Method of controlling the sintering of metal particles
Assignee: International Business Machines Corp
•
Filing: 1984-04-26
•
Granted: 1987-06-09
•
Expires: 2004-04-26
Abstract
Abstract Sintering of metal particles at their normal sintering temperature is inhibited by coating the metal particles with an organic material such as polyvinyl butyral, polyvinyl formvar, polyvinyl alcohol, polyacrylonitrile epoxies, urethanes and cross-linked polyvinyl butyral. The organic coating serves as a barrier preventing physical contact between metal particles during the initial phase of the sintering cycle and degrades into a carbonaceous coating followed by volatilization during the intermediate phase of the cycle permitting coalescence of the metal particles into a dense mass along with the coalescence of the glass-ceramic particles. Co-sintering of the metal particles and the glass-ceramic particles with the aid of the organic coating results in a hermetic multi-layer glass ceramic substrate free of dimensional stability problems without deleteriously affecting the electrical conductivity of the metal conductor pattern.
Inventors
- 👤 Lester W. Herron
- 👤 Raj N. Master
- 👤 Robert W. Nufer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:03
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; B; B22; B22F; B22F1/00; B22F1/10; B22F3/00; B22F3/10; B22F3/1017; B22F3/1021; C04B41/45; C04B41/50; C04B41/51; C04B41/80; C04B41/81; C04B41/85; C04B41/88; H; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H10W70/098; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
109 words
In the fabrication of a glass-ceramic substrate containing a metal-based conductor a method of controlling the sintering onset temperature of metal particles comprising: forming an oxidizable barrier selected from a group consisting of polyvinyl butyral, polyvinyl formvar, polyvinylalcohol, polyacrylonitrile, epoxies, urethanes and cross-linked polyvinyl butyral between said metal particles to prevent mutual physical contact of the particles and, thereby prevent coalescence of said particles when heated to the normal sintering onset temperature of the metal; and heating the barrier-separated particles to a high temperature exceeding the normal sintering onset temperature of the metal to oxidize said barrier and initiate co-sintering of said metal particles and particles of said glass-ceramic.
Claim 2
Dependent Claim
109 words
In the fabrication of a glass-ceramic substrate containing a metal-based conductor a method of controlling the sintering onset temperature of metal particles comprising: forming an oxidizable barrier selected from a group consisting of polyvinyl butyral, polyvinyl formvar, polyvinylalcohol, polyacrylonitrile, epoxies, urethanes and cross-linked polyvinyl butyral between said metal particles to prevent mutual physical contact of the particles and, thereby prevent coalescence of said particles when heated to the normal sintering onset temperature of the metal; and heating the barrier-separated particles to a high temperature exceeding the normal sintering onset temperature of the metal to oxidize said barrier and initiate co-sintering of said metal particles and particles of said glass-ceramic.
Claim 3
Dependent Claim
53 words
The method as in claim 1 wherein said heating step comprises: heating to a first temperature exceeding said normal temperature in a non-oxidizing ambient to transform said barrier into a carbonaceous residue; and heating to a second temperature exceeding said first temperature in an oxidizing ambient to oxidize and volatilize said carbonaceous residue.
Claim 4
Dependent Claim
26 words
The method as in claim 2 wherein said metal is selected from a group consisting of copper, nickel, palladium, platinum, silver and gold and alloys thereof.
Claim 5
Independent Claim
212 words
A method of forming a multilayer glass-ceramic for carrying semiconductor chips comprising: forming a pattern of metal based conductor forming composition on at least a portion of unfired ceramic layers, said composition predominately including metal particles coated with an organic coating selected from a group consisting of polyvinyl butyral, polyvinyl formvar, polyvinylalcohol, plyacrylonitrile, epoxies, urethanes and cross-linked polyvinyl butyral to prevent coalescence of the metal particles when heated to the sintering temperature of the metal; laminating said layers together; heating said laminate in a non-oxidizing ambient to a temperature above the sintering temperature of said metal to transform said organic coating into a carbonaceous residue and prevent sintering of said metal particles despite said temperature; substituting an oxidizing ambient of H 2 and H 2 O in the ratio of H 2 /H 2 O of about 10 -2 to 10 -6 .5 ; heating said laminate to a temperature in the range of 720°-800° C. to oxidize and volatilize said carbonaceous residue and permit sintering of said metal particles simultaneously with the sintering of said ceramic layers; substituting an inert atmosphere for said oxidizing ambient; heating said laminate to the crystallization temperature of said ceramic, whereby is formed a hermetically sealed multilayer glass-ceramic having a high electrical conductivity metal conductor pattern.
Claim 6
Independent Claim
212 words
A method of forming a multilayer glass-ceramic for carrying semiconductor chips comprising: forming a pattern of metal based conductor forming composition on at least a portion of unfired ceramic layers, said composition predominately including metal particles coated with an organic coating selected from a group consisting of polyvinyl butyral, polyvinyl formvar, polyvinylalcohol, plyacrylonitrile, epoxies, urethanes and cross-linked polyvinyl butyral to prevent coalescence of the metal particles when heated to the sintering temperature of the metal; laminating said layers together; heating said laminate in a non-oxidizing ambient to a temperature above the sintering temperature of said metal to transform said organic coating into a carbonaceous residue and prevent sintering of said metal particles despite said temperature; substituting an oxidizing ambient of H 2 and H 2 O in the ratio of H 2 /H 2 O of about 10 -2 to 10 -6 .5 ; heating said laminate to a temperature in the range of 720°-800° C. to oxidize and volatilize said carbonaceous residue and permit sintering of said metal particles simultaneously with the sintering of said ceramic layers; substituting an inert atmosphere for said oxidizing ambient; heating said laminate to the crystallization temperature of said ceramic, whereby is formed a hermetically sealed multilayer glass-ceramic having a high electrical conductivity metal conductor pattern.
Claim 7
Dependent Claim
27 words
The method as recited in claim 4 wherein said metal is selected from a group consisting of copper, nickel, platinum, palladium, silver and gold and alloys thereof.
Claim 8
Dependent Claim
120 words
In the fabrication a glass-ceramic substrate with copper based metallurgy a method of reducing the difference in sintering onset temperatures of copper particles constituting said metallurgy and glass-ceramic particles constituting said substrate, said method comprising: forming a polymeric coating on said copper particles to prevent mutual physical contact of the copper particles and thereby prevent coalescence of said copper particles when heated to the normal sintering temperature of copper particles; and heating to a high temperature corresponding to the sintering temperature of the glass-ceramic particles to initially transform said polymeric coating into a carbonaceous residue followed by volatilizing said residue, thereby permitting the coalescence of said copper particles only simultaneously with the coalescence of said glass-ceramic particles at said temperature.
Claim 9
Dependent Claim
120 words
In the fabrication a glass-ceramic substrate with copper based metallurgy a method of reducing the difference in sintering onset temperatures of copper particles constituting said metallurgy and glass-ceramic particles constituting said substrate, said method comprising: forming a polymeric coating on said copper particles to prevent mutual physical contact of the copper particles and thereby prevent coalescence of said copper particles when heated to the normal sintering temperature of copper particles; and heating to a high temperature corresponding to the sintering temperature of the glass-ceramic particles to initially transform said polymeric coating into a carbonaceous residue followed by volatilizing said residue, thereby permitting the coalescence of said copper particles only simultaneously with the coalescence of said glass-ceramic particles at said temperature.
References Cited (Backward Citations)
US3510296A
Cited
US3266893A
Cited
US3341325A
Cited
US3661571A
Cited
US4055615A
Cited
US4083719A
Cited
US4109377A
Cited
US4289719A
Cited
US4431449A
Cited
US4234367A
Cited
US4483905A
Cited
US4483905B1
Cited
JPS5735601A
Cited
JPS5735561A
Cited
JPS5761026A
Cited
SU929722A1
Cited
US4434134A
Cited
JPS6126A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-08 | 1990-12-08 | 1991-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-08 | 1994-12-08 | 1995-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-08 | 1998-12-08 | 1999-06-09 | $7700.00 | Window Closed / Lapsed |