Abstract Polycrystalline translucent alumina having an average grain size of alumina crystal grain being not smaller than 20μ and an average surface roughness of the fired body being not larger than 1/10 of the maximum grain size of alumina crystal grain and capable of being used for an envelope of a high pressure vapor discharge lamp, which is produced by shaping alumina composition powders consisting mainly of alumina into a given shape, primarily firing the shaped body under vacuum or in an atmosphere of hydrogen gas or dissociated ammonia gas at a temperature within 1,500° C. and then secondarily firing the primarily fired body at a temperature of 1,650°-1,900° C., at least the temperature from 1,400° C. to 1,700° C. being raised at a rate of not lower than 200° C./hr.
A method for producing a polycrystalline translucent alumina envelope for a high pressure vapor discharge lamp, which comprises shaping compounded alumina powders having a grain size not larger than 1μ and a purity of more than 99.5% into a given shape, primarily firing the shaped body under vacuum or in an atmosphere of hydrogen gas or dissociated ammonia gas at a temperature within the range 1,300°-1,500° C. and then secondarily firing the primarily fired body at a temperature of 1,650°-1,900° C., for a period of 1-15 hours at least the temperature from 1,400° C. to 1,700° C. being raised at a rate of not lower than 200° C./hr.
Claim 2
Independent Claim
108 words
A method for producing a polycrystalline translucent alumina envelope for a high pressure vapor discharge lamp, which comprises shaping compounded alumina powders having a grain size not larger than 1μ and a purity of more than 99.5% into a given shape, primarily firing the shaped body under vacuum or in an atmosphere of hydrogen gas or dissociated ammonia gas at a temperature within the range 1,300°-1,500° C. and then secondarily firing the primarily fired body at a temperature of 1,650°-1,900° C., for a period of 1-15 hours at least the temperature from 1,400° C. to 1,700° C. being raised at a rate of not lower than 200° C./hr.
Claim 3
Dependent Claim
56 words
The method as claimed in claim 1, wherein the compounded powders are prepared by adding 0.01-0.2% by weight of MgO, 0.01-0.2% by weight of La 2 O 3 and 0.01-0.2% by weight of Y 2 O 3 to alumina powders having a grain size of not larger than 1μ and a purity of more than 99.5%.