Gas-tight sintered translucent aluminum oxide and method
Assignee: US Philips Corp
•
Filing: 1986-09-04
•
Granted: 1987-10-13
•
Expires: 2006-09-04
Abstract
Abstract The invention relates to gas-tight sintered translucent aluminum oxide having a density of at least 99.5%, which contains at most 1000 ppm by weight of MgO. According to the invention, the aluminum oxide also has a content of Er 2 O 3 lying between 20 ppm by weight and 200 ppm by weight. The material thus obtained has a great mechanical strength, a high resistance to attack by sodium and a satisfactory translucence. Thus, the material is very suitable for use as wall material for the discharge vessels of high-pressure discharge lamps.
Inventors
- 👤 Peter R. Prud'homme van Reine
- 👤 Gerardus H. M. Siebers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 09:25
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/6325; C04B35/01; C04B35/10; C04B35/111; C04B35/115; H; H01; H01J; H01J61/00; H01J61/02; H01J61/30; H01J61/302; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3205; C04B2235/3206; C04B2235/3217; C04B2235/3224; C04B2235/44; C04B2235/50; C04B2235/54; C04B2235/5409; C04B2235/65; C04B2235/658; C04B2235/6581; C04B2235/6582; C04B2235/70; C04B2235/74; C04B2235/77; C04B2235/96
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
59 words
A gas-tight sintered translucent aluminum oxide having a density of at least 99.5% containing MgO in a quantity of from zero to about 1000 ppm by weight, characterized in that the aluminum oxide contains erbium (Er) in a quantity, expressed in Er 2 O 3 , of from about 20 ppm by weight to about 200 ppm by weight.
Claim 2
Dependent Claim
59 words
A gas-tight sintered translucent aluminum oxide having a density of at least 99.5% containing MgO in a quantity of from zero to about 1000 ppm by weight, characterized in that the aluminum oxide contains erbium (Er) in a quantity, expressed in Er 2 O 3 , of from about 20 ppm by weight to about 200 ppm by weight.
Claim 3
Dependent Claim
43 words
Aluminum oxide as claimed in claim 1, characterized in that the MgO content is from zero to about 500 ppm by weight and the Er content, expressed in Er 2 O 3 , is from about 20 to about 130 ppm by weight.
Claim 4
Dependent Claim
116 words
A method of manufacturing an article from gas-tight sintered aluminum oxide as claimed in claim 2, characterized in that: an MgO compound is added to a powder mixture of Al 2 O 3 ; the Al 2 O 3 powder thus obtained is shaped into a desired moulding and is then heated in an oxidizing atmosphere at a temperature between 1150° C. and 1400° C.; a desired quantity of Er 2 O 3 is then added to the moulding by impregnation with an Er-containing solution; and thereafter the moulding is sintered in hydrogen or in a vacuum at a pressure of up to about 0.13 Pa and at a temperature of up to about 1800° C.
Claim 5
Dependent Claim
22 words
A method as claimed in claim 3, characterized in that the Er-containing soluiton consists of an Er acetyl acetonate solution in alcohol.
Claim 6
Dependent Claim
121 words
A method of manufacturing an article from gas-tight sintered aluminum oxide as claimed in claim 1, characterized in that an MgO compound is added to a powder mixture of Al 2 O 3 , in that the Al 2 O 3 powder thus obtained is shaped, after disagglomeration, into a desired moulding and is then heated in an oxidizing atmosphere at a temperature between 1150° C. and 1400° C., in that a desired quantity of Er 2 O 3 is then added to the moulding by impregnation in an Er-containing solution, and in that thereafter the moulding is sintered in hydrogen or in a vacuum at a pressure of at most 0.13 Pa at a temperature of at most 1800° C.
Claim 7
Dependent Claim
22 words
A method as claimed in claim 5, characterized in that the Er-containing solution consists of an Er acetyl acetonate solution in alcohol.
Claim 8
Dependent Claim
21 words
A method as claimed in claim 3, characterized in that the Al 2 O 3 powder is disagglomerated prior to shaping.
Claim 9
Dependent Claim
21 words
A method as claimed in claim 5, characterized in that the Al 2 O 3 powder is disagglomerated prior to shaping.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-12 | 1991-04-13 | 1991-10-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-12 | 1995-04-13 | 1995-10-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-12 | 1999-04-13 | 1999-10-13 | $7700.00 | Window Closed / Lapsed |