Electron beam curable polyrethane compositions
Assignee: Goodrich Corp
•
Filing: 1982-08-02
•
Granted: 1984-05-01
•
Expires: 2002-08-02
Abstract
Abstract Improved electron beam curable compounds are prepared by mixing 100 weight parts of (1) polyurethanes prepared from polymeric polyols, organic diisocyanates and polyethers having terminal hydroxyl and unsaturated groups, or terminal hydroxyl and pendant unsaturated groups with (2) to 1 to 25 weight parts of an acrylate or alkacrylate terminated polyurethanes prepared by reacting isocyanate terminated prepolymers of hydroxyl terminated polymers with hydroxyl-terminated acrylates or alkacrylates. Compositions of this blend may be crosslinked or cured in a few seconds by electron beam to provide an improved stable coating that can be cured to a variety of hardnesses. These polyurethanes combined with phenoxy resins also form particularly useful binder systems for magnetic tape.
Inventors
- 👤 Edmond G. Kolycheck
- 👤 Laura L. Tolle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:27
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/67; C08G18/6795; C08G18/671; C08G18/672; C08L; C08L75/00; C08L75/04; C08L75/14; Y; Y10; Y10S; Y10S525/00; Y10S525/92
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
117 words
Electron beam-curable polyurethane compositions comprising (A) 100 weight parts of the reaction product of (1) hydroxyl-terminated polyesters, polyethers, polylactones, polycarbonates, polyepihalohydrins or polyhydrocarbon macropolyols, (2) unsaturated polyethers having an average of 1/2 to 18 double bonds per molecule, selected from the group consisting of polyethers having one terminal hydroxyl group and one terminal double bond group in amount of up to 20 weight percent, and polyether glycols having pendant double bond groups, in amounts of 5 to 100 weight percent, each based on the total polyols, and (3) an organic diisocyanate, in about an equimolar ratio of diisocyanate to the total polyols used, and (B) 1 to 25 weight parts of an acrylate or alkacrylate terminated polyurethane.
Claim 2
Dependent Claim
117 words
Electron beam-curable polyurethane compositions comprising (A) 100 weight parts of the reaction product of (1) hydroxyl-terminated polyesters, polyethers, polylactones, polycarbonates, polyepihalohydrins or polyhydrocarbon macropolyols, (2) unsaturated polyethers having an average of 1/2 to 18 double bonds per molecule, selected from the group consisting of polyethers having one terminal hydroxyl group and one terminal double bond group in amount of up to 20 weight percent, and polyether glycols having pendant double bond groups, in amounts of 5 to 100 weight percent, each based on the total polyols, and (3) an organic diisocyanate, in about an equimolar ratio of diisocyanate to the total polyols used, and (B) 1 to 25 weight parts of an acrylate or alkacrylate terminated polyurethane.
Claim 3
Dependent Claim
139 words
The polyurethane compositions of claim 1 wherein in (A) (1) are hydroxyl-terminated polyesters or polyethers having average molecular weights of about 400 to 5,000, (2) the unsaturated polyethers are tetrahydrofuran polyethers having average molecular weights from about 300 to 2,000 in amount from about 25 to 75 weight percent and (3) the organic diisocyanate has the formula OCN-Ar-C-Ar-NCO wherein Ar is cyclic radical, X is a valence bond, an alkylene radical containing 1 to 5 carbon atoms or NR wherein R is alkyl radical containing 1 to 5 carbon atoms, oxygen, sulfur, sulfoxide or sulfone and (4) a diol chain extender in amount of 0 to 10 mole per mol of macropolyol, and (B) is a polyurethane reaction product of a hydroxyl terminated polyester, polyether, polylactone, polyepihalohydrin, polycarbonate or polyhydrocarbon with an organic diisocyanate, and a hydroxyacrylate or hydroxyalk-acrylate.
Claim 4
Dependent Claim
171 words
The polyurethanes of claim 2 wherein in (A) (1) the polyethers have the formula HO y H wherein x is 2 to 6 and y is an integer, the polyesters are polyesters of acids of the formula HOOC-R-COOH wherein R is an alkylene radical containing 1 to 10 carbon atoms, containing 2 to 10 carbon atoms and glycols, both having molecular weights of 400 to 2,000, in (3) x is a valence bond or a CH 2 radical, and the polyurethane contains (4) from 1 to 5 mole per mole of polyester or polyether of an aliphatic glycol or aliphatic ether glycol chain extender containing 2 to 10 carbon atoms, and in (B) the polyethers and polyesters are the same as the polyesters on (A) (1), the diisocyanate is the same as (A) (3), and the hydroxyacrylate and hydroxyalkacrylate have the formula ##STR8## wherein Z is hydrogen or an alkyl radical containing 1 to 4 carbon atoms or hydrogen, and R' is a divalent radical containing 2 to 8 carbon atoms.
Claim 5
Dependent Claim
65 words
The polyurethanes of claim 3 wherein in (1) the polyether x is 2 to 4, in the polyester acid R is 4 to 6 and the glycol is an alkylene glycol containing 2 to 6 carbon atoms and the (4) chain extender is an alkylene glycol containing 2 to 6 atoms, and in (B) the polyester and polyether are the same as in (A) (1).
Claim 6
Dependent Claim
54 words
A polyurethane of claim 4 wherein in (A) the (2) unsaturated polyether glycol is a copolyether of 0 to 95 mole percent of copolymerized tetrahydrofuran, 100 to 5 mole percent of ally or methallyl glycidyl ether and 0 to 50 mole percent alkylene oxide wherein the alkylene groups contains 2 to 3 carbon atoms.
Claim 7
Dependent Claim
126 words
A polyurethane of claim 5 wherein in (A) said (1) polyether glycol is poly(tetramethylene ether)glycol and said polyester glycol is poly(tetramethylene adipate)glycol, said (2) unsaturated polyether glycol contains about 40 to 60 mole percent copolymerized tetrahydrofuran with about 5 to 50 mole percent allyl glycidyl ether and 0 to 50 mole percent of ethylene oxide and has a molecular weight of about 400 to 1,400, (4) there is present about 1 to 5 moles of 1,4-butanediol per mole of polyether or polyester glycol and (3) there is less than 0.005 weight percent free unreacted isocyanate groups in the polyurethane and in (B) the polyether glycol is poly(tetramethylene ether)glycol, the said polyester glycol is poly(tetramethylene adipate)glycol, the diisocyanate is aromatic diisocyanate and the hydroxyacrylate is 2-hydroxyethyl acrylate.
Claim 8
Dependent Claim
39 words
A polyurethane of claim 4 wherein in (A) (2) the unsaturated polyether has one terminal hydroxyl and one terminal unsaturated group and are copolymer reaction products of tetrahydrofuran, an alkylene oxide and hydroxyethyl esters of acrylic or methacrylic acid.
Claim 9
Dependent Claim
130 words
A polyurethane of claim 6 wherein in (A) (1) said poly(tetramethylene adipate)glycol has a molecular weight of about 600 to 1,400, in (2) the unsaturated polyether glycol contains about 50 to 60 mole percent copolymerized tetrahydrofuran with about 5 to 50 mole percent allyl glycidyl ether and 0 to 40 mole percent of ethylene oxide, contains an average of 1 to 5 pendant double bond groups per molecule and has a molecular weight of about 500 to 1,400, present in amount of about 0.1 to 1.0 moles per mole of polyester glycol, (4) there is present about 1 to 5 moles of 1,4-butanediol per mole of polyester glycol and (3) is diphenylmethane-4,4'-diisocyanate, and (B) is the reaction product of poly(tetramethylene adipate)glycol with an excess of diphenylmethane-4,4'-diisocyanate, reacted with 2-hydroxyethyl acrylate.
Claim 10
Dependent Claim
113 words
A polyurethane of claim 6 wherein in (A) in (1) said poly(tetramethylene adipate)glycols, has a molecular weight from 600 to 1,400, in (2) the unsaturated polyether glycol contains about 60 mole percent copolymerized tetrahydrofuran with about 40 mole percent allyl glycidyl ether, about 1 to 3 pendant double bond groups per molecule and or molecular weight of about 500 to 1,400, present in amount of about 0.3 to 0.7 mole per mole of polyester glycol, (4) there is present about 1 to 5 moles of 1,4-butanediol per mole of polyester glycol and (3) is diphenylmethane-4,4'-diisocyanate and (B) is the reaction product of poly(tetramethylene adipate)glycol with an excess of diphenylmethane-4,4'-diisocyanate, reacted with 2-hydroxyethyl acrylate.
Claim 11
Dependent Claim
124 words
A polyurethane of claim 5 wherein said (1) polyether glycol is poly(tetramethylene ether)glycol, having a molecular weight of 600 to 1,400, (2) unsaturated polyether glycol contains about 50 to 60 mole percent copolymerized tetrahydrofuran with about 5 to 50 mole percent allyl glycidyl ether and 0 to 50 mole percent of ethylene oxide, about 1 to 5 pendant double bond groups and a molecular weight of about 500 to 1,400, present in amount of about 0.1 to 1.0 moles per mole of polyether glycol, (4) there is present about 1 to 5 moles of 1,4-butanediol per mole of polyether or polyester glycol and (3) is diphenylmethane-4,4'-diisocyanate and (B) is the reaction product of poly(tetramethylene adipate)glycol with an excess of diphenylmethane-4,4'-diisocyanate, reacted with 2-hydroxyethyl acrylate.
Claim 12
Dependent Claim
96 words
A polyurethane of claim 7 wherein the (2) unsaturated polyether containing one terminal hydroxyl group and one terminal double bond group is a copolyether of 30 to 65 mole percent of copolymerized tetrahydrofuran, 5 to 20 mole percent hydroxylethyl ester of acrylic or methacrylic acid and 30 to 50 mole percent alkylene oxide wherein the alkylene groups contains 2 to 4 carbon atoms, present in amount from 0.04 to 0.4 moles per mole of (1) polyether or polyester and (B) is the reaction product of poly(tetramethylene adipate)glycol with an excess of diphenylmethane-4,4'-diisocyanate, reacted with 2-hydroxyethyl acrylate.
Claim 13
Dependent Claim
93 words
A polyurethane of claim 11 wherein said (1) polyether glycol is poly(tetramethylene ether)glycol and said polyester glycol is poly(tetramethylene adipate)glycol, said (2) unsaturated polyether contains 35 to 50 mole percent of ethylene oxide and has a molecular weight of about 400 to 800, present in amount of about to 0.04 0.4 moles per mole of polyether or polyester glycol, (4) there is present about 1 to 5 moles of 1,4-butanediol per mole of polyether or polyester glycol and (3) there is less than one weight percent free unreacted isocyanate groups in the polyurethane.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-01 | 1987-10-31 | 1988-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-01 | 1991-10-31 | 1992-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-01 | 1995-10-31 | 1996-05-01 | $7700.00 | Window Closed / Lapsed |