Process for the manufacture of shaped articles from reaction-bonded silicon nitride by nitridation under elevated nitrogen gas pressure
Assignee: ELEKROSCHMELZWERK KEMPTEN GmbH
•
Filing: 1986-04-11
•
Granted: 1987-08-18
•
Expires: 2006-04-11
Abstract
Abstract The invention is a process for the manufacture of shaped articles of reaction-bonded silicon nitride in which pre-shaped articles of silicon powder are heated in a first stage under a nitrogen gas pressure of at least 6 MPa at a heating rate of not more than 50° C. per hour to a reaction temperature below the melting point of silicon, the article is maintained at the reaction temperature for at least 0.5 hours and subsequently, in a second stage, heating the article at a heating rate of at least 500° C. per hour to a temperature above the melting point of silicon and maintaining the article at that temperature for from 1 to 7 hours. The process can nitridate both pre-shaped articles consisting of silicon powder and, optionally, up to 15% by weight Si 3 N 4 powder and those containing up to 10% by weight of a sintering aid such as Y 2 O 3 . In the former case, porous shaped articles having a density of from 87 to 91% TD and, in the latter case, dense shaped articles having a density of more than 98% TD, are obtained. In all cases, in a total nitridation time of less than 15 hours, a conversion of at least 95% of the silicon originally present into silicon nitride is achieved, which, in the finished shaped article, is substantially in the β-modification.
Inventors
- 👤 Klaus Hunold
- 👤 Alfred Lipp
- 👤 Klaus Reinmuth
- 👤 Peter Arnold
- 👤 Johannes Napholcz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 18:56
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/591; C04B35/593; C04B35/5935; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3205; C04B2235/3206; C04B2235/3217; C04B2235/3224; C04B2235/3225; C04B2235/327; C04B2235/3272; C04B2235/38; C04B2235/3852; C04B2235/3873; C04B2235/3895; C04B2235/42; C04B2235/428; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/5445; C04B2235/65; C04B2235/656; C04B2235/6562; C04B2235/6567; C04B2235/66; C04B2235/661; C04B2235/70; C04B2235/72; C04B2235/728; C04B2235/74; C04B2235/77
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
211 words
A process for the manufacture of shaped articles of reaction bonded silicon nitride by nitridation of preshaped articles of silicon powder which comprises (a) placing the preshaped article of silicon powder in the furnace chamber of a pressure vessel, applying a nitrogen gas pressure of at least 6 MPa to said preshaped article in the pressure vessel and increasing the temperature at a heating rate of not more than 50° C. per hour to a reaction temperature below the melting point of silicon at which the reaction of the nitrogen with the silicon occurs; (b) maintaining said preshaped article at the reaction temperature below the melting point of silicon and under the nitrogen gas pressure of at least 6 MPa in the pressure vessel for at least 0.5 hours to form a prenitridated article; (c) heating said prenitridated article at a heating rate of at least 500° C. per hour to a final temperature above the melting point of silicon and maintaining said prenitridated article at the temperature above the melting point of silicon and under the nitrogen gas pressure of at least 6 MPa in the pressure vessel for from 1 to 7 hours until at least 95 percent of the silicon originally present have been converted into silicon nitride.
Claim 2
Dependent Claim
211 words
A process for the manufacture of shaped articles of reaction bonded silicon nitride by nitridation of preshaped articles of silicon powder which comprises (a) placing the preshaped article of silicon powder in the furnace chamber of a pressure vessel, applying a nitrogen gas pressure of at least 6 MPa to said preshaped article in the pressure vessel and increasing the temperature at a heating rate of not more than 50° C. per hour to a reaction temperature below the melting point of silicon at which the reaction of the nitrogen with the silicon occurs; (b) maintaining said preshaped article at the reaction temperature below the melting point of silicon and under the nitrogen gas pressure of at least 6 MPa in the pressure vessel for at least 0.5 hours to form a prenitridated article; (c) heating said prenitridated article at a heating rate of at least 500° C. per hour to a final temperature above the melting point of silicon and maintaining said prenitridated article at the temperature above the melting point of silicon and under the nitrogen gas pressure of at least 6 MPa in the pressure vessel for from 1 to 7 hours until at least 95 percent of the silicon originally present have been converted into silicon nitride.
Claim 3
Dependent Claim
42 words
The process of claim 1 wherein a pre-shaped article of silicon powder and up to 15% by weight of the silicon nitride powder are nitrided to form a shaped silicon nitride article having a density of from about 87 to 91% TD.
Claim 4
Dependent Claim
46 words
The process of claim 1 wherein the preshaped article of silicon contains up to 10% by weight of at least one sintering aid selected from the group consisting of MgO, Y 2 O 3 , Al 2 O 3 , Fe 2 O 3 and BeO.
Claim 5
Dependent Claim
46 words
The process of claim 2 wherein the preshaped article of silicon contains up to 10% by weight of at least one sintering aid selected from the group consisting of MgO, Y 2 O 3 , Al 2 O 3 , Fe 2 O 3 and BeO.
Claim 6
Dependent Claim
29 words
The process of claim 3 wherein after the reacted article has been heated to at least about 1700° C., the nitrogen pressure is increased to at least 150 MPa.
Claim 7
Dependent Claim
20 words
The process of claim 1 wherein the pressure vessel is flushed with nitrogen while the pre-shaped article is being heated.
Claim 8
Dependent Claim
24 words
The process of claim 6 wherein the pressure vessel is flushed with nitrogen until the temperature of the preshaped article reaches about 400° C.
Claim 9
Dependent Claim
15 words
The process of claim 7 wherein the pressure vessel is evacuated and filled with nitrogen.
Claim 10
Dependent Claim
35 words
The process of claim 1 wherein the preshaped article is maintained at a temperature of from about 50° to 100° C. below the reaction temperature for a period of from about 0.5 to 3 hours.
Claim 11
Dependent Claim
35 words
The process of claim 3 wherein the preshaped article is maintained at a temperature of from about 50° to 100° C. below the reaction temperature for a period of from about 0.5 to 3 hours.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-17 | 1991-02-16 | 1991-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-17 | 1995-02-16 | 1995-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-17 | 1999-02-16 | 1999-08-18 | $7700.00 | Window Closed / Lapsed |