US
⏱️ 0.0 years remaining
Method of brazing with iron-based and hard surfacing alloys
Assignee: Osram Sylvania Inc
•
Filing: 1983-09-29
•
Granted: 1985-05-14
•
Expires: 2003-09-29
Abstract
Abstract Alloys consisting essentially of controlled amounts of boron, controlled amounts of silicon, and at least one element selected from Cr, Ni, Mn, Mo, V, W, Cb, Ti and when present these elements are present in the following amounts by weight from 0% to about 35% by weight of Cr, from 0 to about 25% by weight of Ni, from 0 to 12% by weight of Mn, from 0 to 5% by weight of Mo, from 0 to 5% by weight of V, from 0 to 15% by weight of W, from 0 to 3% by weight of Cb and from 0 to 2% by weight of Ti, balance of the alloy is iron in amounts greater than 50%. Such alloys are satisfactory brazing and hard surfacing alloys.
Inventors
- 👤 Brian C. Coad
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:08
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/3053; B23K35/308; B23K35/3086; B23K1/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
252 words
A method of brazing two similar ferrous based alloys substrates comprising: (a) determining the chromium, nickel, manganese, molybdenum, vanadium, tungsten, columbium, and a titannium content of said ferrous based substrates, (b) providing brazing alloy consisting essentially of from about 2% to about 6% by weight of boron, from about 5% to about 12% by weight of silicon and at least one element selected from the group consisting of chromium, nickel, manganese, molybdenum, vanadium, tungsten, columbium and titanium, said elements, when present, being present in an amount of up to about 35% by weight of chromium, and in an amount of up to about 25% by weight of nickel, up to about 12% by weight of manganese, up to about 5% by weight of molybdenum, up to about 5% by weight of vanadium, up to about 15% by weight of tungsten, up to about 3% by weight of columbium and up to about 2% by weight of titanium, the balance of said alloy being iron in amounts greater than about 50% by weight of said alloy wherein said chromium, nickel, manganese, molybdenum, vanadium, tungsten, columbium and titanium are at approximately the same weight level as these elements are present in the ferrous based alloys substrate being brazed, (c) providing a mutual contact between said alloy and said substrates to achieve an assembly, (d) heating said assembly to at least the liquidus temperature of said brazing alloy for a sufficient time to achieve flow, and (e) cooling said brazed assembly to the ambient temperature.
Claim 2
Independent Claim
252 words
A method of brazing two similar ferrous based alloys substrates comprising: (a) determining the chromium, nickel, manganese, molybdenum, vanadium, tungsten, columbium, and a titannium content of said ferrous based substrates, (b) providing brazing alloy consisting essentially of from about 2% to about 6% by weight of boron, from about 5% to about 12% by weight of silicon and at least one element selected from the group consisting of chromium, nickel, manganese, molybdenum, vanadium, tungsten, columbium and titanium, said elements, when present, being present in an amount of up to about 35% by weight of chromium, and in an amount of up to about 25% by weight of nickel, up to about 12% by weight of manganese, up to about 5% by weight of molybdenum, up to about 5% by weight of vanadium, up to about 15% by weight of tungsten, up to about 3% by weight of columbium and up to about 2% by weight of titanium, the balance of said alloy being iron in amounts greater than about 50% by weight of said alloy wherein said chromium, nickel, manganese, molybdenum, vanadium, tungsten, columbium and titanium are at approximately the same weight level as these elements are present in the ferrous based alloys substrate being brazed, (c) providing a mutual contact between said alloy and said substrates to achieve an assembly, (d) heating said assembly to at least the liquidus temperature of said brazing alloy for a sufficient time to achieve flow, and (e) cooling said brazed assembly to the ambient temperature.
Claim 3
Dependent Claim
21 words
A method according to claim 1, wherein said brazing alloy contains from about 10% to about 35% by weight of chromium.
Claim 4
Dependent Claim
27 words
A method according to claim 1, wherein said brazing alloy contains from about 11% to about 13% by weight chromium and said ferrous based alloy is 410SS.
Claim 5
Dependent Claim
39 words
An alloy according to claim 1, wherein said alloy is particularly suitable for brazing 304 stainless steel and contains from about 17% to 19% by weight of chromium and from about 75 to about 9% by weight of nickel.
Claim 6
Dependent Claim
28 words
A method according to claim 1, wherein said brazing alloy contains from about 17% to about 19% chromium and from about 1.5% to 2.5% by weight of molybdenum.
Claim 7
Dependent Claim
18 words
A method according to claim 1 wherein said brazing alloy contains from about 5% to about 10% silicon.
References Cited (Backward Citations)
US3736128A
Cited
US3836358A
Cited
SU490861A1
Cited
JPS5335618A
Cited
JPS5423020A
Cited
JPS55148701A
Cited
US4402742A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-05-13 | 1988-11-12 | 1989-05-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-05-13 | 1992-11-12 | 1993-05-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-05-13 | 1996-11-12 | 1997-05-14 | $7700.00 | Window Closed / Lapsed |