Cat box litter and process for producing same
Assignee: Individual
•
Filing: 1984-12-11
•
Granted: 1987-08-18
•
Expires: 2004-12-11
Abstract
Abstract A process is provided herein for making absorptive pellets from clay "fines" having open pore spaces therein, the fines including clay particles that will pass through a 30-50 mesh screen. The process includes the steps of (a) mixing the clay "fines" in a mixing apparatus with an aqueous solution of lignin; then (b) transferring the moistened clay-lignin particles from the mixing apparatus to a disc pelletizer having a screw conveyor to feed the moistened clay-lignin particles to a die, the die including a die stiffener ring, a roll assembly, an adjustable feed plow and a rapid pelletizing cartridge; and finally (c) forcing the moistened clay-lignin particles through the die to compact and to form the clay-lignin particles into a coherent mass of material and cutting that coherent mass from the die to form the material into pellets, the forcing through the disc pelletizer being under selected conditions of shear substantially simultaneously to compact the clay-lignin particles into the coherent mass and to flash-off excess moisture to provide pellets having a maximum of about 5% by weight moisture and so that a subsequent drying step is therefore unnecessary. The pellets so formed may be used as cat box litter, since they are absorptive pellets having an absorption capacity in the open pore spaces approaching the capacity of the clay "fines" starting material, i.e. about 90-95% of the pore volume of the clay fines. It is believed that the lignin expands during the drying process to improve the pore volume of the pellets.
Inventors
- 👤 John Rosenfeld
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:13
CPC Classifications
A; A01; A01K; A01K1/00; A01K1/015; A01K1/0152; A01K1/0154; A01K1/0155
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
207 words
A process for making pellets from clay "fines" having open pore spaces therein, said fines including particles that will pass through a 30-50 mesh screen, said process comprising: a. mixing said clay "fines" in a mixing apparatus with an aqueous solution of lignin; b. transferring said moistened clay-lignin particles from said mixing apparatus to a disc pelletizer having a die and a screw conveyor to feed said moistened clay-lignin particles to said die, said die including a die stiffener ring, a roll assembly, an adjustable feed plow and a rapid pelletizing cartridge; and c. forcing said moistened clay-lignin particles through said die to compact and to form said clay-lignin into particles into a coherent mass of material and cutting said coherent mass from said die to form said material into pellets, said forcing through said disc pelletizer being under selected conditions of shear, substantially simultaneously to compact said clay-lignin particles into said coherent mass and to flash-off excess moisture to provide pellets having a maximum of about 5% by weight moisture, a subsequent drying step therefore being rendered unnecessary; said pellets having open pore spaces therein and a liquid absorptive capacity in said open pore spaces substantially equal to the capacity of said clay "fines" starting material.
Claim 2
Dependent Claim
207 words
A process for making pellets from clay "fines" having open pore spaces therein, said fines including particles that will pass through a 30-50 mesh screen, said process comprising: a. mixing said clay "fines" in a mixing apparatus with an aqueous solution of lignin; b. transferring said moistened clay-lignin particles from said mixing apparatus to a disc pelletizer having a die and a screw conveyor to feed said moistened clay-lignin particles to said die, said die including a die stiffener ring, a roll assembly, an adjustable feed plow and a rapid pelletizing cartridge; and c. forcing said moistened clay-lignin particles through said die to compact and to form said clay-lignin into particles into a coherent mass of material and cutting said coherent mass from said die to form said material into pellets, said forcing through said disc pelletizer being under selected conditions of shear, substantially simultaneously to compact said clay-lignin particles into said coherent mass and to flash-off excess moisture to provide pellets having a maximum of about 5% by weight moisture, a subsequent drying step therefore being rendered unnecessary; said pellets having open pore spaces therein and a liquid absorptive capacity in said open pore spaces substantially equal to the capacity of said clay "fines" starting material.
Claim 3
Dependent Claim
30 words
The process of claim 1 wherein said aqueous solution of lignin is provided in the range of about 8 to about 15 lbs based on 100 lbs of clay "fines".
Claim 4
Dependent Claim
31 words
The process of claim 2 wherein said aqueous solution of lignin is provided in the range of about 8 to about 121/2 lbs based on each 100 lbs of clay "fines".
Claim 5
Dependent Claim
46 words
The process of claim 1 for the making of said pellets to be used as a cat box absorbent, wherein calcined clay "fines" are used, said clay "fines" having said open pore spaces therein including particles of a size to pass through a 30 mesh screen.
Claim 6
Dependent Claim
63 words
The process of claim 1 for the making of said pellets to be used as a cat box absorbent wherein calcined clay "fines" are used having said open pore spaces therein, and including particles of a size to pass through a 30 mesh screen; and further wherein at least one of a deodorizer, a batericide, an antioxidant, and a mold inhibitor is included.
Claim 7
Dependent Claim
54 words
The process of claim 1 for the making of said pellets to be used as a cat box absorbent, wherein calcined clay "fines" are used having said open pore spaces therein and including particles of a size to pass through a 30 mesh screen; and further wherein said pellets are approximately 1/16"-3/16" in size.
Claim 8
Dependent Claim
60 words
The process of claim 1 for the making of said pellets to be used as a cat box absorbent wherein calcined clay "fines" are used having said open pore spaces therein, and including particles of a size to pass through a 30 mesh screen; said clay "fines" being of Georgia clay [Al 2 O 3 .2SiO 2 .2H 2 O].
Claim 9
Dependent Claim
23 words
Absorbent pellets made by the process of claim 1 comprising an extruded, dried-in-situ mixture of clay "fines" and an aqueous solution of lignin.
Claim 10
Dependent Claim
18 words
The absorbent pellets of claim 8 wherein said clay "fines" are of a size passing through 30 mesh.
Claim 11
Dependent Claim
29 words
The absorbent pellets of claim 8 wherein the amount of aqueous solution of lignin is about 8 to about 15 lbs based on each 100 lbs of clay "fines".
Claim 12
Dependent Claim
29 words
The absorbent pellets of claim 10 wherein the amount of aqueous solution of lignin is about 8 to about 121/2 lbs based on each 100 lbs of clay "fines".
Claim 13
Dependent Claim
21 words
The absorbent pellets of claim 8 wherein said clay is Georgia clay [Al 2 O 3 ,2SiO 2 .2H 2 O].
Claim 14
Dependent Claim
31 words
The absorbent pellets of claim 8 including at least one of a deodorizer, a bactericide, an antioxidant, and a mold inhibitor to provide cat litter box absorbent pellets containing the same.
Claim 15
Dependent Claim
48 words
The absorbent pellets of claim 8, wherein said clay is Georgia clay (Al 2 O 3 .2SiO 2 .2H 2 O) and further including at least one of a deodorizer, a bactericide, an antioxidant, and a mold inhibitor to provide cat box litter absorbent pellets containing the same.
Claim 16
Dependent Claim
178 words
A continuous method for the preparation of absorbent pellets comprising: 1. continuously transferring clay "fines" to a bulk storage area and continuously transferring said clay "fines" to a disc pelletizer having a screw conveyor and a die, said die including a die stiffener ring, a roll assembly, an adjustable feed plow and a rapid pelletizing cartridge; 2. continuously transferring an aqueous solution of lignin to said disc pelletizer; 3. continuously mixing said clay "fines" with said aqueous solution of lignin to form a moistened mixture of clay-lignin particles; and 4. continuously forcing said moistened mixture of clay-lignin particles through said die to compact and to form said clay-lignin into a coherent mass of material and cutting said coherent mass from said die to form said coherent mass into pellets, said forcing through said die being under selected conditions of shear substantially simultaneously to compact said moistened clay-lignin particles into said coherent mass and to flash-off excess moisture to provide pellets having a maximum of about 5% by weight moisture so that a subsequent drying step is rendered unnecessary.
Claim 17
Dependent Claim
178 words
A continuous method for the preparation of absorbent pellets comprising: 1. continuously transferring clay "fines" to a bulk storage area and continuously transferring said clay "fines" to a disc pelletizer having a screw conveyor and a die, said die including a die stiffener ring, a roll assembly, an adjustable feed plow and a rapid pelletizing cartridge; 2. continuously transferring an aqueous solution of lignin to said disc pelletizer; 3. continuously mixing said clay "fines" with said aqueous solution of lignin to form a moistened mixture of clay-lignin particles; and 4. continuously forcing said moistened mixture of clay-lignin particles through said die to compact and to form said clay-lignin into a coherent mass of material and cutting said coherent mass from said die to form said coherent mass into pellets, said forcing through said die being under selected conditions of shear substantially simultaneously to compact said moistened clay-lignin particles into said coherent mass and to flash-off excess moisture to provide pellets having a maximum of about 5% by weight moisture so that a subsequent drying step is rendered unnecessary.
Claim 18
Dependent Claim
27 words
The continuous method of claim 15 including the steps of 5. continuously transferring said pellets to a pellet bulk storage area and 6. continuously bagging said pellets.
Claim 19
Dependent Claim
21 words
The continuous method of claim 15 including the step of providing air filter means associated with said pellet bulk storage area.
Claim 20
Dependent Claim
23 words
The continuous method of claim 15 wherein said clay "fines" are transferred to such bulk storage area by means of a vacuum pump.
Claim 21
Dependent Claim
21 words
The continuous method of claim 15 including the step of providing a dust collecting area associated with said bulk storage area.
Claim 22
Dependent Claim
24 words
The continuous method of claim 15 including the step of providing externally generated heat to said pelletizing apparatus to assist in drying said pellets.
References Cited (Backward Citations)
US3244635A
Cited
US4187803A
Cited
US3789797A
Cited
US4206718A
Cited
US4163674A
Cited
US4157696A
Cited
US4278047A
Cited
US4506628A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-17 | 1991-02-16 | 1991-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-17 | 1995-02-16 | 1995-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-17 | 1999-02-16 | 1999-08-18 | $7700.00 | Window Closed / Lapsed |