Ultra-violet ray curing type resin composition
Assignee: Mitsubishi Electric Corp
•
Filing: 1986-02-27
•
Granted: 1987-09-01
•
Expires: 2006-02-27
Abstract
Abstract A resin composition of excellent ultra-violet ray curing property and remarkably improved adhesive force to a base material to form a cured coating film, the resin composition being composed of cationically polymerizable compound, photo-initiator, phenoxy resin, and polyhydric alcohol.
Inventors
- 👤 Hirofumi Fujioka
- 👤 Masami Inoue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:25
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/68; C08F; C08F283/00; C08F283/10; C08G59/40; C08G59/62; C08L; C08L63/00; Y; Y10; Y10S; Y10S525/00; Y10S525/93
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
142 words
An ultra-violet ray curing type resin composition, which consists essentially of: (A) at least one kind of cationically polymerizable compound containing, as the principal constituent thereof, an epoxy resin having two or more oxirane rings is one molecule thereof; (B) 0.5 to 20% by weight, with respect to said cationically polymerizable compound, of phenoxy resin having a molecular weight in a range of from 10,000 to 60,000; (C) 0.5 to 20% by weight, with respect to said cationically polymerizable compound, of polyhydric aliphatic alcohol other than (B) containing two or more hydroxyl groups in its molecule; and (D) an effective amount of from 0.5 to 10% by weight, with respect to said cationically polymerizable compound, of a photo-initiator capable of isolating a Lewis acid catalyst which is able to initiate polymerization of said cationically polymerizable compound by irradiation of the ultra-violet rays.
Claim 2
Dependent Claim
142 words
An ultra-violet ray curing type resin composition, which consists essentially of: (A) at least one kind of cationically polymerizable compound containing, as the principal constituent thereof, an epoxy resin having two or more oxirane rings is one molecule thereof; (B) 0.5 to 20% by weight, with respect to said cationically polymerizable compound, of phenoxy resin having a molecular weight in a range of from 10,000 to 60,000; (C) 0.5 to 20% by weight, with respect to said cationically polymerizable compound, of polyhydric aliphatic alcohol other than (B) containing two or more hydroxyl groups in its molecule; and (D) an effective amount of from 0.5 to 10% by weight, with respect to said cationically polymerizable compound, of a photo-initiator capable of isolating a Lewis acid catalyst which is able to initiate polymerization of said cationically polymerizable compound by irradiation of the ultra-violet rays.
Claim 3
Dependent Claim
51 words
An ultra-violet ray curing type resin composition according to claim 1, wherein said photo-initiator is one selected from the group consisting of aromatic halonium salts, and photosensitive aromatic onium salts of the group VIa elements and the group Va elements, and a mixture of two or more kinds of said salts.
References Cited (Backward Citations)
US3776729A
Cited
US4035189A
Cited
US4256828A
Cited
US4168173A
Cited
US4173476A
Cited
US4446286A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-31 | 1991-03-02 | 1991-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-31 | 1995-03-02 | 1995-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-31 | 1999-03-02 | 1999-09-01 | $7700.00 | Window Closed / Lapsed |