Method for the manufacture of glass bodies
Assignee: US Philips Corp
•
Filing: 1986-03-03
•
Granted: 1987-08-04
•
Expires: 2006-03-03
Abstract
Abstract Method and equipment for the manufacture of glass bodies in which a porous green body is formed from the starting material for the glass body in the form of a thixotropic suspension, is dried, purified and then sintered, during which process the starting material is transformed into a state with minimum viscosity and homogenized by the introduction of mechanical forces, is poured in the low-viscosity state into a mould of hydrophobic material corresponding to the shape of the glass body to be manufactured and is dried in the mould until a shrinkage of approximately 10% is achieved and then, after removal from the mould, is subjected to further processing steps to produce the glass body.
Inventors
- 👤 Rolf Clasen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:38
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03B19/00; C03B19/12; Y; Y10; Y10S; Y10S65/00; Y10S65/90; Y10S65/901
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
137 words
A method for the manufacture of a glass body, said method comprising: (a) forming a starting thixotropic suspension of silicon dioxide in a dispersing liquid; (b) applying a mechanical force in sufficient degree to said suspension to homogenize said suspension and reduce its viscosity to the minimum; (c) pouring the resultant low-viscosity suspension into a mold made of a hydrophobic material and having a shape corresponding to the shape of the glass body to be produced and allowing said suspension to thixotropically solidify in said mold to form a green body; (d) drying the green body while in said mold until a shrinkage of about 10% of the green body is achieved; (e) then removing the green body from said mold and subjecting the green body to additional manufacturing steps for the production of the glass body.
Claim 2
Independent Claim
137 words
A method for the manufacture of a glass body, said method comprising: (a) forming a starting thixotropic suspension of silicon dioxide in a dispersing liquid; (b) applying a mechanical force in sufficient degree to said suspension to homogenize said suspension and reduce its viscosity to the minimum; (c) pouring the resultant low-viscosity suspension into a mold made of a hydrophobic material and having a shape corresponding to the shape of the glass body to be produced and allowing said suspension to thixotropically solidify in said mold to form a green body; (d) drying the green body while in said mold until a shrinkage of about 10% of the green body is achieved; (e) then removing the green body from said mold and subjecting the green body to additional manufacturing steps for the production of the glass body.
Claim 3
Dependent Claim
45 words
The method as claimed in claim 1, wherein starting suspension for the glass body is a suspension which contains SiO 2 particles having diameters in the range from 10 to 500 nm, preferably 15 to 100 nm, with a mean particle diameter of 40 nm.
Claim 4
Dependent Claim
21 words
The method as claimed in claim 2, wherein a suspension with a solid-dispersing liquid ratio of 0.5:1 to 1.2:1 is used.
Claim 5
Dependent Claim
13 words
The method as claimed in claim 1, wherein the dispersing liquid is water.
Claim 6
Dependent Claim
28 words
The method as claimed in claim 1, wherein an ionogenic additive which shifts the pH-value of the suspension towards the basic region (pH=5.5-8) is added to the suspension.
Claim 7
Dependent Claim
25 words
The method as claimed in claim 5, wherein the ionogenic additive is added in a quantity of ≦5 wt.% per solids content in the suspension.
Claim 8
Dependent Claim
16 words
The method as claimed in claim 5, wherein an ammonium compound is used as the additive.
Claim 9
Dependent Claim
20 words
The method as claimed in claim 7, wherein an aqueous 5% NH 4 F solution is used as the additive.
Claim 10
Dependent Claim
75 words
The method as claimed in claim 8, wherein the starting suspension used is an aqueous suspension which contains SiO 2 particles having diameters in the range from 10 to 100 nm with a mean particle diameter of 40 nm and a SiO 2 :water weight ratio of 1:1, to which a 5% NH 4 F aqueous solution is added as the ionogenic additive in a quantity of 0.8 wt.% per solids content in the suspension.
Claim 11
Dependent Claim
40 words
A method as claimed in claim 1, wherein the viscosity of the starting suspension is reduced to the minimum by the action of sound at a frequency f=20 to 200 Hz or ultrasound at a frequency f=20 to 50 kHz.
Claim 12
Dependent Claim
41 words
A method as claimed in claim 1, wherein the starting suspension is poured into a mold of synthetic material and is dried by means of diffusion of the dispersing agent through at least one aperture at the top of the mold.
Claim 13
Dependent Claim
26 words
The method as claimed in claim 11, wherein the material used for the mould is polytetrafluoroethylene, polyethylene, polycarbonate, polymethylmethacrylate or polyvinylchloride, preferably with a polished surface.
Claim 14
Dependent Claim
46 words
A method as claimed in claim 1, wherein the starting suspension is poured into a mold made of a porous elastic synthetic material with pores the size of the molecules of the dispersing liquid and is dried by diffusion of the dispersing agent through the pores.
Claim 15
Dependent Claim
36 words
The method as claimed in claim 13, wherein the mold is a thin-walled hose of silicone rubber which is arranged in a porous support mould corresponding to the shape of the glass body to be produced.
Claim 16
Dependent Claim
42 words
The method as claimed in claim 11, wherein the mold is made of a plastic foil which is soluble in a solvent which has a lower surface tension than the dispersing liquid and is immiscible or largely immiscible with the dispersing liquid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-08-03 | 1991-02-02 | 1991-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-08-03 | 1995-02-02 | 1995-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-08-03 | 1999-02-02 | 1999-08-04 | $7700.00 | Window Closed / Lapsed |