Coated cemented carbide tool for steel roughing applications and methods for machining
Assignee: Verizon Laboratories Inc
•
Filing: 1985-11-18
•
Granted: 1987-10-06
•
Expires: 2005-11-18
Abstract
Abstract A steel roughing grade coated cemented carbide cutting tool comprises WC grains equal to or less than 70 w/o of the tool substrate, from about 5 to about 10 w/o of a cobalt bonding phase and the remainder being metal carbide grains selected from the group TiC, TaC, NbC, HfC and combinations thereof. The average WC grain size is from about 0.9 to about 1.3 microns and less than 10% of the WC grains have a size less than 0.5 microns. The coated cemented carbide tool is coated with an adherent refractory coating layer. The coated cemented carbide cutting tool can be used to machine steel at rough and heavy rough cutting conditions.
Inventors
- 👤 Sergei-Tomislav V. Buljan
- 👤 Helmut Lingertat
- 👤 J. Gary Baldoni
- 👤 Vinod K. Sarin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 00:54
CPC Classifications
C; C22; C22C; C22C29/00; C22C29/02; C22C29/06; C22C29/08; B; B23; B23B; B23B27/00; B23B27/14; B23B27/148; C23; C23C; C23C28/00; C23C28/04; C23C30/00; C23C30/005; B22; B22F; B22F2998/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
116 words
A coated cemented carbide cutting tool comprising a densified body having tungsten carbide grains, metal carbide grains selected from the group consisting of TiC, TaC, NbC, HfC, and combinations thereof, a bonding phase consisting essentially of cobalt, and an adherent refractory coating layer; said tungsten carbide grains being equal to or greater than 70 weight percent of said densified body; said cobalt being from about 5 to about 10 weight percent of said densified body; and the remainder being said metal carbide grains; said tungsten carbide grains having an average grain size from about 0.9 to about 1.3 microns and less than 10 percent of said tungsten carbide grains having a size less than 0.5 microns.
Claim 2
Dependent Claim
116 words
A coated cemented carbide cutting tool comprising a densified body having tungsten carbide grains, metal carbide grains selected from the group consisting of TiC, TaC, NbC, HfC, and combinations thereof, a bonding phase consisting essentially of cobalt, and an adherent refractory coating layer; said tungsten carbide grains being equal to or greater than 70 weight percent of said densified body; said cobalt being from about 5 to about 10 weight percent of said densified body; and the remainder being said metal carbide grains; said tungsten carbide grains having an average grain size from about 0.9 to about 1.3 microns and less than 10 percent of said tungsten carbide grains having a size less than 0.5 microns.
Claim 3
Dependent Claim
31 words
A coated cemented carbide cutting tool in accordance with claim 1 wherein said adherent refractory coating layer comprises an intermediate adherent refractory coating layer and an outer adherent alumina coating layer.
Claim 4
Dependent Claim
32 words
A coated cemented carbide cutting tool in accordance with claim 2 wherein said intermediate adherent coating layer comprises a coating layer having a thickness between about 0.1 microns and about 10 microns.
Claim 5
Dependent Claim
31 words
A coated cemented carbide cutting tool in accordance with claim 2 wherein said outer adherent coating layer comprises a coating layer having a thickness between about 1.0 and about 10 microns.
Claim 6
Dependent Claim
44 words
A coated cemented carbide cutting tool in accordance with claim 2 wherein said intermediate adherent refractory coating layer is selected from the group consisting of titanium nitride, vanadium nitride, chromium nitride, zirconium nitride, niobium nitride, molybdenum nitride, hafnium nitride, tantalum nitride and combinations thereof.
Claim 7
Dependent Claim
45 words
A coated cemented carbide cutting tool in accordance with claim 1 wherein said adherent refractory coating layer is selected from the group consisting of titanium carbide, vanadium carbide, chromium carbide, zirconium carbide, niobium carbide, molybdenum carbide, hafnium carbide, tantalum carbide, tungsten carbide and combinations thereof.
Claim 8
Dependent Claim
45 words
A coated cemented carbide cutting tool in accordance with claim 1 wherein said adherent refractory coating layer is selected from the group consisting of titanium carbonitride, vanadium carbonitride, chromium carbonitride, zirconium carbonitride, niobium carbonitride, molybdenum carbonitride, hafnium carbonitride, tantalum carbonitride, tungsten carbonitride and combinations thereof.
Claim 9
Dependent Claim
179 words
A coated cemented carbide cutting tool comprising a densified body having an intermediate adherent refractory coating layer and an outer adherent refractory coating layer, wherein said intermediate adherent refractory coating layer has a different chemical composition than said outer adherent refractory coating layer; said densified body consisting essentially of tungsten carbide grains being equal to or greater than 70 weight percent of said densified body; from about 5 to about 10 weight percent of said densified body being a bonding phase consisting essentially of cobalt; and the remainder being metal carbide grains being selected from the group consisting of TiC, TaC, NbC, HfC, and combinations thereof; said tungsten carbide grains having an average grain size from about 0.9 to about 1.3 microns and less than 10 percent of said tungsten carbide grains having a size less than 0.5 microns; and said intermediate adherent refractory coating layer and said outer adherent refractory coating layer being selected from the group consisting of carbides, nitrides, and carbonitrides of Ti, V, Cr, Zr, Nb, Mo, Hf, Ta, W and combinations thereof and alumina.
Claim 10
Dependent Claim
179 words
A coated cemented carbide cutting tool comprising a densified body having an intermediate adherent refractory coating layer and an outer adherent refractory coating layer, wherein said intermediate adherent refractory coating layer has a different chemical composition than said outer adherent refractory coating layer; said densified body consisting essentially of tungsten carbide grains being equal to or greater than 70 weight percent of said densified body; from about 5 to about 10 weight percent of said densified body being a bonding phase consisting essentially of cobalt; and the remainder being metal carbide grains being selected from the group consisting of TiC, TaC, NbC, HfC, and combinations thereof; said tungsten carbide grains having an average grain size from about 0.9 to about 1.3 microns and less than 10 percent of said tungsten carbide grains having a size less than 0.5 microns; and said intermediate adherent refractory coating layer and said outer adherent refractory coating layer being selected from the group consisting of carbides, nitrides, and carbonitrides of Ti, V, Cr, Zr, Nb, Mo, Hf, Ta, W and combinations thereof and alumina.
Claim 11
Dependent Claim
32 words
A coated cemented carbide cutting tool in accordance with claim 8 wherein said intermediate adherent coating layer comprises a coating layer having a thickness between about 0.1 microns and about 10 microns.
Claim 12
Dependent Claim
31 words
A coated cemented carbide cutting tool in accordance with claim 6 wherein said outer adherent coating layer comprises a coating layer having a thickness between about 1.0 and about 10 microns.
References Cited (Backward Citations)
US31526A
Cited
US3525610A
Cited
US3752655A
Cited
GB1291388A
Cited
US3779746A
Cited
US3737289A
Cited
US4101703B1
Cited
US4101703A
Cited
US3955038A
Cited
US4097275A
Cited
US4018631A
Cited
US4035541A
Cited
USRE31526E
Cited
US4150984A
Cited
US4268582A
Cited
US4269899A
Cited
US4282289A
Cited
US4357382A
Cited
US4320156A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-05 | 1991-04-06 | 1991-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-05 | 1995-04-06 | 1995-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-05 | 1999-04-06 | 1999-10-06 | $7700.00 | Window Closed / Lapsed |