Opaque polymer film laminate having an absorbent surface

Claim 2

An oriented, opaque polymer film laminate which comprises: (a) a non-absorbent thermoplastic polymer core layer having an upper major surface and a lower major surface; and, (b) a liquid-absorbent, opaque surface layer adherently applied to the upper major surface of the core layer and, optionally, to the lower major surface of the core layer, said surface layer comprising a thermoplastic matrix polymer containing numerous opaquing voids, said voids containing one or more void-intiating particles derives from a material which is phase distinct from, and incompatible with, the matrix material, there being present in said surface layer filler particles having a particle size from about 1 to about 15 microns as measured along the greatest dimension, said particles increasing the absorbency of surface layer(s).

Claim 3

The polymer film laminate of claim 1 wherein the polymer of core layer (a) is an isotactic polypropylene.

Claim 4

The polymer film laminate of claim 1 wherein the matrix polymer of surface layer(s)(b) is an isotactic polypropylene.

Claim 5

The polymer film laminate of claim 2 wherein the the matrix polymer of surface layer(s)(b) is an isotactic polypropylene.

Claim 6

The polymer film laminate of claim 1 wherein the void-initiating particles are spheroidal in shape, range in average size of from bout 0.1 to about 10 microns and are derived from inorganic or organic material

Claim 7

The polymer film laminate of claim 5 wherein the spheroidal void-initiating particles are pre-formed and are derived from an inorganic material.

Claim 8

The polymer film laminate of claim 6 wherein the pre-formed, spheroidal, inorganic void-initiating particles are solid or hollow glass, ceramic or metal spheres or beads.

Claim 9

The polymer film laminate of claim 5 wherein the spheroidal void-initiating particles are pre-formed or formed in situ and are derived from an organic polymer material.

Claim 10

The polymer film laminate of claim 8 wherein the organic polymer material is a polyamide.

Claim 11

The polymer film of claim 1 wherein the film is coextruded and biaxially oriented, the polymer of the core layer is isotactic polypropylene, the thermoplastic matrix polymer of surface layer(s) is isotactic polypropylene and the void-initiating particles are spheroidal in shape, range in average size of from about 0.1 to about 10 microns and are derived from a polyamide.

Claim 12

The polymer film of claim 1 wherein a liquid is absorbed on the exposed surface of a surface layer.

Claim 13

The polymer film of claim 11 wherein said liquid contains water, an oil, a water soluble component, an oil soluble component or mixture of two or more of the foregoing.

Claim 14

The polymer film of claim 12 wherein said liquid is a solution, suspension, emulsion, dispersion or latex.

Claim 15

The polymer film of claim 13 wherein said liquid is a water based adhesive or ink.

Claim 16

A process for producing an oriented, opaque polymer film laminate which comprises: (a) providing a non-absorbent thermoplastic core layer having an upper major surface and lower major surface; (b) providing a surface layer by: (i) mixing a thermoplastic matrix polymer material with a void-initiating material which is phase distinct from, and incompatible with, the matrix polymer material and which possesses a melting point or glass transition temperature which is higher than the melting point or glass transition temperature of the matrix polymer material, (ii) heating the mixture of matrix polymer material and void-initiating material to a temperature which is at or above the melting point of the matrix polymer material, (iii) distributing the void-initiating material throughout the molten matrix polymer material in the form of microparticles, and (iv) forming the microparticle-containing matrix polymer material into said surface layer; (c) adherently applying the surface layer to the upper major surface of the core layer and, optionally, to the lower major surface of the core layer, to provide a polymer film laminate; and, (d) biaxially orienting the polymer film laminate at a temperature which is signifiantly greater than the glass transition temperature of the thermoplastic polymer matrix material of the surface layer, to form numerous opaquing voids in the surface layer(s) thereof, at least a portion of said voids becoming open during orienting so as to impart liquid-absorbent capability to the surfae layer(s).

Claim 17

A process for producing an oriented, opaque polymer film laminate which comprises: (a) providing a non-absorbent thermoplastic core layer having an upper major surface and lower major surface; (b) providing a surface layer by: (i) mixing a thermoplastic matrix polymer material with a void-initiating material which is phase distinct from, and incompatible with, the matrix polymer material and which possesses a melting point or glass transition temperature which is higher than the melting point or glass transition temperature of the matrix polymer material, (ii) heating the mixture of matrix polymer material and void-initiating material to a temperature which is at or above the melting point of the matrix polymer material, (iii) distributing the void-initiating material throughout the molten matrix polymer material in the form of microparticles, and (iv) forming the microparticle-containing matrix polymer material into said surface layer; (c) adherently applying the surface layer to the upper major surface of the core layer and, optionally, to the lower major surface of the core layer, to provide a polymer film laminate; and, (d) biaxially orienting the polymer film laminate at a temperature which is signifiantly greater than the glass transition temperature of the thermoplastic polymer matrix material of the surface layer, to form numerous opaquing voids in the surface layer(s) thereof, at least a portion of said voids becoming open during orienting so as to impart liquid-absorbent capability to the surfae layer(s).

Claim 18

The process of claim 15 wherein the polymer of core layer (a) is an isotactic polypropylene.

Claim 19

The process of claim 15 wherein the matrix polymer of surface layer(s)(b) is an isotactic polypropylene.

Claim 20

The process of claim 16 wherein the matrix polymer of surface layer(s)(b) is an isotactic polypropylene.

Claim 21

The process of claim 15 wherein the void-initiating particles are spheroidal in shape, range in average size of from about 0.1 to about 10 microns and are derived from inorganic or organic material.

Claim 22

The process of claim 19 wherein the spheroidal void-initiating particles are pre-formed and are derived from an inorganic material.

Claim 23

The process of claim 20 wherein the pre-formed, spheroidal, inorganic void-initiating particles are solid or hollow glass, ceramic or metal spheres or beads.

Claim 24

The process of claim 19 wherein the spheroidal void-initiating particles are pre-formed or formed in situ and are derived from an organic polymer material.

Claim 25

The process of claim 22 wherein the organic polymer material is a polyamide.

Claim 26

The process of claim 15 wherein the conditions of step (d) are such that a minor amount of void splitting and/or fibrillation providing enhanced absorbency results.

Claim 27

The polymer film of claim 15 wherein the film is coextruded and biaxially oriented, the polymer of the core layer is isotactic polypropylene, the thermoplastic matrix polymer of surface layer(s) is isotactic polypropylene and the void-initiating particles are spheroidal in shape, range in average size of from about 0.1 to about 10 microns and are derived from a polyamide.

Claim 28

The process of claim 15 wherein a liquid is absorbed on the exposed surface of a surface layer.

Claim 29

The process of claim 26 wherein said liquid contains water, an oil, a water soluble component, an oil soluble component or mixture of two or more of the foregoing.

Claim 30

The process of claim 27 wherein said liquid is a solution, suspension, emulsion, dispersion or latex.

Claim 31

The process of claim 28 wherein said liquid is a water based adhesive or ink.

Claim 32

An oreinted, opaque polymer film laminate which comprises: (a) a non-absorbent thermoplastic polymer core layer having an upper major surface and a lower major surface; and, (b) a liquid-absorbent, opaque surface layer adherently applied to the upper major surface of the core layer, and optionally, to the lower major surface of the core layer, said surface layer comprising a thermoplastic matrix polymer containing numerous opaquing voids, said voids containing one or more void-initiating particles derived from a material which is phase distinct from, and incompatible with, the matrix material, there being present in said surface layer filler particles provided as rods, fibers or filaments which increase the absorbency of the surface layers.

Claim 33

An oreinted, opaque polymer film laminate which comprises: (a) a non-absorbent thermoplastic polymer core layer having an upper major surface and a lower major surface; and, (b) a liquid-absorbent, opaque surface layer adherently applied to the upper major surface of the core layer, and optionally, to the lower major surface of the core layer, said surface layer comprising a thermoplastic matrix polymer containing numerous opaquing voids, said voids containing one or more void-initiating particles derived from a material which is phase distinct from, and incompatible with, the matrix material, there being present in said surface layer filler particles provided as rods, fibers or filaments which increase the absorbency of the surface layers.

Claim 34

A process for producing an oriented, opaque polymer film laminate which comprises: (a) providing a non-absorbent thermoplastic core layer having an upper major surface and lower major surface; (b) providing a surface layer by: (i) mixing a thermoplastic matrix polymer material with a void-initiating material which is phase distinct from, and incompatible with, the matrix polymer material and which possesses a melting point or glass transition temperature which is higher than the melting point or glass transition temperature of the matrix polymer material, (ii) heating the mixture of matrix polymer material and void-initiating material to a temperature which is at or above the melting point of the matrix polymer material, (iii) distributing the void-initiating material throughout the molten matrix polymer material in the form of microparticles, and (iv) forming the microparticle-containing matrix polymer material into said surface layer; said surface including a minor amount of filler particles provided as rods, fibers or filaments, to enhance the absorbency of said surface layer(s); (c) adherently applying the surface layer to the upper major surface of the core layer and, optionally, to the lower major surface of the core layer, to provide a polymer film laminate; and, (d) biaxially orienting the polymer film laminate under selected temperature conditions to avoid excessive incidence of void splitting and/or film fibrillation, to form numerous opaquing voids in the surface layer(s) thereof, at least a portion of said voids becoming open during orienting so as to impart liquid-absorbent capability to the surface layer(s).

Claim 35

A process for producing an oriented, opaque polymer film laminate which comprises: (a) providing a non-absorbent thermoplastic core layer having an upper major surface and lower major surface; (b) providing a surface layer by: (i) mixing a thermoplastic matrix polymer material with a void-initiating material which is phase distinct from, and incompatible with, the matrix polymer material and which possesses a melting point or glass transition temperature which is higher than the melting point or glass transition temperature of the matrix polymer material, (ii) heating the mixture of matrix polymer material and void-initiating material to a temperature which is at or above the melting point of the matrix polymer material, (iii) distributing the void-initiating material throughout the molten matrix polymer material in the form of microparticles, and (iv) forming the microparticle-containing matrix polymer material into said surface layer; said surface including a minor amount of filler particles provided as rods, fibers or filaments, to enhance the absorbency of said surface layer(s); (c) adherently applying the surface layer to the upper major surface of the core layer and, optionally, to the lower major surface of the core layer, to provide a polymer film laminate; and, (d) biaxially orienting the polymer film laminate under selected temperature conditions to avoid excessive incidence of void splitting and/or film fibrillation, to form numerous opaquing voids in the surface layer(s) thereof, at least a portion of said voids becoming open during orienting so as to impart liquid-absorbent capability to the surface layer(s).