layer of copper from the pattern.
Claim 9
Dependent Claim
30 words
The method of claim 6 wherein the oxiding agent comprises about 25 to less than 100 grams of sodium chlorite and 10 to 40 grams of sodium hydroxide per liter.
Claim 10
Dependent Claim
196 words
A process for preparing a laminated printed wiring board having at least two layers that resists delamination during manufacture which can be caused by an interaction between a copper wiring board pattern and a printed wiring board substrate during manufacture and use which comprises: (a) on a stainless steel mandrel forming a copper layer having a thickness of less than about 2 mil; (b) forming a layer of a photosensitive photoresist composition on the copper layer; (c) chemically forming an etched pattern in the photoresist; (d) forming a copper printed wiring circuit in the etched pattern in the photoresist; (e) contacting the copper printed wiring circuit in the photoresist with a sulfuroxy acid compound to form a treated circuit; (f) contacting the treated circuit with an oxiding agent to form an inert copper oxide layer; (g) forming an organic substrate in contact with the inert copper oxide layer to form a printed wiring board; (h) removing the printed wiring board from the mandrel at the interface between the first copper layer and the mandrel; and (i) removing the first copper layer by chemical etching and laminating the printed wiring board with at least one other board.
Claim 11
Dependent Claim
196 words
A process for preparing a laminated printed wiring board having at least two layers that resists delamination during manufacture which can be caused by an interaction between a copper wiring board pattern and a printed wiring board substrate during manufacture and use which comprises: (a) on a stainless steel mandrel forming a copper layer having a thickness of less than about 2 mil; (b) forming a layer of a photosensitive photoresist composition on the copper layer; (c) chemically forming an etched pattern in the photoresist; (d) forming a copper printed wiring circuit in the etched pattern in the photoresist; (e) contacting the copper printed wiring circuit in the photoresist with a sulfuroxy acid compound to form a treated circuit; (f) contacting the treated circuit with an oxiding agent to form an inert copper oxide layer; (g) forming an organic substrate in contact with the inert copper oxide layer to form a printed wiring board; (h) removing the printed wiring board from the mandrel at the interface between the first copper layer and the mandrel; and (i) removing the first copper layer by chemical etching and laminating the printed wiring board with at least one other board.
Claim 12
Dependent Claim
26 words
The method of claim 9 wherein the sulfuroxy acid compound comprises a thiosulfate compound, a dithionate compound, a trithionate compound, a tetrathionate compound or mixtures thereof.
Claim 13
Dependent Claim
25 words
The method of claim 10 wherein the thiosulfate compound comprises an alkali metal thiosulfate at a concentration of about 5 to 750 grams per liter.
Claim 14
Dependent Claim
24 words
The process of claim 11 wherein the alkali metal thiosulfate comprises sodium thiosulfate having a concentration of about 10 to 200 grams per liter.
Claim 15
Dependent Claim
23 words
The process of claim 9 wherein the oxiding agent comprises an aqueous solution of an alkali metal chlorite and an alkali metal hydroxide.
References Cited (Backward Citations)
US2364993A
Cited
US2460896A
Cited
US2460898A
Cited
US2481854A
Cited
US2964436A
Cited
US3137600A
Cited
US3293109A
Cited
US3434889A
Cited
US3455775A
Cited
US3544389A
Cited
US3657023A
Cited
US3677828A
Cited
US4063984A
Cited
US4411710A
Cited
US4409037A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-26 | 1991-04-27 | 1991-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-26 | 1995-04-27 | 1995-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-26 | 1999-04-27 | 1999-10-27 | $7700.00 | Window Closed / Lapsed |