Assignee: Ceradyne Inc
•
Filing: 1979-09-24
•
Granted: 1981-08-25
•
Expires: 1999-09-24
Abstract
Abstract A method of densifying a reaction bonded silicon nitride article is disclosed. In accordance with the broadest principles disclosed, a densification aid is incorporated into a reaction bonded silicon nitride article. The so-made reaction bonded silicon nitride article is enclosed in a chamber which also contains a mixture of silicon nitride powder and powder the same as the densification aid incorporated into the reaction bonded silicon nitride article. The reaction bonded silicon nitride article, and the powder mixture associated therewith, is subjected to a nitrogen gas pressure sufficient to prohibit a significant volatilization of silicon nitride at a sintering temperature. The reaction bonded silicon nitride article, the powder mixture and nitrogen gas associated therewith are heated to a temperature above 1700° C. for a time sufficient to permit sintering of that article whereby the strength of the reaction bonded silicon nitride article is increased. In accordance with preferred teachings, the densification aid can be selected from the group of materials consisting of magnesium oxide, yttrium oxide, cerium oxide and zirconium oxide.
Inventors
- 👤 John A. Mangels
- 👤 Gerald J. Tennenhouse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:37
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593; C04B35/5935
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
117 words
A method of densifying a reaction bonded silicon nitride article which comprises: packing the reaction bonded silicon nitride article in a packing mixture consisting of silicon nitride powder and a densification aid; subjecting the reaction bonded silicon nitride article and packing mixture to a nitrogen gas pressure sufficient to prohibit a significant volatilization of silicon nitride at a sintering temperature; and heating the reaction bonded silicon nitride article, packing mixture and nitrogen gas present to a sintering temperature above 1700° C. for a time sufficient to permit migration of said densification aid into the reaction bonded silicon nitride article and a sintering of that article whereby the strength of the reaction bonded silicon nitride article is increased.
Claim 2
Independent Claim
117 words
A method of densifying a reaction bonded silicon nitride article which comprises: packing the reaction bonded silicon nitride article in a packing mixture consisting of silicon nitride powder and a densification aid; subjecting the reaction bonded silicon nitride article and packing mixture to a nitrogen gas pressure sufficient to prohibit a significant volatilization of silicon nitride at a sintering temperature; and heating the reaction bonded silicon nitride article, packing mixture and nitrogen gas present to a sintering temperature above 1700° C. for a time sufficient to permit migration of said densification aid into the reaction bonded silicon nitride article and a sintering of that article whereby the strength of the reaction bonded silicon nitride article is increased.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein: said densification aid is selected from the group consisting of magnesium oxide, yttrium oxide, cerium oxide and zirconium oxide.
Claim 4
Independent Claim
31 words
The method of claims 1 or 2 wherein: said packing mixture consists of from 4 to 20% by weight of said densification aid, the balance consisting essentially of silicon nitride powder.
Claim 5
Dependent Claim
37 words
The method of claim 1 wherein: prior to packing the reaction bonded silicon nitride article in said packing mixture the silicon nitride article is impregnated with the same densification aid which is used in said packing mixture.
Claim 6
Dependent Claim
15 words
The method of claim 4 wherein: the metallic component of said densification aid is magnesium.
Claim 7
Dependent Claim
81 words
The method of claim 1 wherein: the reaction bonded silicon nitride article, said packing mixture, and said nitrogen gas present are heated to a sintering temperature in a range above 1700° C. to no more than 1950° C. wherein a hold time at reaction temperature is for a period of time from one-half hour to four hours, and wherein said nitrogen gas pressure is in a range from about 250 lbs. per square inch to about 1500 lbs. per square inch.
Claim 8
Independent Claim
87 words
A method of densifying a reaction bonded silicon nitride article which comprises: incorporating a densification aid into a reaction bonded silicon nitride article; enclosing the reaction bonded silicon nitride article in a chamber also containing a mixture of silicon nitride powder and powder the same as the densification aid incorporated into the reaction bonded silicon nitride article; subjecting the reaction bonded silicon nitride article and the powder mixture to a nitrogen gas pressure sufficient to prohibit a significant volatilization of silicon nitride at a sintering temperature; and
Claim 9
Independent Claim
87 words
A method of densifying a reaction bonded silicon nitride article which comprises: incorporating a densification aid into a reaction bonded silicon nitride article; enclosing the reaction bonded silicon nitride article in a chamber also containing a mixture of silicon nitride powder and powder the same as the densification aid incorporated into the reaction bonded silicon nitride article; subjecting the reaction bonded silicon nitride article and the powder mixture to a nitrogen gas pressure sufficient to prohibit a significant volatilization of silicon nitride at a sintering temperature; and
Claim 10
Dependent Claim
43 words
heating the reaction bonded silicon nitride article, the powder mixture and the nitrogen gas present to a temperature above 1700° C. for a time sufficient to permit sintering of that article whereby the strength of the reaction bonded silicon nitride article is increased.
Claim 11
Dependent Claim
43 words
heating the reaction bonded silicon nitride article, the powder mixture and the nitrogen gas present to a temperature above 1700° C. for a time sufficient to permit sintering of that article whereby the strength of the reaction bonded silicon nitride article is increased.
Claim 12
Dependent Claim
38 words
The method of claim 7 wherein: the reaction bonded silicon nitride article is made by a method wherein starting materials for the article are injection molded and the densification aid is included as one of the starting materials.
Claim 13
Dependent Claim
38 words
The method of claim 7 wherein: the reaction bonded silicon nitride article is made by a method wherein starting materials for the article are slip cast and the densification aid is included as one of the starting materials.
Claim 14
Dependent Claim
45 words
The method of claim 7 wherein: the reaction bonded silicon nitride article is made by a method wherein the shape of the article is formed in a slip cast operation and the densification aid is incorporated in the article after formation but before nitriding thereof.
Claim 15
Independent Claim
25 words
The method of claims 7, 8, 9 or 10 wherein: the mixture contained in the chamber is packed about the reaction bonded silicon nitride article.
References Cited (Backward Citations)
US4071372A
Cited
US3992497A
Cited
US4038092A
Cited
US4119690A
Cited
US4112143A
Cited
US4179486A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-24 | 1985-02-23 | 1985-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-24 | 1989-02-23 | 1989-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-24 | 1993-02-23 | 1993-08-25 | $7700.00 | Window Closed / Lapsed |