Metal surface hardening by carbide formation
Assignee: Rolls Royce PLC
•
Filing: 1985-12-17
•
Granted: 1987-10-06
•
Expires: 2005-12-17
Abstract
Abstract A method of surface hardening a metal surface in which the surface is firstly coated with a colloidal dispersion of graphite and then locally melted, in an inert atmosphere or vacuum, so that the molten metal reacts with the graphite to form a metal carbide. On resolidification, the metal carbide defines a dendritic carbide structure within the metal adjacent its surface.
Inventors
- 👤 Robert M. MacIntyre
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:01
CPC Classifications
C; C23; C23C; C23C26/00; C23C26/02; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/32; B23K35/325; B23K35/327
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
64 words
A method of surface hardening a metal surface comprising locally melting the metal surface with a beam of high energy radiation in an inert atmosphere or vacuum and in the presence of elemental carbon for sufficient time for said metal and carbon to react to produce a carbide which, on subsequent resolidification, defines a dendritic carbide structure within said metal adjacent the surface thereof.
Claim 2
Independent Claim
64 words
A method of surface hardening a metal surface comprising locally melting the metal surface with a beam of high energy radiation in an inert atmosphere or vacuum and in the presence of elemental carbon for sufficient time for said metal and carbon to react to produce a carbide which, on subsequent resolidification, defines a dendritic carbide structure within said metal adjacent the surface thereof.
Claim 3
Dependent Claim
50 words
A method of surface hardening a metal surface as claimed in claim 1 wherein said local melting and resolidification of said metal surface in the presence of elemental carbon to produce a dendritic carbide structure is performed more than once on each portion of said metal surface requiring surface hardening.
Claim 4
Dependent Claim
26 words
A method of surface hardening a metal surfce as claimed in claim 1 wherein said beam of high energy radiation is constituted by a laser beam.
Claim 5
Dependent Claim
31 words
A method of surface hardening a metal surface as claimed in claim 3 wherein said laser beam is provided by a laser having a power output of up to 2 KW.
Claim 6
Dependent Claim
35 words
A method of surface hardening a metal surface as claimed in claim 4 wherein said laser beam has a diameter of between 0.4 and 3 mm at its point of impingement upon said metal surface.
Claim 7
Dependent Claim
46 words
A method of surface hardening a metal surface as claimed in claim 1 wherein relative motion is effected between said beam and said metal surface so that adjacent regions of said metal surface are successively melted in the presence of said elemental carbon and subsequently resolidify.
Claim 8
Dependent Claim
28 words
A method of surface hardening a metal surface as claimed in claim 6 wherein said relative motion is effected at a speed of between 7 and 50 mm/second.
Claim 9
Dependent Claim
37 words
A method of surface hardening a metal surface as claimed in claim 1 wherein said elemental carbon is in the form of particulate carbon substantially evenly distributed over said metal surface prior to the local melting thereof.
Claim 10
Dependent Claim
23 words
A method of surface hardening a metal surface as claimed in claim 8 wherein said carbon is in the form of colloidal graphite.
Claim 11
Dependent Claim
28 words
A method of surface hardening a metal surface as claimed in claim 1 wherein said elemental carbon is directed into the metal melted by said high energy beam.
Claim 12
Dependent Claim
22 words
A method of surface hardening a metal surface as claimed in claim 1 wherein said metal is titanium or an alloy thereof.
References Cited (Backward Citations)
US2196128A
Cited
US2719355A
Cited
GB1258561A
Cited
GB1248733A
Cited
US4232094A
Cited
GB1501342A
Cited
US4122240A
Cited
GB1547172A
Cited
US4157923A
Cited
GB1587235A
Cited
GB1538364A
Cited
GB2004919A
Cited
GB1574984A
Cited
GB2022146A
Cited
US4212900A
Cited
EP0092683A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-05 | 1991-04-06 | 1991-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-05 | 1995-04-06 | 1995-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-05 | 1999-04-06 | 1999-10-06 | $7700.00 | Window Closed / Lapsed |