US4701352A — Surface preparation of ceramic substrates for met…

Claim 1

Independent Claim 165 words

In a process for metallizing a surface of a ceramic substrate which includes adhesion promoting the surface with an alkali metal composition containing one or more alkali metal compounds and subsequently depositing metal on the adhesion promoted surface, the improvement which comprises: providing said alkali metal compound(s) in the form of one or more discrete solid shapes sized 25 mg to about 500 mg contacting the ceramic surface with a quantity of the solid shapes which when molten will spread across and uniformly wet the ceramic surface; heating the alkali metal composition and the substrate for a time period and at or above a temperature at which the alkali metal composition becomes molten in situ on the ceramic surface, spreading out and uniformly wetting the ceramic surface and which is sufficient to adhesion promote the ceramic surface, and render it receptive to subsequent adherent metal deposition; and in a later step, plating an adherent metal layer on the treated ceramic surface or selected parts thereof.

Claim 2

Dependent Claim 165 words

In a process for metallizing a surface of a ceramic substrate which includes adhesion promoting the surface with an alkali metal composition containing one or more alkali metal compounds and subsequently depositing metal on the adhesion promoted surface, the improvement which comprises: providing said alkali metal compound(s) in the form of one or more discrete solid shapes sized 25 mg to about 500 mg contacting the ceramic surface with a quantity of the solid shapes which when molten will spread across and uniformly wet the ceramic surface; heating the alkali metal composition and the substrate for a time period and at or above a temperature at which the alkali metal composition becomes molten in situ on the ceramic surface, spreading out and uniformly wetting the ceramic surface and which is sufficient to adhesion promote the ceramic surface, and render it receptive to subsequent adherent metal deposition; and in a later step, plating an adherent metal layer on the treated ceramic surface or selected parts thereof.

Claim 3

Dependent Claim 100 words

The process of claim 1, further including, after adhesion promoting said ceramic surface and before forming said metal layer thereon, the step of exposing said surface to an acidic halide solution containing one or more halides selected from the group consisting of chloridies, bromides and iodides in an amount greater than 0.5 moles halide per liter and sufficient to promote adsorption of catalyst on the surface and eliminate bare spots in an adherent metal layer formed on the surface or selected parts thereof; and treating said surface with a catalyst solution for rendering said surface receptive to deposition of metal.

Claim 4

Dependent Claim 116 words

The process of claim 1, further including, after adhesion promoting said ceramic surface and before forming said metal layer thereon, the step of exposing said surface to an adsorption promoter selected from the group consisting of ethoxylated non-ionic compounds and nitrogen-containing compounds, said nitrogen-containing compounds being selected from the group consisting of quaternary compounds, amine oxides, alkanolamines, amides, betaines, amino acids and guanidine derivatives, in an amount sufficient to, and at a pH which will promote adsorption of catalyst on the surface and eliminate bare spots in an adherent metal layer formed on the surface or selected parts thereof; and treating said surface with a catalyst solution for rendering said surface receptive to deposition of metal.

Claim 5

Dependent Claim 21 words

The process of claim 1, wherein a multiplicity of said shapes are distributed on the ceramic surface in a preselected pattern.

Claim 6

Dependent Claim 17 words

The process of claim 1, wherein the alkali metal compound is present in the form of pellets.

Claim 7

Dependent Claim 25 words

The process of claim 1, wherein the solid shapes each have a mass in the anhydrous state between about 50 mg and about 500 mg.

Claim 8

Dependent Claim 24 words

The process of claim 6, wherein the solid shapes each have a mass in the anhydrous state between about 100 mg and 350 mg.

Claim 9

Dependent Claim 27 words

The process of claim 7, wherein the solid shapes are hemispheres and each has a mass in the anhydrous state between about 150 mg and 200 mg.

Claim 10

Dependent Claim 13 words

A process of claim 1, wherein the alkali metal compound is sodium hydroxide.

Claim 11

Dependent Claim 27 words

The process of claim 1, wherein the alkali metal composition and the ceramic substrate are heated to a temperature between about 450° C. and about 700° C.

Claim 12

Dependent Claim 32 words

The process of claim 1, wherein the ceramic substrate is alumina, and the alumina and the alkali metal composition are heated at a temperature between about 450° C. and about 650° C.

Claim 13

Dependent Claim 35 words

The process of claim 1, wherein the total weight of alkali metal composition shapes applied to the ceramic surface is at least about 0.1 mg of alkali metal composition per square millimeter of ceramic surface.

Claim 14

Dependent Claim 37 words

The process of claim 1, wherein the total weight of alkali metal composition shapes applied to the ceramic surface is between about 0.1 and about 0.4 mg of alkali metal composition per square millimeter of ceramic surface.

Claim 15

Dependent Claim 24 words

The process of claim 1, wherein the alkali metal composition and the substrate are heated for a time period between 5 and 20 minutes.

Claim 16

Dependent Claim 15 words

The process of claim 14, wherein the time period is between 7 and 10 minutes.

Claim 17

Dependent Claim 181 words

In a process for metallizing a surface of a ceramic substrate which includes adhesion promoting the surface with an alkali metal composition containing one or more alkali metal compounds and subsequently depositing metal on the adhesion promoted surface, the improvement which comprises: providing said alkali metal compound(s) in the form of a multiplicity of discrete solid pellets, each pellet having a mass between 150 mg and 200 mg; contacting the ceramic surface with a quantity of said alkali metal composition which when molten will spread across and uniformly wet the ceramic surface; heating the alkali metal composition and the substrate for a time period between 5 to 20 minutes at a temperature between about 450° C. and about 700° C. to melt the pellets in situ on the ceramic surface, the melting pellets spreading out and uniformly wetting the ceramic surface, said time and temperature being sufficient to adhesion promote the ceramic surface and render it receptive to subsequent adherent metal deposition, and in a later step plating an adherent metal layer on the treated ceramic surface or selected parts thereof.

Claim 18

Dependent Claim 181 words

In a process for metallizing a surface of a ceramic substrate which includes adhesion promoting the surface with an alkali metal composition containing one or more alkali metal compounds and subsequently depositing metal on the adhesion promoted surface, the improvement which comprises: providing said alkali metal compound(s) in the form of a multiplicity of discrete solid pellets, each pellet having a mass between 150 mg and 200 mg; contacting the ceramic surface with a quantity of said alkali metal composition which when molten will spread across and uniformly wet the ceramic surface; heating the alkali metal composition and the substrate for a time period between 5 to 20 minutes at a temperature between about 450° C. and about 700° C. to melt the pellets in situ on the ceramic surface, the melting pellets spreading out and uniformly wetting the ceramic surface, said time and temperature being sufficient to adhesion promote the ceramic surface and render it receptive to subsequent adherent metal deposition, and in a later step plating an adherent metal layer on the treated ceramic surface or selected parts thereof.

Claim 19

Dependent Claim 175 words

A process for producing a printed circuit on a surface of a ceramic substrate comprising: (a) contacting the ceramic surface with an alkali metal composition comprised of an alkali metal compound in the form of a multiplicity of discrete solid shapes sized 25 mg to about 500 mg, each shape having a preselected mass, said shapes being present in a quantity which when molten will spread across and uniformly wet the ceramic surface; (b) heating the alkali metal composition and the substrate for a time period and at or above a temperature at which the alkali metal composition becomes molten in situ on the ceramic surface, spreading out and uniformly wetting the ceramic surface, and which is sufficient to adhesion promote the ceramic surface and render it receptive to subsequent adherent metal deposition (c) treating the ceramic surface to activate it for electroless metal deposition; (d) depositing metal onto the activated surface; (e) removing portions of the deposited metal to produce a metal printed circuit conductor pattern adhering to the surface of the ceramic substrate.

Claim 20

Dependent Claim 175 words

A process for producing a printed circuit on a surface of a ceramic substrate comprising: (a) contacting the ceramic surface with an alkali metal composition comprised of an alkali metal compound in the form of a multiplicity of discrete solid shapes sized 25 mg to about 500 mg, each shape having a preselected mass, said shapes being present in a quantity which when molten will spread across and uniformly wet the ceramic surface; (b) heating the alkali metal composition and the substrate for a time period and at or above a temperature at which the alkali metal composition becomes molten in situ on the ceramic surface, spreading out and uniformly wetting the ceramic surface, and which is sufficient to adhesion promote the ceramic surface and render it receptive to subsequent adherent metal deposition (c) treating the ceramic surface to activate it for electroless metal deposition; (d) depositing metal onto the activated surface; (e) removing portions of the deposited metal to produce a metal printed circuit conductor pattern adhering to the surface of the ceramic substrate.

Claim 21

Dependent Claim 204 words

The process for producing a metallized conductor pattern on a surface of a ceramic substrate having a surface roughness less than about 0.7 micrometers, the process comprising: contacting the surface with an alkali metal composition comprised of one or more alkali metal compounds in the form of a multiplicity of discrete solid shapessized 25 mg to about 500 mg, said shapes being present in a quantity which when molten will spread across and uniformly wet the ceramic surface; heating the alkali metal composition and the substrate for a time period and at or above a temperature at which the alkali metal composition becomes molten in situ on the ceramic surface, spreading out and uniformly wetting the ceramic surface, and which is sufficient to adhesion promote the ceramic surface and render it receptive to subsequent adherent metal deposition; rinsing said surface with an aqueous solution; neutralizing said ceramic surface with an acid; repeating said rinsing step; contacting said ceramic surface with an activator solution providing stannous tin ions and precious metal ions, to activate said surface for electroless metal deposition; and contacting said activated surface or selected parts thereof with a metal depositing solution for a time period sufficient to form a metal layer thereon.

Claim 22

Dependent Claim 204 words

The process for producing a metallized conductor pattern on a surface of a ceramic substrate having a surface roughness less than about 0.7 micrometers, the process comprising: contacting the surface with an alkali metal composition comprised of one or more alkali metal compounds in the form of a multiplicity of discrete solid shapessized 25 mg to about 500 mg, said shapes being present in a quantity which when molten will spread across and uniformly wet the ceramic surface; heating the alkali metal composition and the substrate for a time period and at or above a temperature at which the alkali metal composition becomes molten in situ on the ceramic surface, spreading out and uniformly wetting the ceramic surface, and which is sufficient to adhesion promote the ceramic surface and render it receptive to subsequent adherent metal deposition; rinsing said surface with an aqueous solution; neutralizing said ceramic surface with an acid; repeating said rinsing step; contacting said ceramic surface with an activator solution providing stannous tin ions and precious metal ions, to activate said surface for electroless metal deposition; and contacting said activated surface or selected parts thereof with a metal depositing solution for a time period sufficient to form a metal layer thereon.

Claim 23

Dependent Claim 27 words

The process of claim 2 wherein said acid halide solution constitutes part of said catalyst solution used for rendering said ceramic surface receptive to deposition of metal.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1990-10-19	1991-04-20	1991-10-20	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1994-10-19	1995-04-20	1995-10-20	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1998-10-19	1999-04-20	1999-10-20	$7700.00	Window Closed / Lapsed

Surface preparation of ceramic substrates for metallization

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag