Degradable agricultural plastic articles, e.g., mulching film, comprising slowly released multinutrients in matrix of thermoplastic, and process for preparing same
Assignee: Kuwait Institute for Scientific Research
•
Filing: 1985-10-29
•
Granted: 1987-08-18
•
Expires: 2005-10-29
Abstract
Abstract An agricultural mulch film is prepared by mixing conventional plant nutrients with a water-soluble polymer such as polyvinyl alcohol. The mixture is cast in the liquid form and allowed to dry to form a thin film. The dried film is then coated with a thin layer of a water-resistant resin such as polyvinyl acetate to form a composite mulch film. The release of the nutrients contained in the mulch film is controlled by the addition to the water-soluble polymer mixture of either (1) a nitrification inhibitor along with urea, or (2) a water-soluble urea-formaldehyde condensation product. The release of the nutrients is also controlled somewhat by the water-resistant resin coating. Other additives may be added to the mulch film to produce a multi-purpose product.
Inventors
- 👤 Shawqui Lahalih
- 👤 Saed-el-Deen Akashah
- 👤 Farouk Al-Hajjar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:18
CPC Classifications
A; A01; A01G; A01G13/00; A01G13/30; A01G13/32; A01G13/33; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/3192
Claims Analysis
Total Claims: 47
Claim 1
Independent Claim
117 words
A self-supporting, composite, degradable agricultural mulch film, which comprises: (a) a first film formed from a water-soluble synthetic resin and having admixed therein at least one releasable form of nitrogen, at least one releasable plant nutrient in addition to nitrogen, and at least one agent which functions to slow the release of nitrogen from said first film; and (b) a second film formed as an adherent coating on said first film, said second film comprising a water-resistant synthetic resin, said second film functioning to retard the degradation rate of the composite mulch film, to further slow the rate of release of said nitrogen, and to slow the rate of release of said plant nutrient other than nitrogen.
Claim 2
Dependent Claim
117 words
A self-supporting, composite, degradable agricultural mulch film, which comprises: (a) a first film formed from a water-soluble synthetic resin and having admixed therein at least one releasable form of nitrogen, at least one releasable plant nutrient in addition to nitrogen, and at least one agent which functions to slow the release of nitrogen from said first film; and (b) a second film formed as an adherent coating on said first film, said second film comprising a water-resistant synthetic resin, said second film functioning to retard the degradation rate of the composite mulch film, to further slow the rate of release of said nitrogen, and to slow the rate of release of said plant nutrient other than nitrogen.
Claim 3
Dependent Claim
30 words
The agricultural mulch of claim 1, wherein said water-soluble synthetic resin comprises polyvinyl alcohol, and wherein said polyvinyl alcohol comprises from about 20% to about 85% of said first film.
Claim 4
Dependent Claim
27 words
The agricultural mulch of claim 2, wherein said polyvinyl alcohol has a molecular weight ranging from about 14,000-100,000 and a degree of hydrolysis ranging from about 86-100%.
Claim 5
Dependent Claim
34 words
The agricultural mulch film of claim 3, wherein said first film has a thickness on the order of about 0.1-0.25 mm, and wherein said composite film is free from any black pigment or filler.
Claim 6
Dependent Claim
31 words
The agricultural mulch of claim 2, wherein said water-resistant resin is selected from the group consisting of polyvinyl acetate, plasticized polyvinyl chloride, ethylene/acrylic acid copolymers, and ethylene/ethylacrylate copolymers, and mixtures thereof.
Claim 7
Dependent Claim
21 words
The agricultural mulch of claim 5, wherein said second film comprises up to about 15% by weight of the composite film.
Claim 8
Dependent Claim
24 words
The agricultural mulch of claim 6, wherein said water-resistant resin comprises polyvinyl acetate having a molecular weight in the range of from about 45,000-160,000.
Claim 9
Dependent Claim
39 words
The agricultural mulch of claim 6, wherein said releasable plant nutrient comprises at least one member selected from the group consisting of phosphoric acid, potassium salts and complexes, phosphate salts and complexes, nitrate salts and complexes and mixtures thereof.
Claim 10
Dependent Claim
52 words
The agricultural much of claim 2, wherein said releasable form of nitrogen comprises at least one member selected from the group consisting of urea, water-soluble urea-formaldehyde condensates, and mixtures thereof; provided, however, that when urea is present as the only releasable form of nitrogen, said first film further comprises a nitrification inhibitor.
Claim 11
Dependent Claim
41 words
The agricultural mulch of claim 9, wherein said releasable form of nitrogen comprises urea, and wherein said first film further comprises a nitrification inhibitor, said urea being present in said first film in an amount up to about 35% by weight.
Claim 12
Dependent Claim
31 words
The agricultural mulch of claim 10, wherein said nitrification inhibitor is thiourea, and wherein said thiourea is present in said first film in an amount up to about 2% by weight.
Claim 13
Dependent Claim
22 words
The agricultural mulch film of claim 11, wherein said second film comprises up to about 15% by weight of the composite film.
Claim 14
Dependent Claim
23 words
The agricultural mulch of claim 12, wherein said second film comprises from about 2% to about 12% by weight of the composite film.
Claim 15
Dependent Claim
31 words
The agricultural mulch of claim 13, wherein said water-resistant resin is selected from the group consisting of polyvinyl acetate, plasticized polyvinyl chloride, ethylene/acrylic acid copolymers, and ethylene/ethylacrylate copolymers, and mixtures thereof.
Claim 16
Dependent Claim
37 words
The agricultural mulch of claim 9, wherein said releasable form of nitrogen comprises a water-soluble urea-formaldehyde condensate, and wherein said urea-formaldehyde condensate is present in said first film in an amount up to about 70% by weight.
Claim 17
Dependent Claim
23 words
The agricultural mulch of claim 9, wherein said first film comprises 0-35% urea, 0-70% water-soluble urea-formaldehyde condensate, and from about 15-25% phosphoric acid.
Claim 18
Dependent Claim
21 words
The agricultural mulch of claim 16, wherein said second film comprises up to about 15% by weight of the composite film.
Claim 19
Dependent Claim
21 words
The agricultural mulch of claim 17, wherein said second film comprises from about 2% to about 12% of the composite film.
Claim 20
Dependent Claim
31 words
The agricultural mulch of claim 18, wherein said water-resistant resin is selected from the group consisting of polyvinyl acetate, plasticized polyvinyl chloride, ethylene/acrylic acid copolymers, and ethylene/ethylacrylate copolymers, and mixtures thereof.
Claim 21
Dependent Claim
150 words
A clear, degradable agricultural mulch film which is substantially free from any black pigments or fillers, which comprises: (a) a first film formed from a water-soluble synthetic resin; and (b) a second film formed from a water-resistant synthetic resin and coated on said first film such that said first film and said second film define the clear, degradable agricultural mulch film; said first film comprising, in addition to said water-soluble resin, at least one nitrogeneous source, at least one releasable plant nutrient other than said nitrogeneous source, and at least one constituent which functions to slow the release of nitrogen from said mulch film during use; said second film comprising up to about 15% by weight of said mulch film and functioning to delay the degradation of said mulch film and to cooperate with said constituent in said first film for slowing the release of nitrogen from said mulch film.
Claim 22
Dependent Claim
150 words
A clear, degradable agricultural mulch film which is substantially free from any black pigments or fillers, which comprises: (a) a first film formed from a water-soluble synthetic resin; and (b) a second film formed from a water-resistant synthetic resin and coated on said first film such that said first film and said second film define the clear, degradable agricultural mulch film; said first film comprising, in addition to said water-soluble resin, at least one nitrogeneous source, at least one releasable plant nutrient other than said nitrogeneous source, and at least one constituent which functions to slow the release of nitrogen from said mulch film during use; said second film comprising up to about 15% by weight of said mulch film and functioning to delay the degradation of said mulch film and to cooperate with said constituent in said first film for slowing the release of nitrogen from said mulch film.
Claim 23
Dependent Claim
115 words
The agricultural mulch of claim 20, wherein said nitrogeneous source comprises at least one member selected from the group consisting of urea, water-soluble urea-formaldehyde condensates, and mixtures thereof, wherein said urea may be present in said first film in an amount up to about 35% by weight, wherein said urea-formaldehyde condensate may be present in said first film in an amount up to about 70% by weight, wherein said water-soluble resin is present in said first film in an amount of from about 20% to about 85%, and wherein said first film further comprises up to about 2% by weight of a nitrification inhibitor when urea comprises the only nitrogeneous source in said first film.
Claim 24
Dependent Claim
12 words
The agricultural mulch of claim 21, wherein said nitrification inhibitor is thiourea.
Claim 25
Dependent Claim
13 words
The agricultural mulch of claim 21, wherein said water-soluble resin comprises polyvinyl alcohol.
Claim 26
Dependent Claim
39 words
The agricultural mulch of claim 21, wherein said releasable plant nutrient comprises at least one member selected from the group consisting of phosphoric acid, potassium salts and complexes, phosphate salts and complexes, nitrate salts and complexes and mixtures thereof.
Claim 27
Dependent Claim
31 words
The agricultural mulch of claim 23, wherein said water-resistant resin is selected from the group consisting of polyvinyl acetate, plasticized polyvinyl chloride, ethylene/acrylic acid copolymers, and ethylene/ethylacrylate copolymers, and mixtures thereof.
Claim 28
Dependent Claim
27 words
The agricultural mulch of claim 25, wherein said polyvinyl alcohol has a molecular weight ranging from about 14,000-100,000 and a degree of hydrolysis ranging from about 86-100%.
Claim 29
Independent Claim
145 words
A method of preparing a clear, multi-nutrient-containing degradable agricultural mulch film, which comprises the steps of: (a) forming an aqueous admixture comprising a water-soluble synthetic film-forming resin, at least one nitrogeneous constituent which functions as a releasable source of nitrogen, and at least one plant nutrient in addition to said nitrogeneous constituent; (b) casting a film from the admixture resulting from step (a); (c) drying the film resulting from step (b); (d) coating the dried film resulting from step (c) with a layer of a water-resistant thermoplastic resin to form the degradable mulch film, said layer being sufficiently thick so that the amount of water-resistant thermoplastic resin comprises up to about 15% by weight of the resulting mulch film, said layer of water-resistant resin functioning to retard the rate of release of nitrogen from said mulch film and to retard the rate of degradation thereof.
Claim 30
Independent Claim
145 words
A method of preparing a clear, multi-nutrient-containing degradable agricultural mulch film, which comprises the steps of: (a) forming an aqueous admixture comprising a water-soluble synthetic film-forming resin, at least one nitrogeneous constituent which functions as a releasable source of nitrogen, and at least one plant nutrient in addition to said nitrogeneous constituent; (b) casting a film from the admixture resulting from step (a); (c) drying the film resulting from step (b); (d) coating the dried film resulting from step (c) with a layer of a water-resistant thermoplastic resin to form the degradable mulch film, said layer being sufficiently thick so that the amount of water-resistant thermoplastic resin comprises up to about 15% by weight of the resulting mulch film, said layer of water-resistant resin functioning to retard the rate of release of nitrogen from said mulch film and to retard the rate of degradation thereof.
Claim 31
Dependent Claim
54 words
The method of claim 27, wherein the water-soluble resin used in step (a) comprises polyvinyl alcohol, wherein the nitrogeneous constituent is a member selected from the group consisting of urea, water-soluble urea-formaldehyde condensates, and mixtures thereof, and wherein a nitrification inhibitor is added to said admixture when urea is selected as the nitrogeneous constituent.
Claim 32
Dependent Claim
35 words
The method of claim 28, wherein the water-resistant resin used in step (d) comprises a member selected from the group consisting of polyvinyl acetate, plasticized polyvinyl chloride, ethylene/acrylic acid copolymer, ethylene/ethylacrylate copolymer and mixtures thereof.
Claim 33
Dependent Claim
70 words
The method of claim 29, wherein the polyvinyl alcohol used in step (a) has a molecular weight ranging from about 14,000-100,000 and a degree of hydrolysis ranging from about 86-100%; wherein said polyvinyl alcohol comprises from about 20% to about 85% by weight of the dried film resulting from step (c); and wherein said water-resistant resin comprises from about 2% to about 12% by weight of said coated mulch film.
Claim 34
Dependent Claim
66 words
The method of claim 29, wherein the coating step (d) comprises the sub-steps of: (d 1 ) preparing a solution of said water-resistant resin in a solvent for said resin; (d 2 ) coating the film resulting from step (c) with the solution resulting from step (d 1 ); and (d 3 ) removing the solvent from the coated film resulting from step (d 2 ).
Claim 35
Dependent Claim
82 words
The method of claim 31, wherein the aqueous admixture formed in step (a) comprises urea as said nitrogeneous constituent; wherein the dried film resulting from step (c) comprises up to about 35% by weight of urea, from about 20% to about 85% by weight polyvinyl alcohol and from about 0.005% to about 2% by weight of a nitrification inhibitor; and wherein the coated mulch film resulting from step (d) comprises from about 2% to about 12% by weight of said water-resistant resin.
Claim 36
Dependent Claim
59 words
The method of claim 32, wherein said water-soluble resin used in step (a) comprises polyvinyl alcohol having a molecular weight ranging from about 14,000 to about 100,000 and a degree of hydrolysis ranging from about 86-100%; and wherein said water-resistant resin used in step (d) comprises polyvinyl acetate having a molecular weight in the range of from about 45,000-160,000.
Claim 37
Dependent Claim
75 words
The method of claim 31, wherein the aqueous mixture formed in step (a) comprises a water-soluble urea-formaldehyde condensate as said nitrogeneous constituent; wherein the dried film resulting from step (c) comprises up to about 70% by weight of said urea-formaldehyde condensate and from about 20% to about 85% by weight polyvinyl alcohol; and wherein said coated mulch film resulting from step (d) comprises from about 2% to about 12% by weight of said water-resistant resin.
Claim 38
Dependent Claim
59 words
The method of claim 34, wherein said water-soluble resin used in step (a) comprises polyvinyl alcohol having a molecular weight ranging from about 14,000 to about 100,000 and a degree of hydrolysis ranging from about 86-100%; and wherein said water-resistant resin used in step (d) comprises polyvinyl acetate having a molecular weight in the range of from about 45,000-160,000.
Claim 39
Dependent Claim
66 words
The method of claim 29, wherein the coating step (d) comprises the sub-steps of: (d 1 ) preparing a solution of said water-resistant resin in a solvent for said resin; (d 2 ) coating the film resulting from step (c) with the solution resulting from step (d 1 ); and (d 3 ) removing the solvent from the coated film resulting from step (d 2 ).
Claim 40
Dependent Claim
82 words
The method of claim 29, wherein the aqueous admixture formed in step (a) comprises urea as said nitrogeneous constituent; wherein the dried film resulting from step (c) comprises up to about 35% by weight of urea, from about 20% to about 85% by weight polyvinyl alcohol and from about 0.005% to about 2% by weight of a nitrification inhibitor; and wherein the coated mulch film resulting from step (a) comprises from about 2% to about 12% by weight of said water-resistant resin.
Claim 41
Dependent Claim
75 words
The method of claim 29, wherein the aqueous mixture formed in step (a) comprises a water-soluble urea-formaldehyde condensate as said nitrogeneous constituent; wherein the dried film resulting from step (c) comprises up to about 70% by weight of said urea-formaldehyde condensate and from about 20% to about 85% by weight polyvinyl alcohol; and wherein said coated mulch film resulting from step (d) comprises from about 2% to about 12% by weight of said water-resistant resin.
Claim 42
Independent Claim
164 words
A method of preparing a degradable agricultural mulch film, comprising the steps of: (a) forming an aqueous mixture comprising (i) a water-soluble film-forming resin (ii) a nitrogeneous constituent selected from the group consisting of urea, water-soluble urea-formaldehyde condensates, a mixtures thereof, and (iii) at least one plant nutrient other than said nitrogeneous constituent; said admixture further comprising of (iv) a nitrification inhibitor when urea is selected as the only nitrogeneous constituent; (b) casting a film from the admixture resulting from step (a); (c) drying the film resulting from step (b), the resulting dried film having a water-soluble resin content of from about 20% to about 85% by weight; (d) preparing a solution of a water-resistant resin; (e) coating the film resulting from step (c) with the resin solution prepared in step (d); and (f) removing the solvent from the coated film resulting from step (e) to form a degradable agricultural mulch film having a water-resistant resin content of up to about 15% by weight.
Claim 43
Independent Claim
164 words
A method of preparing a degradable agricultural mulch film, comprising the steps of: (a) forming an aqueous mixture comprising (i) a water-soluble film-forming resin (ii) a nitrogeneous constituent selected from the group consisting of urea, water-soluble urea-formaldehyde condensates, a mixtures thereof, and (iii) at least one plant nutrient other than said nitrogeneous constituent; said admixture further comprising of (iv) a nitrification inhibitor when urea is selected as the only nitrogeneous constituent; (b) casting a film from the admixture resulting from step (a); (c) drying the film resulting from step (b), the resulting dried film having a water-soluble resin content of from about 20% to about 85% by weight; (d) preparing a solution of a water-resistant resin; (e) coating the film resulting from step (c) with the resin solution prepared in step (d); and (f) removing the solvent from the coated film resulting from step (e) to form a degradable agricultural mulch film having a water-resistant resin content of up to about 15% by weight.
Claim 44
Dependent Claim
64 words
The method of claim 39, wherein the water-soluble resin used in step (a) comprises polyvinyl alcohol having a molecular weight ranging from about 14,000-100,000 and a degree of hydrolysis ranging from about 86-100%; and wherein the water-resistant resin used in step (d) comprises a member selected from the group consisting of polyvinyl acetate, plasticized polyvinyl chloride, ethylene/acrylic acid copolymers, ethylene/ethylacrylate copolymers and mixtures thereof.
Claim 45
Dependent Claim
69 words
The method of claim 40, wherein said nitrogeneous constituent used in step (a) comprises urea; wherein the dried film resulting from step (c) comprises up to about 35% by weight of said urea and from about 0.005% to about 2% by weight of said nitrificationn inhibitor; and wherein the coated mulch film resulting from step (f) comprises from about 2% to about 12% by weight of said water-resistant resin.
Claim 46
Dependent Claim
60 words
The method of claim 40, wherein said nitrogeneous constituent used in step (a) comprises a water-soluble condensate of urea-formaldehyde; wherein the dried film resulting from step (c) comprises up to 70% by weight of said urea-formaldehyde condensate; and wherein said coated mulch film resulting from step (f) comprises from about 2% to about 12% by weight of said water-resistant resin.
Claim 47
Dependent Claim
42 words
The method of claim 40, wherein the plant nutrients (iii) used in step (a) comprise at least one member selected from the group consisting of phosphoric acid, potassium salts and complexes, phosphate salts and complexes, nitrate salts and complexes and mixtures thereof.
References Cited (Backward Citations)
SU268074A1
Cited
SU273575A1
Cited
US3274731A
Cited
US3341357A
Cited
US3427194A
Cited
US3384993A
Cited
US3299568A
Cited
US3454510A
Cited
GB1253449A
Cited
US3590528A
Cited
US3828471A
Cited
US3886683A
Cited
US3707056A
Cited
FR2203586A1
Cited
US3812615A
Cited
US3867324A
Cited
US3929937A
Cited
US3931068A
Cited
US3896585A
Cited
US3833401A
Cited
US3810328A
Cited
US3984940A
Cited
US4071975A
Cited
US3949145A
Cited
JPS5272773A
Cited
US4063919A
Cited
JPS54150490A
Cited
US4214034A
Cited
JPS5672035A
Cited
JPS5783583A
Cited
JPS5779822A
Cited
SU1027183A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-17 | 1991-02-16 | 1991-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-17 | 1995-02-16 | 1995-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-17 | 1999-02-16 | 1999-08-18 | $7700.00 | Window Closed / Lapsed |