Method of diffusion of impurities
Assignee: Sony Corp
•
Filing: 1985-11-27
•
Granted: 1987-10-06
•
Expires: 2005-11-27
Abstract
Abstract A method for selectively diffusing impurities such as zinc into the substrate of a compound semiconductor such as gallium arsenide (GaAs). The method makes use of a diffusion mask in such a manner that the thickness of the oxygen-containing layer at the interface between the diffusion mask and the semiconductor substrate is less than 20Å so that the abnormal transverse diffusion that would otherwise occur at the interface in the vicinity of the opening of the diffusion mask on the semiconductor surface is suppressed. The result is an increased accuracy in the diffusion pattern of the impurities.
Inventors
- 👤 Masaru Wada
- 👤 Yoji Kato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:03
CPC Classifications
H; H10; H10P; H10P32/00; H10P32/10; H10P32/12; H10P32/17; H10P32/174; H10P76/00; H10P76/40; H10P76/405
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
56 words
A method of selectively diffusing an impurity into the surface of a compound semiconductor which comprises: applying a diffusion mask directly onto the compound semiconductor substrate while limiting the oxygen-containing layer at the interface between said mask and said substrate to less than 20 Å, and diffusing said impurity through said mask and into said substrate.
Claim 2
Independent Claim
56 words
A method of selectively diffusing an impurity into the surface of a compound semiconductor which comprises: applying a diffusion mask directly onto the compound semiconductor substrate while limiting the oxygen-containing layer at the interface between said mask and said substrate to less than 20 Å, and diffusing said impurity through said mask and into said substrate.
Claim 3
Dependent Claim
14 words
A method according to claim 1 wherein said compound semiconductor is gallium arsenide (GaAs).
Claim 4
Dependent Claim
12 words
A method according to claim 1 wherein said impurity is elemental zinc.
Claim 5
Dependent Claim
30 words
A method according to claim 1 which includes the step of etching the surface of the compound semiconductor with a potassium hydroxide solution prior to applying said diffusion mask thereover.
Claim 6
Dependent Claim
28 words
A method according to claim 1 wherein at least that portion of the diffusion mask which contacts the semiconductor substrate is composed of a layer of silicon nitride.
Claim 7
Dependent Claim
26 words
A method according to claim 5 in which: the step of applying said diffusion mask is carried out by the plasma assisted chemical vapor deposition method.
Claim 8
Dependent Claim
39 words
A method according to claim 6 which includes the steps of subjecting the semiconductor substrate to annealing before the formation of said silicon nitride layer, and carrying out the plasma assisted chemical vapor deposition in a hydrogen gas atmosphere.
Claim 9
Dependent Claim
18 words
A method according to claim 5 wherein said layer of silicon nitride has a refractive index of 2.0±0.07.
Claim 10
Dependent Claim
18 words
A method according to claim 5 wherein said layer of silicon nitride has a refractive index of 2.0±0.05.
Claim 11
Dependent Claim
18 words
A method according to claim 5 wherein said layer of silicon nitride has a refractive index of 2.0±0.03.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-10-05 | 1991-04-06 | 1991-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-10-05 | 1995-04-06 | 1995-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-10-05 | 1999-04-06 | 1999-10-06 | $7700.00 | Window Closed / Lapsed |