Surface alloying and heat treating processes
Assignee: Ford Motor Co
•
Filing: 1976-09-13
•
Granted: 1979-06-12
•
Expires: 1996-09-13
Abstract
Abstract A method is disclosed for increasing physical properties of a non-allotropic metal article along a beam affected zone. A preferred method comprises passing a high energy beam (of at least 10,000 watts/cm 2 measured at the interface of the beam with the article across a predetermined surface area at a rate to cooperate with the proportioning of the total article mass with respect to the beam affected zone mass to produce a rapid self-quenching rate and thus assure a desired precipitate and/or intermetallic compound in the resolidification zone. The high energy beam is preferably a laser generated by a device having a power level of at least 500 watts. The method requires and facilitates alloying which may be varied in several respects: (a) alloying ingredients may be previously deposited over the beam affected zone so as to be turbulently mixed with melting of the base material in said zone, (b) alloying ingredients may be constituted as a wire and fed into the high energy beam to be contemporaneously melted with the base material, (c) the alloying ingredients are selected as those having an affinity to form intermetallic compounds with the non-alloptropic metal base, such as copper, manganese, chromium, zinc, cobalt, magnesium, molybdenum, titanium, vanadian, tungsten, zirconium, iron and nickel for an aluminum base and silicon as an independent wear resistance particle, and (d) the alloying ingredients are proportioned with respect to the thickness of the melted zone to render a desired alloy concentration after melting to facilitate greater hardness, greater corrosion resistance, or greater fatigue life of the affected surface region of the article.
Inventors
- 👤 Chia M. Yen
- 👤 Uck I. Chang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:59
CPC Classifications
C; C22; C22F; C22F3/00; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/28; B23K35/286; Y; Y10; Y10S; Y10S277/00; Y10S277/922
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
283 words
A method of treating a selected exposed region of a non-allotropic metal article for enhancing the physical properties of said region, comprising: (a) selecting the non-allotropic metal for said article having a thermal conductivity of at least 0.25 Cal. /cm 2 cm/sec./°C., (b) directing a high energy beam at an exposed region of said article to heat said article at a first zone and to melt said article at a second zone within said first zone to a predetermined depth, said beam providing an energy level at the interface with said article of at least 10,000 watts/cm 2 , (c) either prior to or simultaneous with directing a high energy beam at said article, introducing a molten alloying ingredient to said second zone to be mixed with the molten metal thereof, said alloying ingredient comprising a material having an affinity for said non-allotropic metal to form a solid solution with intermetallic compounds therewith, and to form precipitate particles, said alloying ingredients being introduced is proportioned to be within the range of 1:1 to 1:10 taken as a ratio of alloying ingredient to melted non-allotropic metal in said second zone. (d) controlling the area of said beam interface, beam energy level, and rate of displacement of said beam along said article to restrict said first zone to a predetermined volume and insure a predetermined fast heat-up rate of said first zone, and (e) proportioning the mass of said article to the volume of said first zone to provide a fast self-quenching cooling rate of said first zone upon removal of the influence of said beam therefrom whereby a fine grain solution-hardened structure and fine precipitated particles are promoted in at least said second zone.
Claim 2
Independent Claim
283 words
A method of treating a selected exposed region of a non-allotropic metal article for enhancing the physical properties of said region, comprising: (a) selecting the non-allotropic metal for said article having a thermal conductivity of at least 0.25 Cal. /cm 2 cm/sec./°C., (b) directing a high energy beam at an exposed region of said article to heat said article at a first zone and to melt said article at a second zone within said first zone to a predetermined depth, said beam providing an energy level at the interface with said article of at least 10,000 watts/cm 2 , (c) either prior to or simultaneous with directing a high energy beam at said article, introducing a molten alloying ingredient to said second zone to be mixed with the molten metal thereof, said alloying ingredient comprising a material having an affinity for said non-allotropic metal to form a solid solution with intermetallic compounds therewith, and to form precipitate particles, said alloying ingredients being introduced is proportioned to be within the range of 1:1 to 1:10 taken as a ratio of alloying ingredient to melted non-allotropic metal in said second zone. (d) controlling the area of said beam interface, beam energy level, and rate of displacement of said beam along said article to restrict said first zone to a predetermined volume and insure a predetermined fast heat-up rate of said first zone, and (e) proportioning the mass of said article to the volume of said first zone to provide a fast self-quenching cooling rate of said first zone upon removal of the influence of said beam therefrom whereby a fine grain solution-hardened structure and fine precipitated particles are promoted in at least said second zone.
Claim 3
Dependent Claim
43 words
The method as in claim 1, in which said beam interface with said article and the depth of said second zone are each controlled to promote turbulence of the melted metal for thorough mixing of said melted alloying ingredient thereinto prior to solidification.
Claim 4
Dependent Claim
19 words
The method as in claim 1, in which said metal article is comprised of aluminum or an aluminum alloy.
Claim 5
Dependent Claim
29 words
The method as in claim 3, in which said article mass beneath said first zone has a thickness of at least 5 times the depth of said first zone.
Claim 6
Dependent Claim
55 words
The method as in claim 1, in which the high energy beam is comprised of rays controlled like visible light rays, said beam having a focal point out of the plane of the surface of said exposed region whereby the beam interface area with said region is controlled to be at least 0.00003 square inches.
Claim 7
Dependent Claim
30 words
The method as in claim 1, in which said beam is pulsated to achieve either an interrupted first zone or to affect a predetermined controlled depth of said second zone.
Claim 8
Independent Claim
230 words
A method of alloying a selected exposed region of a non-allotropic metal article for enhancing the physical properties of said region, comprising the steps of: (a) providing a non-allotropic metal casting to constitute said article, said metal having a thermal conductivity of at least 0.25 Cal./cm 2 /cm/sec./°C., (b) plasma spraying an alloying ingredient onto said exposed region, said alloying ingredient comprising substantially a material having an affinity to form intermetallic compounds with non-allotropic metal, (c) directing a high energy beam at said selected exposed region of said article to melt said article along a predetermined zone and to melt an amount of said alloying ingredient proportioned to said zone, (d) controlling the area of interface of said beam with said region, beam energy level, and rate of displacement of said beam along said article to restrict said zone to a predetermined volume for insuring a fast heat-up of said zone and to create a turbulence in said melted metal and melted alloying ingredient, the amount of alloying ingredient melted and dissolved in a corresponding melted zone of said article is proportioned to be within the range of 1:10 to 1:20 (alloying ingredient: non-allotropic metal in zone) whereby said zone will have a solidification structure principally providing increased fatigue life characterized by a uniform fine grain structure, absence of intermetallic compounds and a precipitation hardened aluminum matrix promoting age hardening.
Claim 9
Independent Claim
230 words
A method of alloying a selected exposed region of a non-allotropic metal article for enhancing the physical properties of said region, comprising the steps of: (a) providing a non-allotropic metal casting to constitute said article, said metal having a thermal conductivity of at least 0.25 Cal./cm 2 /cm/sec./°C., (b) plasma spraying an alloying ingredient onto said exposed region, said alloying ingredient comprising substantially a material having an affinity to form intermetallic compounds with non-allotropic metal, (c) directing a high energy beam at said selected exposed region of said article to melt said article along a predetermined zone and to melt an amount of said alloying ingredient proportioned to said zone, (d) controlling the area of interface of said beam with said region, beam energy level, and rate of displacement of said beam along said article to restrict said zone to a predetermined volume for insuring a fast heat-up of said zone and to create a turbulence in said melted metal and melted alloying ingredient, the amount of alloying ingredient melted and dissolved in a corresponding melted zone of said article is proportioned to be within the range of 1:10 to 1:20 (alloying ingredient: non-allotropic metal in zone) whereby said zone will have a solidification structure principally providing increased fatigue life characterized by a uniform fine grain structure, absence of intermetallic compounds and a precipitation hardened aluminum matrix promoting age hardening.
Claim 10
Dependent Claim
14 words
The method as in claim 1, in which said non-allotropic metal is aluminum based.
Claim 11
Dependent Claim
39 words
The method as in claim 7, in which said non-allotropic metal has a reflective surface, said metal casting region being coated with an energy beam absorption material to facilitate absorption of the rays of said beam within said casting.
Claim 12
Dependent Claim
27 words
This method as in claim 7, in which said absorptive coating is arranged in a predetermined pattern for selecting treatment of the surface of said metal casting.
Claim 13
Dependent Claim
56 words
The method as in claim 7, in which the alloying ingredient is deposited as a coating on said metal casting prior to the application of said high energy beam, said deposition being carried out by plasma stream whereby the alloying ingredient is mechanically and molecularly locked to the surface of said casting along said predetermined zone.
Claim 14
Dependent Claim
34 words
The method as in claim 7, in which the alloying ingredient is formed as a wire, said wire being fed into said high energy beam to be melted and carried into said melted zone.
Claim 15
Dependent Claim
32 words
The method as in claim 7, in which the alloying ingredients are mixed with resin and brushed on said non-allotropic metal prior to directing said high energy beam at said exposed region.
Claim 16
Dependent Claim
32 words
The method as in claim 7, in which the alloying ingredients are in powder form and are fed into said high energy beam to be melted and alloyed with said non-allotropic metal.
Claim 17
Dependent Claim
35 words
The method as in claim 7, in which said beam is moved along a plurality of separated and spaced paths whereby the beam affected zones form spaced lands on the exposed surface of said article.
Claim 18
Independent Claim
211 words
A method of alloying a selected exposed region of a non-allotropic metal article for enhancing the physical properties of said region, comprising the steps of: (a) providing a non-allotropic metal casting to constitute said article, said metal having a thermal conductivity of at least 0.25 Cal./cm 2 /cm/sec./°C. (b) placing an alloying ingredient adjacent said exposed region, said alloying ingredient comprising substantially a material having an affinity to form intermetallic compounds with said non-allotropic metal, (c) directing a high energy beam at said selected exposed region of said article to melt said article along a predetermined zone and to melt an amount of said alloying ingredient proportioned to said zone, (d) controlling the area of interface of said beam with said region, beam energy level, and rate of displacement of said beam along said article to restrict said zone to a predetermined volume for insuring a fast heat-up of said zone and to create a turbulence in said melted metal and melted alloying ingredient, the amount of alloying ingredient melted and dissolved in a corresponding melted zone of said article is proportioned to be at least 2:1 (alloying ingredient: non-allotropic metal in zone) whereby said zone will be changed in base and have a solidification structure principally providing increased corrosion resistance.
Claim 19
Independent Claim
211 words
A method of alloying a selected exposed region of a non-allotropic metal article for enhancing the physical properties of said region, comprising the steps of: (a) providing a non-allotropic metal casting to constitute said article, said metal having a thermal conductivity of at least 0.25 Cal./cm 2 /cm/sec./°C. (b) placing an alloying ingredient adjacent said exposed region, said alloying ingredient comprising substantially a material having an affinity to form intermetallic compounds with said non-allotropic metal, (c) directing a high energy beam at said selected exposed region of said article to melt said article along a predetermined zone and to melt an amount of said alloying ingredient proportioned to said zone, (d) controlling the area of interface of said beam with said region, beam energy level, and rate of displacement of said beam along said article to restrict said zone to a predetermined volume for insuring a fast heat-up of said zone and to create a turbulence in said melted metal and melted alloying ingredient, the amount of alloying ingredient melted and dissolved in a corresponding melted zone of said article is proportioned to be at least 2:1 (alloying ingredient: non-allotropic metal in zone) whereby said zone will be changed in base and have a solidification structure principally providing increased corrosion resistance.
Claim 20
Dependent Claim
28 words
The method as in claim 16, in which said alloying ingredient is aluminum and said non-allotropic metal is an aluminum alloy containing less than 5% of alloying ingredients.
References Cited (Backward Citations)
US2902583A
Cited
US3802927A
Cited
US3834947A
Cited
US3806380A
Cited
GB1392812A
Cited
DE2134662A1
Cited
US3839618A
Cited
US3850698A
Cited
US3935417A
Cited
US3872279A
Cited
US4015100A
Cited
US3944443A
Cited
US3989512A
Cited
US3992164A
Cited
US3952180A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-11 | 1982-12-11 | 1983-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-11 | 1986-12-11 | 1987-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-11 | 1990-12-11 | 1991-06-12 | $7700.00 | Window Closed / Lapsed |