Trench filling and planarization process
Assignee: MagnaChip Semiconductor Ltd
•
Filing: 1986-02-05
•
Granted: 1987-06-09
•
Expires: 2006-02-05
Abstract
Abstract A process for forming planar trench oxide isolated integrated circuit devices. In particular, the process fills trenches of diverse widths, yet provides a final structure in which the narrow trench dielectrics, the wide trench dielectrics, and the active region surfaces are substantially coplanar. Furthermore, the process reduces the likelihood of creating voids in the narrow trenches. According to one practice, following the formation of the trenches in the substrate, successive layers of conformal silicon nitride, conformal polysilicon, and relatively conformal CVD oxide are formed to the relative depth of the trenches. A photoresist mask is then first selectively formed over the central regions of the wide trenches and then used as a mask during the anisotropic etch of exposed oxide. The underlying polysilicon layer serves as an oxide etchant stop, and also provides the material from which the next successive oxidation partially fills the previously etched regions with thermal silicon dioxide. A further planarizing layer of oxide is then formed by poly deposition and oxidation. The nitride layer underlying the polysilicon layer prevents oxidation of the substrate. Fabrication is concluded with a planarization to the level of the active regions, including an etch of the nitride layer over such active regions.
Inventors
- 👤 Alan E. Keiser
- 👤 Randall S. Mundt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:32
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0143; H10W10/10; H10W10/17
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
164 words
A process for creating dielectric material filled trenches of diverse widths between active regions of a semiconductor substrate, comprising the steps of: forming trenches in the substrate; forming a first conformal layer comprised of an oxidation barrier material over the trenches and active regions; forming a second conformal layer over the oxidation barrier material, the second conformal layer being comprised of a material which is characterized first by its ability to withstand etchants of a dielectric material and secondly by its convertability to a dielectric upon conditioning; depositing a third, substantially conformal, layer comprising of a dielectric material; selectively removing dielectric material from the active regions, the narrow width trenches, and the perimeter regions of the wide width trenches; converting the material of the second conformal layer to a dielectric; filling the regions of selectively removed dielectric material with a further dielectric material to a level above the planar of the active regions; and planarizing the substrate to the level of the active regions.
Claim 2
Dependent Claim
164 words
A process for creating dielectric material filled trenches of diverse widths between active regions of a semiconductor substrate, comprising the steps of: forming trenches in the substrate; forming a first conformal layer comprised of an oxidation barrier material over the trenches and active regions; forming a second conformal layer over the oxidation barrier material, the second conformal layer being comprised of a material which is characterized first by its ability to withstand etchants of a dielectric material and secondly by its convertability to a dielectric upon conditioning; depositing a third, substantially conformal, layer comprising of a dielectric material; selectively removing dielectric material from the active regions, the narrow width trenches, and the perimeter regions of the wide width trenches; converting the material of the second conformal layer to a dielectric; filling the regions of selectively removed dielectric material with a further dielectric material to a level above the planar of the active regions; and planarizing the substrate to the level of the active regions.
Claim 3
Dependent Claim
42 words
The process recited in claim 1, wherein the step of selectively removing dielectric material is comprised of: the forming of mask over the central regions of the wide width trenches; and anisotropically etching the dielectric material in the presence of the mask.
Claim 4
Dependent Claim
42 words
The process recited in claim 2, wherein the material of the second conformal layer volumetrically expands upon conversion to a dielectric material and in so doing partially fills the narrow width trenches and perimeter regions of the wide width trenches with dielectric.
Claim 5
Dependent Claim
26 words
The process recited in claim 3, wherein the step of converting the material of the second conformal layer to a dielectric is comprised of thermal oxidation.
Claim 6
Dependent Claim
35 words
The process recited in claim 4, wherein the step of filling the regions of selectively removed dielectric material with further dielectric material is comprised of: forming a silicon layer; and thermally oxidizing the silicon layer.
Claim 7
Dependent Claim
32 words
The process recited in claim 4, wherein the step of filling the regions of selectively removed dielectric material with further dielectric material is comprised of depositing a layer of CVD silicon dioxide.
Claim 8
Dependent Claim
39 words
The process recited in claim 5, wherein the oxidation barrier material is comprised of silicon nitride, the second conformal layer is comprised of polycrystalline or amorphous silicon, and the third, substantially conformal, layer is comprised of CVD silicon dioxide.
Claim 9
Dependent Claim
62 words
The process recited in claim 7, wherein the step of planarizing the substrate to a level of the active regions is comprised of: forming a planarizing polymer layer over the thermally oxidized silicon layer; etching the polymer and thermally oxidized silicon at corresponding rates to the plane of the active regions; and removing the silicon nitride layer from over the active regions.
Claim 10
Dependent Claim
130 words
A process for creating oxide filled trenches of diverse widths between active regions of a silicon substrate, comprising the steps of: etching vertically oriented trenches in the substrate; thermally oxidizing the substrate to form a PAD silicon dioxide layer; depositing a relatively thin conformal silicon nitride layer; depositing a conformal silicon layer; depositing a relatively thick, substantially conformal, silicon dioxide layer; etching the deposited silicon dioxide layer from over the active regions, the narrow width trenches, and the perimeter regions of the wide width trenches; thermally oxidizing the conformal silicon layer to partially fill the narrow width trenches and the perimeter regions of the wide width trenches with silicon dioxide; forming a layer of silicon dioxide over the substrate; and planarizing the substrate to the level of the active regions.
Claim 11
Dependent Claim
130 words
A process for creating oxide filled trenches of diverse widths between active regions of a silicon substrate, comprising the steps of: etching vertically oriented trenches in the substrate; thermally oxidizing the substrate to form a PAD silicon dioxide layer; depositing a relatively thin conformal silicon nitride layer; depositing a conformal silicon layer; depositing a relatively thick, substantially conformal, silicon dioxide layer; etching the deposited silicon dioxide layer from over the active regions, the narrow width trenches, and the perimeter regions of the wide width trenches; thermally oxidizing the conformal silicon layer to partially fill the narrow width trenches and the perimeter regions of the wide width trenches with silicon dioxide; forming a layer of silicon dioxide over the substrate; and planarizing the substrate to the level of the active regions.
Claim 12
Dependent Claim
54 words
The process recited in claim 9, wherein the step of etching the deposited silicon dioxide is comprised of: photolithographically forming a masking layer of photoresist over the central regions of the wide width trenches; and anisotropically etching the silicon dioxide in the presence of the mask with a silicon dioxide etchant ineffective against silicon.
Claim 13
Dependent Claim
47 words
The process recited in claim 10, wherein the anisotropic etch of the silicon dioxide is terminated following the removal of all vertically exposed silicon dioxide except nominal residuals situated within the inside corners of the narrow width trenches and the perimeter regions of the wide width trenches.
References Cited (Backward Citations)
US4493740A
Cited
US4506434A
Cited
US4445967A
Cited
US4473598A
Cited
US4509249A
Cited
US4551911A
Cited
US4571819A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-08 | 1990-12-08 | 1991-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-08 | 1994-12-08 | 1995-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-08 | 1998-12-08 | 1999-06-09 | $7700.00 | Window Closed / Lapsed |