Abstract A process for preparing an iron group sintered compact involves forming an admixture of an iron group metal alloy powder additive and iron powder wherein the melting point of the alloy additive is at least about 50° C. lower than that of the iron, compacting the admixture to form a green compact, and sintering the green compact at a temperature of from about 20° C. above the solidus to about 100° C. above the liquidus of the alloy additive whereby a sintered compact is formed. A compact having an iron group alloy additive as a continuous phase and iron as a discontinuous phase wherein the continuous phase has a melting point of at least about 50° C. lower than that of the discontinuous phase can be prepared at lower sintering temperatures than a typical iron powder.
Inventors
👤 Brian C. Coad
Bibliographic Details
Application Number—
JurisdictionUS
Data Sourcegoogle_patents
Last Synchronized2026-11-09 08:55
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0207
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
60 words
A compact having an iron group alloy additive selected from a nickel boron-silicon alloy having nickel as the major element and an iron-silicon-chromium-nickel alloy having iron as the major element as a continuous phase and iron as a discontinuous phase wherein said additive has a melting point of at least about 50° C. lower than that of the discontinuous phase.
Claim 2
Dependent Claim
60 words
A compact having an iron group alloy additive selected from a nickel boron-silicon alloy having nickel as the major element and an iron-silicon-chromium-nickel alloy having iron as the major element as a continuous phase and iron as a discontinuous phase wherein said additive has a melting point of at least about 50° C. lower than that of the discontinuous phase.
Claim 3
Dependent Claim
23 words
A compact according to claim 1 wherein the alloy additive melts at a temperature of from about 950° C. to about 1200° C.
Claim 4
Dependent Claim
33 words
A compact according to claim 1 wherein the alloy additive consists essentially of, by weight from about 3% to about 10% silicon, from about 2% to about 5% boron and the balance nickel.