Enhancement of shape selectivity of zeolites
Assignee: Mobil Oil AS
•
Filing: 1985-02-22
•
Granted: 1987-07-07
•
Expires: 2005-02-22
Abstract
Abstract A method is provided for enhancing the shape selectivity of a crystalline zeolite having a silica-to-alumina mol ratio greater than 10. The method consists of treating the zeolite with an ammonium fluoride solution at moderately elevated temperature, in the absence or in the presence of a matrix. The products are useful as shape-selective sorbents, and also as shape-selective catalysts for organic reactions including catalytic dewaxing.
Inventors
- 👤 Edward J. Rosinski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:48
CPC Classifications
C; C10; C10G; C10G45/00; C10G45/58; C10G45/60; C10G45/64; B; B01; B01J; B01J29/00; B01J29/90; Y; Y10; Y10S; Y10S423/00; Y10S423/22; Y10S423/23; Y10S423/25; Y10S423/27; Y10S423/33
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
143 words
A method for enhancing the selectivity for dewaxing of a porous crystalline zeolite selected from the group consisting of ZSM- 5, ZSM-35, and ZSM-38 having a silica to alumina mol ratio greater than about 10 and a crystal size ranging from about 2 to 5 microns which comprises: (a) calcining said zeolite between the temperature of about 300° C. and about 900° C.; (b)impregnating said calcined zeolite at 80° to 150° C. with an aqueous solution of ammonium fluoride which yields available fluoride ions to provide between about 2.0 to about 30% by weight of elemental fluorine in the final treated product of (e); (c) calcining said fluoride treated zeolite at a temperature between about 300° C. and about 900° C.; (d) contacting said calcined, fluoride treated zeolite with an aqueous solution of an ammoniun salt; and (e) calcining said ammonium treated zeolite.
Claim 2
Independent Claim
143 words
A method for enhancing the selectivity for dewaxing of a porous crystalline zeolite selected from the group consisting of ZSM- 5, ZSM-35, and ZSM-38 having a silica to alumina mol ratio greater than about 10 and a crystal size ranging from about 2 to 5 microns which comprises: (a) calcining said zeolite between the temperature of about 300° C. and about 900° C.; (b)impregnating said calcined zeolite at 80° to 150° C. with an aqueous solution of ammonium fluoride which yields available fluoride ions to provide between about 2.0 to about 30% by weight of elemental fluorine in the final treated product of (e); (c) calcining said fluoride treated zeolite at a temperature between about 300° C. and about 900° C.; (d) contacting said calcined, fluoride treated zeolite with an aqueous solution of an ammoniun salt; and (e) calcining said ammonium treated zeolite.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein said zeolite has a silica-to-alumina ratio greater than about 100.
Claim 4
Dependent Claim
15 words
The method of claim 1 wherein zeolite has a silica-to-alumina ratio greater than about 500.
Claim 5
Dependent Claim
27 words
The method of claim 1 wherein the ammonium salt of (d) is selected from the group consisting of ammonium chloride, ammonium sulfate, ammonium chloride and mixtures thereof.
Claim 6
Dependent Claim
32 words
The method of claim 4 wherein the concentration of ammonium salt in the resultant treated zeolite composition is the equivalent of between about 0.1 and about 30% by weight of elemental fluorine.
Claim 7
Dependent Claim
20 words
The method of claim 1 wherein subsequent to step (b) and prior to step (c) said zeolite is water washed.
Claim 8
Dependent Claim
10 words
The method of claim 1 wherein said zeolite is ZSM-5.
Claim 9
Dependent Claim
25 words
The method of claim 1 wherein said impregnating said calcined zeolite of (b) is effected at a temperature between about 82° and about 150° C.
Claim 10
Independent Claim
107 words
A method for enhancing the selectivity for dewaxing of a crystalline zeolite having a silica-to-alumina mol ratio greater than 10, a crystal size ranging from about 2 to 5 microns and selected from the group consisting of ZSM-5, ZSM-35, and ZSM-38, which method comprises: contacting said zeolite with an amount of aqueous solution of ammonium fluoride, said amount containing sufficient salt to provide between about 2.0 to about 30 percent by weight of said zeolite of fluorine, said contacting being for a time and at a temperature effective to enhance said selectivity; and; calcining said contacted zeolite at a temperature of about 300° C. to 900° C.
Claim 11
Independent Claim
107 words
A method for enhancing the selectivity for dewaxing of a crystalline zeolite having a silica-to-alumina mol ratio greater than 10, a crystal size ranging from about 2 to 5 microns and selected from the group consisting of ZSM-5, ZSM-35, and ZSM-38, which method comprises: contacting said zeolite with an amount of aqueous solution of ammonium fluoride, said amount containing sufficient salt to provide between about 2.0 to about 30 percent by weight of said zeolite of fluorine, said contacting being for a time and at a temperature effective to enhance said selectivity; and; calcining said contacted zeolite at a temperature of about 300° C. to 900° C.
Claim 12
Dependent Claim
13 words
The method of claim 9 wherein said zeolite is free of alumina binder.
Claim 13
Dependent Claim
27 words
The method of claim 9 including the step of calcining said zeolite at about 540° C. in a gs containing elemental oxygen prior to said contacting step.
Claim 14
Dependent Claim
12 words
The method of claim 9 wherein said contacting is effected by impregnation.
Claim 15
Dependent Claim
12 words
The method of claim 11 wherein said contacting is effected by impregnation.
Claim 16
Dependent Claim
19 words
The method of claim 9 including the step of water washing said contacted zeolite prior to said calcining step.
Claim 17
Dependent Claim
29 words
The method of claim 11 including the step of water washing said contacted zeolite prior to the step of calcining at 300° C. to 900° C. said contacted zeolite.
Claim 18
Dependent Claim
17 words
The method of claim 9 including the step of converting said calcined zeolite to the hydrogen form.
Claim 19
Dependent Claim
17 words
The method of claim 11 including the step of converting said twice-calcined zeolite to the hydrogen form.
Claim 20
Dependent Claim
19 words
The product formed by the method of claim 10 and having an alpha value of at least about 100.
Claim 21
Dependent Claim
19 words
The product formed by the method of claim 11 and having an alpha value of at least about 100.
Claim 22
Dependent Claim
19 words
The product formed by the method of claim 12 and having an alpha value of at least about 100.
Claim 23
Dependent Claim
19 words
The product formed by the method of claim 13 and having an alpha value of at least about 100.
Claim 24
Dependent Claim
19 words
The product formed by the method of claim 14 and having an alpha value of at least about 100.
Claim 25
Dependent Claim
19 words
The product formed by the method of claim 15 and having an alpha value of at least about 100.
Claim 26
Dependent Claim
19 words
The product formed by the method of claim 16 and having an alpha value of at least about 100.
Claim 27
Dependent Claim
19 words
The product formed by the method of claim 17 and having an alpha value of at least about 100.
References Cited (Backward Citations)
US3594331A
Cited
US3700585A
Cited
US3702886A
Cited
US3933983A
Cited
US4073865A
Cited
US4297335A
Cited
US4324698A
Cited
US4444738A
Cited
US4361713A
Cited
US4444902A
Cited
US4427787A
Cited
US4427788A
Cited
US4427786A
Cited
US4414189A
Cited
US4520219A
Cited
US4548913A
Cited
US4427791A
Cited
US4567310A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-06 | 1991-01-05 | 1991-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-06 | 1995-01-05 | 1995-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-06 | 1999-01-05 | 1999-07-07 | $7700.00 | Window Closed / Lapsed |