Starting mixture for an insulating composition comprising a lead glass, silk-screening ink comprising such a mixture, and the use of said ink for the protection of hybrid microcircuits on ceramic substrates
Assignee: US Philips Corp
•
Filing: 1985-06-17
•
Granted: 1987-08-04
•
Expires: 2005-06-17
Abstract
Abstract The invention relates to starting mixtures for an insulating composition comprising (a) a from about 70 to 80% by volume of vitreous phase comprising Al2O3, SiO2, B2O3, PbO, ZnO, CaO, and CuO and (b) from about 30 to 20% by volume of at least one oxide of lead having an oxidation degree of at least two, in powder form. The starting mixtures are useful in silk-screening inks for hybrid microcircuits.
Inventors
- 👤 Hugues Baudry
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 09:25
CPC Classifications
C; C03; C03C; C03C8/00; C03C8/24; H; H01; H01C; H01C17/00; H01C17/02; H10; H10W; H10W74/00; H10W74/40; H10W74/43; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/22; H05K3/28
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
116 words
A starting mixture for an insulating composition comprising on the one hand a vitreous phase formed from alumina (Al 2 O 3 ), silica (SiO 2 ), boric oxide (B 2 O 3 ) and including a lead monoxide (PbO), and comprising on the other hand one or several lead oxides having a degree of oxidation higher than or equal to two in powderform, characterized in that the vitreous phase includes in addition zinc oxide (ZnO), calcium oxide (CaO) and copper oxide (CuO) and in that said vitreous phase represents 70 to 80% of the mixture said mixture containing a second phase consisting of PbO 2 and constituting 30% to 20% by volume of the mixture.
Claim 2
Dependent Claim
116 words
A starting mixture for an insulating composition comprising on the one hand a vitreous phase formed from alumina (Al 2 O 3 ), silica (SiO 2 ), boric oxide (B 2 O 3 ) and including a lead monoxide (PbO), and comprising on the other hand one or several lead oxides having a degree of oxidation higher than or equal to two in powderform, characterized in that the vitreous phase includes in addition zinc oxide (ZnO), calcium oxide (CaO) and copper oxide (CuO) and in that said vitreous phase represents 70 to 80% of the mixture said mixture containing a second phase consisting of PbO 2 and constituting 30% to 20% by volume of the mixture.
Claim 3
Dependent Claim
58 words
A mixture as claimed in claim 1, characterized in that the vitreous phase is formed by molar ratios of the following oxides: alumina (Al 2 O 3 ) 5%, silica (SiO 2 ) 40%, boric oxide (B 2 O 3 ) 20%, lead monoxide (PbO) 22%, calcium anhydride (CaO) 3%, zinc oxide (ZnO) 8%, copper oxide (CuO) 2%.
Claim 4
Dependent Claim
23 words
A mixture as claimed in claim 2, characterized in that the vitreous phase represents 75% by volume and lead dioxide 25% by volume.
Claim 5
Dependent Claim
27 words
A silk-screening ink comprising a mixture as claimed in any one of the claims 1 to 3, is incorporated in an ethyl cellulose solution in terpineol carrier.
Claim 6
Dependent Claim
49 words
An ink as claimed in claim 4, characterized in that it is used as a protection layer for hybrid microcircuits manufactured on a substrate of alumina deposited by silk-screening on the surface of said circuits and fired at a temperature of 550° C. constant for at least 5 minutes.
Claim 7
Dependent Claim
69 words
A starting mixture for an insulating composition comprising (a) from about 70 to 80% by volume, based upon the total volume of the mixture, of a vitreous phase comprising Al 2 O 3 , SiO 2 , B 2 O 3 , PbO, ZnO, CaO, and CuO and (b) from about 30 to 20% by volume, based upon the total volume of the mixture PbO 2 in powder form.
Claim 8
Dependent Claim
69 words
A starting mixture for an insulating composition comprising (a) from about 70 to 80% by volume, based upon the total volume of the mixture, of a vitreous phase comprising Al 2 O 3 , SiO 2 , B 2 O 3 , PbO, ZnO, CaO, and CuO and (b) from about 30 to 20% by volume, based upon the total volume of the mixture PbO 2 in powder form.
Claim 9
Dependent Claim
77 words
A starting mixture for an insulating composition consisting essentially of (a) from 70 to 80% volume, based upon the total volume of the starting mixture, of a mixture, in mol % of: Al 2 O 3 :5, SiO 2 : 40, B 2 O 3 : 20, PbO: 22, CaO: 3, ZnO: 8, CuO: 2, and (b) from about 30 to 20% by volume, based upon the total volume of the starting mixture, of PbO 2 .
Claim 10
Dependent Claim
77 words
A starting mixture for an insulating composition consisting essentially of (a) from 70 to 80% volume, based upon the total volume of the starting mixture, of a mixture, in mol % of: Al 2 O 3 :5, SiO 2 : 40, B 2 O 3 : 20, PbO: 22, CaO: 3, ZnO: 8, CuO: 2, and (b) from about 30 to 20% by volume, based upon the total volume of the starting mixture, of PbO 2 .
Claim 11
Dependent Claim
22 words
A starting mixture of claim 6 or 7, wherein component (a) represents 75% by volume and component (b) represents 25% by volume.
Claim 12
Dependent Claim
20 words
A silk-screening ink for hybrid circuit fabrication comprising a starting mixture of claim 6 or 7 and an organic carrier.
Claim 13
Dependent Claim
17 words
A silk-screening ink of claim 9, wherein the organic carrier is an ethyl cellulose solution in terpineol.
Claim 14
Dependent Claim
16 words
A silk-screening ink of claim 9 which comprises an insulatingly effective amount of the starting mixture.
Claim 15
Dependent Claim
44 words
A method of forming a protective layer on a hybrid microcircuit having an alumina substrate which comprises depositing on the surface of said microcircuit a silk-screening ink of claim 9 and then heating said thus-treated microcircuit at 550° C. for at least five minutes.
References Cited (Backward Citations)
GB1489031A
Cited
US4108786A
Cited
US4152282A
Cited
US4420338A
Cited
US4369220A
Cited
US4388347A
Cited
US4412377A
Cited
US4431451A
Cited
US4415624A
Cited
US4547625A
Cited
US4604298A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-03 | 1991-02-02 | 1991-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-03 | 1995-02-02 | 1995-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-03 | 1999-02-02 | 1999-08-04 | $7700.00 | Window Closed / Lapsed |