US4431451A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Dental material
Assignee: American Dental Association
•
Filing: 1982-01-22
•
Granted: 1984-02-14
•
Expires: 2002-01-22
Abstract
Abstract Dentures, dental glazes or coatings, reconstructive jacket-crowns and inlays and restorative constructions over metal or preformed alumina substrates are fabricated from a dental porcelain frit prepared by a gel route.
Inventors
- 👤 Curtis P. Mabie
- 👤 Daniel L. Menis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 11:26
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/006; C03C1/008; A; A61; A61K; A61K6/00; A61K6/15; A61K6/17; A61K6/80; A61K6/802; A61K6/807; A61K6/813; A61K6/816; A61K6/818; A61K6/822; A61K6/824; A61K6/831; A61K6/833
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
150 words
A method of preparing a dental porcelain article which comprises preparing a dental porcelain frit by the process comprising: (a) preparing a sol comprising in weight percent based on total solids content, 55-80% silica, 5-20% alumina, 12-40% flux constituents, and 0-7% additives, the 12-40% flux constituents comprising the solubilized oxides of boron, sodium, potassium, and lithium, the 0-7% additives comprising the solubilized oxides of calcium, magnesium, barium, strontium, zinc, tin, phosphorus, cesium, rubidium, yttrium, ytterbium, samarium, lanthanum, titanium, zirconium, terbium, thulium, cerium, europium and scandium with no single additive being present in an amount greater than 4%, (b) gelling the sol, and (c) calcining the gelled sol by heating it to calcination temperature to form a calcined frit, the frit being characterized by minimal microporosity and by a fusion temperature of 960° C. or less, and then comminuting the frit, forming it into a dental porcelain article and firing it.
Claim 2
Independent Claim
150 words
A method of preparing a dental porcelain article which comprises preparing a dental porcelain frit by the process comprising: (a) preparing a sol comprising in weight percent based on total solids content, 55-80% silica, 5-20% alumina, 12-40% flux constituents, and 0-7% additives, the 12-40% flux constituents comprising the solubilized oxides of boron, sodium, potassium, and lithium, the 0-7% additives comprising the solubilized oxides of calcium, magnesium, barium, strontium, zinc, tin, phosphorus, cesium, rubidium, yttrium, ytterbium, samarium, lanthanum, titanium, zirconium, terbium, thulium, cerium, europium and scandium with no single additive being present in an amount greater than 4%, (b) gelling the sol, and (c) calcining the gelled sol by heating it to calcination temperature to form a calcined frit, the frit being characterized by minimal microporosity and by a fusion temperature of 960° C. or less, and then comminuting the frit, forming it into a dental porcelain article and firing it.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein the sol is peptized by acid.
Claim 4
Dependent Claim
13 words
The method of claim 1 wherein the sol is peptized by carbonate anions.
Claim 5
Independent Claim
164 words
A method of preparing a dental porcelain article which comprises preparing a dental porcelain frit by the process comprising: (a) preparing a sol comprising in weight percent based on total solids content, 55-80% silica, 5-20% alumina, 12-40% flux constituents and 0-7% additives, the 12-40% flux constituents comprising solubilized oxides of boron, sodium, potassium, and lithium, the 0-7% additives comprising the solubilized oxides of calcium, magnesium, barium, strontium, zinc, tin, phosphorus, cesium, rubidium, yttrium, ytterbium, samarium, lanthanum, titanium, zirconium, terbium, thulium, cerium, europium and scandium with no single additive being present in an amount greater than 4%, (b) gelling the sol, (c) precalcining the gelled sol by heating it at a moderate temperature, (d) comminuting the heated, gelled sol, and (e) calcining the comminute at a higher temperature to form a calcined frit, the frit being characterized by minimal microporosity and by a fusion temperature of 960° C. or less, and then recomminuting the frit, forming it into a dental porcelain article and firing it.
Claim 6
Independent Claim
164 words
A method of preparing a dental porcelain article which comprises preparing a dental porcelain frit by the process comprising: (a) preparing a sol comprising in weight percent based on total solids content, 55-80% silica, 5-20% alumina, 12-40% flux constituents and 0-7% additives, the 12-40% flux constituents comprising solubilized oxides of boron, sodium, potassium, and lithium, the 0-7% additives comprising the solubilized oxides of calcium, magnesium, barium, strontium, zinc, tin, phosphorus, cesium, rubidium, yttrium, ytterbium, samarium, lanthanum, titanium, zirconium, terbium, thulium, cerium, europium and scandium with no single additive being present in an amount greater than 4%, (b) gelling the sol, (c) precalcining the gelled sol by heating it at a moderate temperature, (d) comminuting the heated, gelled sol, and (e) calcining the comminute at a higher temperature to form a calcined frit, the frit being characterized by minimal microporosity and by a fusion temperature of 960° C. or less, and then recomminuting the frit, forming it into a dental porcelain article and firing it.
Claim 7
Dependent Claim
68 words
The method of claim 1 or 4 wherein the sol comprises, in weight percent based on total solids content, 55-70% silicon dioxide, 5-18% aluminum oxide, 0-10% solubilized boric oxide, 2-15% solubilized sodium oxide, 2-18% solubilized potassium oxide, 0-18% solubilized lithium oxide, and 0-5% solubilized oxides of calcium, magnesium, barium, strontium, zinc, tin, phosphorus, cesium, rubidium, yttrium, ytterbium, samarium, lanthanum, titanium, tantanlum, zirconium, terbium, thulium, cerium, europium and scandium.
Claim 8
Dependent Claim
51 words
The method of claim 5 wherein the calcined frit comprises 69.0-72.3 mole % silicon dioxide, 4.9-11.9 mole percent aluminum oxide, 6.0-9.0 mole percent boric oxide, 4.9-5.2 mole percent potassium oxide, 4.4-4.6 mole percent sodium oxide, and less than 1.5 mole percent total of oxides of zirconium, calcium, magnesium, phosphorus and zinc.
Claim 9
Dependent Claim
41 words
The method of claim 5 wherein the calcined frit comprises 69-73 mole % silicon dioxide, 7.5-9.6 mole % aluminum oxide, 5.0-9.6 mole % boric oxide, 3.0-6.3 mole % potassium oxide, 2.8-4.5 mole % sodium oxide and 0.5-5.0 mole % lithium oxide.
Claim 10
Dependent Claim
50 words
The method of claim 5 wherein the sol further comprises fine particles selected from the group consisting of quartz, potash feldspar, nepheline syenite, beta alumina, pyrex fiber, fused quartz fiber, silica fiber, hydrated unfused alumina, glass frit, unfused alumina, fused alumina, mica, high-fusing porcelain frit, titanium, aluminum, silicon, and tantalum.
Claim 11
Dependent Claim
20 words
The method of claim 8 wherein the fine particles are quartz, potash feldspar, pyrex fiber, fused alumina or lepidolite mica.
Claim 12
Dependent Claim
17 words
The method of claim 1 wherein the calcination temperature is between about 700 and about 1,500° C.
Claim 13
Dependent Claim
45 words
The method of claim 4 wherein precalcination comprises: (a) heating the gelled sol at temperatures from about 90 to about 200° C. for up to 40 to 60 hours, and then (b) heating the gelled sol at temperatures from about 400 to about 700° C.
Claim 14
Dependent Claim
52 words
The method of claim 11 wherein precalcination comprises: (a) dessicating the gelled sol at 90° to 100° C. for 20 to 30 hours and then at 190° to 200° C. for 20 to 30 hours, then (b) defuming the gelled sol for one hour at each of 500°, 600° and 700° C.
Claim 15
Dependent Claim
17 words
The method of claim 4 wherein the comminution of the heated, gelled sol is effected by grinding.
Claim 16
Dependent Claim
23 words
The method of claim 4 wherein calcination comprises heating the comminuted, heated, gelled sol at temperatures from about 700° to about 1500° C.
Claim 17
Dependent Claim
45 words
The method of claim 14 wherein the calcination further comprises heating the comminuted, heated, gelled sol from an initial temperature of 725° C. at successive 25° C. intervals for one hour each with retention time at maximum calcination temperature varying from 1 to 61 hours.
Claim 18
Dependent Claim
19 words
The method of claim 1 comprising the additional sub-step of (d) melting the calcined frit, before comminuting the frit.
Claim 19
Dependent Claim
19 words
The method of claim 4 comprising the additional sub-step of (f) melting the calcined frit, before recomminuting the frit.
Claim 20
Dependent Claim
138 words
A dental porcelain frit prepared by the method comprising: (a) preparing a sol comprising in weight percent based on total solids content, 55-80% silica, 5-20% alumina, 12-40% flux constituents, and 0-7% additives, the 12-40% flux constituents comprising solubilized oxides of boron, sodium, potassium, and lithium, the 0-7% additives comprising the solubilized oxides of calcium, magnesium, barium, strontium, zinc, tin, phosphorus, cesium, rubidium, yttrium, ytterbium, samarium, lanthanum, titanium, zirconium, terbium, thulium, cerium, europium and scandium with no single additive being present in an amount greater than 4%, (b) gelling the sol, (c) precalcining the gelled sol by heating it at a moderate temperature, (d) comminuting the heated, gelled sol, and (e) calcining the comminute at a higher temperature to form a calcinate, the calcinate being characterized by minimal microporosity and by a fusion temperature of 960° C. or less.
Claim 21
Dependent Claim
138 words
A dental porcelain frit prepared by the method comprising: (a) preparing a sol comprising in weight percent based on total solids content, 55-80% silica, 5-20% alumina, 12-40% flux constituents, and 0-7% additives, the 12-40% flux constituents comprising solubilized oxides of boron, sodium, potassium, and lithium, the 0-7% additives comprising the solubilized oxides of calcium, magnesium, barium, strontium, zinc, tin, phosphorus, cesium, rubidium, yttrium, ytterbium, samarium, lanthanum, titanium, zirconium, terbium, thulium, cerium, europium and scandium with no single additive being present in an amount greater than 4%, (b) gelling the sol, (c) precalcining the gelled sol by heating it at a moderate temperature, (d) comminuting the heated, gelled sol, and (e) calcining the comminute at a higher temperature to form a calcinate, the calcinate being characterized by minimal microporosity and by a fusion temperature of 960° C. or less.
Claim 22
Dependent Claim
69 words
A dental porcelain frit as in claim 18 wherein the sol comprises, in weight percent based on total solids content, 55-70% silicon dioxide, 5-18% aluminum oxide, 0-10% solubilized boric oxide, 2-15% solubilized sodium oxide, 2-18% solubilized potassium oxide, 0-18% solubilized lithium oxide, and 0-5% solubilized oxides of calcium, magnesium, barium, strontium, zinc, tin, phosphorus, cesium, rubidium, yttrium, ytterbium, samarium, lanthanum, titanium, tantalum, zirconium, terbium, thulium, cerium, europium and scandium.
Claim 23
Dependent Claim
53 words
A dental porcelain frit as in claim 19 wherein the sol further comprises fine particles selected from the group consisting of quartz, potash feldspar, nepheline syenite, beta alumina, pyrex fiber, fused quartz fiber, silica fiber, hydrated unfused alumina, glass frit, unfused alumina, fused alumina, mica, high-fusing porcelain frit, titanium, aluminum, silicon, and tantalum.
Claim 24
Dependent Claim
48 words
A dental porcelain frit as in claim 18 wherein precalcination comprises: (a) heating the gelled sol at temperatures from about 90° to about 200° C. for up to 40 to 60 hours, and then (b) heating the gelled sol at temperatures from about 400° to about 700° C.
Claim 25
Dependent Claim
26 words
A dental porcelain frit as in claim 18 wherein calcination comprises heating the comminuted, heated, gelled sol at temperatures from about 700° to about 1500° C.
Claim 26
Dependent Claim
22 words
A dental porcelain frit as in claim 18 prepared by a method further comprising the additional step of (f) melting the calcinate.
Claim 27
Dependent Claim
28 words
In a porcelain denture tooth prepared from porcelain frit, the improvement which comprises employing the dental porcelain frit of claims 18, 19, 20, 21, 22, or 23, therein.
Claim 28
Dependent Claim
27 words
In a jacket-crown reconstruction prepared from porcelain frit, the improvement which comprises employing the dental porcelain frit of claims 18, 19, 20, 21, 22, or 23, therein.
Claim 29
Dependent Claim
31 words
In a method for preparing an inlay reconstruction prepared from porcelain frit, the improvement which comprises employing the dental porcelain frit of claims 18, 19, 20, 21, 22, or 23, therein.
Claim 30
Dependent Claim
39 words
In a method for preparing a restorative construction prepared from porcelain frit coated over a metal or preformed alumina substrate, the improvement which comprises employing the dental porcelain frit of claims 18, 19, 20, 21, 22, or 23, therein.
Claim 31
Dependent Claim
18 words
A dental glaze prepared from the dental porcelain frit of claims 18, 19, 20, 21, 22, or 23.
References Cited (Backward Citations)
US3759683A
Cited
US3782982A
Cited
US3929439A
Cited
US3973970A
Cited
US4217264A
Cited
US4361654A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-13 | 1987-08-15 | 1988-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-13 | 1991-08-15 | 1992-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-13 | 1995-08-15 | 1996-02-14 | $7700.00 | Window Closed / Lapsed |