Method of forming a substantially interwoven matrix containing a refractory hard metal and a metal compound

Claim 2

In a process wherein a first reactant comprising one or more metals or metal compounds exothermically reacts with at least one or more metals or metal compounds in the presence of a third reactant to form a substantially interwoven matrix of a conductive material and an insulating material; the improvement which comprises locally applying, to a selected region of a shaped body formed from a mixture of said reactants, sufficient energy to initiate said exothermic reaction which propagates throughout the remainder of said body to form said interwoven matrix.

Claim 3

The process of claim 1 including the additional step of adding to said mixture of reactants a previously reacted conductive material in an amount, not less than 3 wt. % nor exceeding 20 wt. %, which will be sufficient to inhibit the generation of excessive exothermic heat without inhibiting propagation of the exothermic reaction throughout the mixture.

Claim 4

The process of claim 2 wherein said previously reacted material is selected from the class consisting of TiB 2 and ZrB 2 .

Claim 5

The process of claim 2 wherein said step of locally applying energy comprises locally applying heat energy to initiate said reaction.

Claim 6

The process of claim 4 wherein said step of locally applying heat energy comprises energizing a resistance heater in thermal proximity to said selected region in said body.

Claim 7

The process of claim 4 wherein said step of locally applying energy comprises directing a stream of a gas at an elevated temperature toward said selected region in said body.

Claim 8

The process of claim 4 wherein said step of locally applying energy comprises providing an ignition spark adjacent said selected region in said body.

Claim 9

The process of claim 7 wherein said step of providing an ignition spark further comprises placing two spaced apart electrodes adjacent said selected region and providing a sufficient electrical potential between said electrodes to cause an ignition spark to occur to initiate said invention.

Claim 10

The process of claim 4 wherein said step of locally applying heat energy comprises supplying heat energy from an induction heater adjacent said selected region of said body.

Claim 11

The process of claim 2 which further comprises the step of directing a sufficient amount of ultraviolet light energy at said selected region to initiate said reaction.

Claim 12

The process of claim 2 including the further steps of forming a body from said reactants having a conductive electrode therein; contacting said body with a second electrode in said selected region; and providing a sufficient energy potential between said electrodes to initiate said reaction in said preselected region.

Claim 13

The process of claim 11 including the further step of passing said second electrode into said body a sufficient distance with respect to said conductive electrode therein to permit initiation of said reaction by placing a sufficient potential between said electrodes.

Claim 14

An improved process for producing a ceramic composite comprising a substantially interwoven matrix of a first material and a second material, the process comprising the steps of: (a) forming a body containing first and second reactants capable of exothermically reacting to form said first material and a third reactant capable of oxidizing to form said second material; and (b) locally applying sufficient energy to a first region of said body to initiate a self propagating exothermic reaction which propagates throughout the remainder of said body in order to reduce said first and second reactants and oxidize said third reactant to form said composite of said first material and said second material.

Claim 15

An improved process for producing a ceramic composite comprising a substantially interwoven matrix of a first material and a second material, the process comprising the steps of: (a) forming a body containing first and second reactants capable of exothermically reacting to form said first material and a third reactant capable of oxidizing to form said second material; and (b) locally applying sufficient energy to a first region of said body to initiate a self propagating exothermic reaction which propagates throughout the remainder of said body in order to reduce said first and second reactants and oxidize said third reactant to form said composite of said first material and said second material.

Claim 16

The process of claim 13 which includes the further step of adding previously reacted amounts of said first material to the reactant mixture in an amount insufficient to lower the amount of exothermic heat generated sufficiently to interfere with the propagation of the reaction but sufficient to prevent distortion of said composite by the generation of excessive exothermic heat.

Claim 17

The process of claim 14 wherein said first material comprises a conductive material which forms an interwoven matrix with said second material which comprises an insulating material.

Claim 18

The process of claim 14 wherein said step of locally applying sufficient energy to a first region comprises locally applying heat energy to said first region.

Claim 19

The process of claim 14 wherein said first reactant is selected from the class consisting of a titanium compound, a zirconium compound, or mixtures thereof.

Claim 20

The process of claim 14 wherein said second reactant is a boron compound.

Claim 21

The process of claim 14 wherein said third reactant is a metal capable of reacting with said first and second reactants to form an insulating compound which forms a substantially interwoven matrix with a conductive material formed from said first and second reactants.

Claim 22

The process of claim 19 wherein said first reactant is selected from the class consisting of a titanium compound, a zirconium compound, or mixtures thereof; said second compound comprises a boron compound; and said first and second reactants react with said third reactant to form a substantially interwoven matrix of a refractory hard metal and an insulating material.

Claim 23

The process of claim 20 wherein said third reactant is aluminum and said reactants react by a displacement reaction to form a substantially interwoven matrix of a refractory hard metal and aluminum oxide.

Claim 24

An improved process for producing a ceramic composite comprising a substantially interwoven matrix of a first material selected from the class consisting of TiB 2 and ZrB 2 and a second material consisting essentially of Al 2 O 3 , the process comprising the steps of: (a) forming a body from a mixture containing: (1) 15 to 25 mol. % of a first reactant selected from the class consisting of titanium, an oxide of titanium, zirconium, and an oxide of zirconium; (2) 18 to 25 mol. % B 2 O 3 ; and (3) 50 to 70 mol. % aluminum; and (b) locally applying sufficient energy to a first region of said body to initiate a self propagating exothermic reaction which propagates throughout the remainder of said body in order to form said first material by the reduction of said first reactant and said B 2 O 3 and to form said second material by the oxidation of said aluminum to form said composite of said first material and said second material.

Claim 25

An improved process for producing a ceramic composite comprising a substantially interwoven matrix of a first material selected from the class consisting of TiB 2 and ZrB 2 and a second material consisting essentially of Al 2 O 3 , the process comprising the steps of: (a) forming a body from a mixture containing: (1) 15 to 25 mol. % of a first reactant selected from the class consisting of titanium, an oxide of titanium, zirconium, and an oxide of zirconium; (2) 18 to 25 mol. % B 2 O 3 ; and (3) 50 to 70 mol. % aluminum; and (b) locally applying sufficient energy to a first region of said body to initiate a self propagating exothermic reaction which propagates throughout the remainder of said body in order to form said first material by the reduction of said first reactant and said B 2 O 3 and to form said second material by the oxidation of said aluminum to form said composite of said first material and said second material.

Claim 26

The process of claim 22 including the further step of adding to said mixture a sufficient amount of previously formed TiB 2 or ZrO 2 to control the exothermic heat generated by formation of said interwoven matrix of said first and second materials to prevent generation of excessive heat without interfering with the self propagation of said exothermic reaction.