Magnetically soft ferritic Fe-Cr-Ni alloys
Assignee: Nokia Bell Labs
•
Filing: 1982-10-28
•
Granted: 1985-09-10
•
Expires: 2002-10-28
Abstract
Abstract Disclosed are magnetically soft ferritic multiphase Fe-Cr-Ni alloys containing at least about 82 weight percent Fe, between about 3 and about 10 weight percent Cr, and between about 2 and about 8 weight percent Ni, a method for producing such alloys, and devices comprising such an alloy body. The method comprises a low-temperature anneal in the ( alpha + gamma ) region of the Fe-Cr-Ni phase diagram. Inventive alloys typically have a coercive force Hc no more than about 3.0 Oe, preferably no more than about 2.0 Oe, a maximum permeability mu m of at least about 1500 G/Oe, preferably at least about 2500 G/Oe, and contain at least about 5 volume percent non- alpha -phase material, typically alpha '- and gamma -phase material. Inventive alloys typically also have yield strength to 0.2% offset of at least about 26.107 Pa (40.103 psi), elongation to fracture of at least about 15%, good formability and rust resistance. Alloys according to the invention can advantageously be used in devices comprising a magnetically soft body, for instance, in electro-acoustic transducers, e.g., in telephone receivers, recording heads, pole pieces, and armatures.
Inventors
- 👤 Chester M. Boredelon
- 👤 Gilbert Y. Chin
- 👤 Sungho Jin
- 👤 Richard C. Sherwood
- 👤 Jack H. Wernick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:10
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; C; C22; C22C; C22C38/00; C22C38/18; C22C38/40
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
100 words
Device comprising a magnetically soft alloy body, the alloy having a coercive force H c of no more than about 3.0 Oe and a maximum permeability μ m of at least about 1,500 G/Oe, both measured at room temperature, characterized in that (a) the alloy comprises at least about 82 weight percent Fe, between about 3 and about 10 weight percent Cr, between about 2 and about 8 weight percent Ni, and (b) the alloy has a multiphase structure comprising α-phase material, with the amount of non-α-phase material present in the alloy body being at least about 5 volume percent.
Claim 2
Dependent Claim
100 words
Device comprising a magnetically soft alloy body, the alloy having a coercive force H c of no more than about 3.0 Oe and a maximum permeability μ m of at least about 1,500 G/Oe, both measured at room temperature, characterized in that (a) the alloy comprises at least about 82 weight percent Fe, between about 3 and about 10 weight percent Cr, between about 2 and about 8 weight percent Ni, and (b) the alloy has a multiphase structure comprising α-phase material, with the amount of non-α-phase material present in the alloy body being at least about 5 volume percent.
Claim 3
Dependent Claim
29 words
Device of claim 1, wherein the non-α-phase material present in the alloy body comprises at least one material selected from the group consisting of α'-phase material and γ-phase material.
Claim 4
Dependent Claim
24 words
Device of claim 1, wherein the alloy contains no element, other than Fe, Cr, and Ni, in an amount greater than 1 weight percent.
Claim 5
Dependent Claim
21 words
Device of claim 3, wherein the alloy comprises a combined amount of at least 99 weight percent Fe, Cr, and Ni.
Claim 6
Dependent Claim
23 words
Device of claim 4, wherein no element other than Fe, Cr, and Ni is present in an amount greater than 0.5 weight percent.
Claim 7
Dependent Claim
30 words
Device of claim 5, wherein the alloy contains no element of the group consisting of C, N, O, S, B and P in an amount greater than 0.1 weight percent.
Claim 8
Dependent Claim
23 words
Device of claim 1, wherein the alloy has a room temperature yield strength to 0.2% offset of at least about 26.10 7 Pa.
Claim 9
Dependent Claim
16 words
Device of claim 7, wherein the alloy has room temperature elongation of at least about 15%.
Claim 10
Dependent Claim
32 words
Device of claim 1, wherein the alloy has an incremental permeability Δμ of at least about 80 G/Oe, measured with an applied 1 kHz field of 0.005 Oe amplitude at room temperature.
Claim 11
Dependent Claim
44 words
Device of claim 1, wherein the alloy shows a weight gain of no more than about 0.3% after temperature-humidity cycling, between -40° C. and 66° C., and between 20% and 90% relative humidity, a 0.01 inch thick alloy foil in air for 14 days.
Claim 12
Dependent Claim
35 words
Device of claim 1, wherein the magnetically soft alloy body forms at least a part of a component whose position with respect to the device is dependent on strength or direction of a magnetic field.
Claim 13
Dependent Claim
14 words
Device of claim 11, wherein the magnetic field is produced by an induction coil.
Claim 14
Dependent Claim
11 words
Device of claim 12, wherein the device comprises an electro-acoustic transducer.
Claim 15
Dependent Claim
11 words
Device of claim 13, wherein the transducer is a telephone receiver.
Claim 16
Dependent Claim
201 words
A telephone receiver comprising a component whose position with respect to the receiver is dependent on strength or direction of a magnetic field, the component comprising a magnetically soft alloy body, the alloy having a coercive force H c of no more than about 2.0 Oe and a maximum permeability μ m of at least about 2500 G/Oe, both measured at room temperature, and a yield strength to 0.2% offset of at least about 35.10 7 Pa, characterized in that (a) the alloy comprises at least about 82 weight percent Fe, between about 3 and about 10 weight percent Cr, between about 2 and about 8 weight percent Ni, these three elements being present in the alloy in a combined amount of at least 99 weight percent, with no element other than Fe, Cr, and Ni being present in an amount greater than 0.5 weight percent, and no element of the group consisting of C, N, O, S, B and P being present in an amount greater than 0.1 weight percent, and (b) the alloy body has a multiphase structure comprising α-phase material, with the amount of non-α-phase material present in the alloy body being at least about 5 volume percent.
Claim 17
Dependent Claim
201 words
A telephone receiver comprising a component whose position with respect to the receiver is dependent on strength or direction of a magnetic field, the component comprising a magnetically soft alloy body, the alloy having a coercive force H c of no more than about 2.0 Oe and a maximum permeability μ m of at least about 2500 G/Oe, both measured at room temperature, and a yield strength to 0.2% offset of at least about 35.10 7 Pa, characterized in that (a) the alloy comprises at least about 82 weight percent Fe, between about 3 and about 10 weight percent Cr, between about 2 and about 8 weight percent Ni, these three elements being present in the alloy in a combined amount of at least 99 weight percent, with no element other than Fe, Cr, and Ni being present in an amount greater than 0.5 weight percent, and no element of the group consisting of C, N, O, S, B and P being present in an amount greater than 0.1 weight percent, and (b) the alloy body has a multiphase structure comprising α-phase material, with the amount of non-α-phase material present in the alloy body being at least about 5 volume percent.
Claim 18
Dependent Claim
92 words
Magnetically soft alloy having a coercive force H c of no more than about 3.0 Oe and a maximum permeability μ m of at least about 1500 G/Oe, both measured at room temperature, characterized in that (a) the alloy comprises at least about 82 weight percent Fe, between about 3 and about 10 weight percent Cr, between about 2 and about 8 weight percent Ni, and (b) the alloy has a multiphase structure comprising α-phase material, with the amount of non-α-phase material in the alloy being at least about 5 volume percent.
Claim 19
Dependent Claim
92 words
Magnetically soft alloy having a coercive force H c of no more than about 3.0 Oe and a maximum permeability μ m of at least about 1500 G/Oe, both measured at room temperature, characterized in that (a) the alloy comprises at least about 82 weight percent Fe, between about 3 and about 10 weight percent Cr, between about 2 and about 8 weight percent Ni, and (b) the alloy has a multiphase structure comprising α-phase material, with the amount of non-α-phase material in the alloy being at least about 5 volume percent.
Claim 20
Dependent Claim
65 words
Alloy of claim 1, wherein the combined amount of Fe, Cr, and Ni is at least about 99 weight percent, no element other than Fe, Cr, and Ni is present in an amount greater than about 0.5 weight percent, and no element of the group consisting of C, N, O, S, B and P is present in an amount greater than about 0.1 weight percent.
Claim 21
Dependent Claim
32 words
Alloy of claim 1, having a room temperature yield strength to 0.2% offset of at least about 26.10 7 Pa, and a room temperature elongation to fracture of at least about 15%.
Claim 22
Dependent Claim
50 words
Device of claim 1, wherein the alloy optionally comprises one or more additives chosen from the group consisting of Mn, Al, Zr, and Si, with no element other than Fe, Cr, Ni, and the optional additives being present in the alloy in an individual amount greater than 1 weight percent.
Claim 23
Dependent Claim
47 words
Alloy of claim 16 optionally comprising one or more additives chosen from the group consisting of Mn, Al, Zr, and Si, with no element other than Fe, Cr, Ni, and the optimal additives being present in the alloy in an individual amount greater than 1 weight percent.
References Cited (Backward Citations)
US2382654A
Cited
US3673010A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-09 | 1989-03-11 | 1989-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-09 | 1993-03-11 | 1993-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-09 | 1997-03-11 | 1997-09-10 | $7700.00 | Window Closed / Lapsed |