US4669176A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for diffusing a semiconductor substrate through a metal silicide layer by rapid heating
Assignee: Seiko Epson Corp
•
Filing: 1985-07-19
•
Granted: 1987-06-02
•
Expires: 2005-07-19
Abstract
Abstract A method for forming a diffused region on a semiconductor substrate is provided. A silicide layer is formed in a region of a substrate where a diffused layer is to be formed and a material containing an impurity to be defined into the substrate deposited on the silicide layer. The device is heat treated to cause the impurity to diffuse through the silicide layer into the substrate. The method may be used to produce a MOSFET.
Inventors
- 👤 Juri Kato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:40
CPC Classifications
H; H10; H10P; H10P32/00; H10P32/10; H10P32/17; H10P32/171; H10P32/14; H10P32/1408; H10P32/1414; Y; Y10; Y10S; Y10S438/00; Y10S438/914; Y10S438/923
Claims Analysis
Total Claims: 44
Claim 1
Independent Claim
116 words
A method of forming a region of impurities diffused into a silicon substrate of a semiconductor device comprising: providing a silicon substrate; forming a silicide layer on the surface of the substrate in at least a region where the region of impurities is to be formed; depositing an impurity layer including the impurity to be diffused onto the silicide layer to form a device; and heating the device for a period of less than about 100 seconds at a temperature sufficient to cause the impurities from the impurity layer on the silicide layer to be diffused through the silicide layer into the surface of the substrate for forming a shallow diffused region in the silicon substrate.
Claim 2
Independent Claim
116 words
A method of forming a region of impurities diffused into a silicon substrate of a semiconductor device comprising: providing a silicon substrate; forming a silicide layer on the surface of the substrate in at least a region where the region of impurities is to be formed; depositing an impurity layer including the impurity to be diffused onto the silicide layer to form a device; and heating the device for a period of less than about 100 seconds at a temperature sufficient to cause the impurities from the impurity layer on the silicide layer to be diffused through the silicide layer into the surface of the substrate for forming a shallow diffused region in the silicon substrate.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein said impurity is selected from the group consisting of phosphorus and boron.
Claim 4
Dependent Claim
29 words
The method of claim 1, wherein said step of depositing the impurity layer onto said silicide layer comprises coating said silicide layer with a phosphosilicate glass containing the impurity.
Claim 5
Dependent Claim
20 words
The method of claim 3, wherein said step of depositing the impurity layer onto said silicide layer comprises spin coating.
Claim 6
Dependent Claim
18 words
The method of claim 1, wherein said step of heating comprises exposing said device to a halogen lamp.
Claim 7
Dependent Claim
31 words
The method of claim 1, wherein said step of heating is performed at a temperature of greater than about 900° C. for a period of between about one and 100 seconds.
Claim 8
Dependent Claim
18 words
The method of claim 1, wherein said step of heating is performed in an atmosphere of inactive gas.
Claim 9
Dependent Claim
15 words
The method of claim 7, wherein the inactive gas is nitrogen or an inert gas.
Claim 10
Dependent Claim
27 words
The method of claim 1, further comprising baking the device at a temperature of less than 500° C. after depositing the impurity layer onto the silicide layer.
Claim 11
Dependent Claim
17 words
The method of claim 1, wherein said silicide layer is comprised of a high melting point silicide.
Claim 12
Dependent Claim
24 words
The method of claim 10, wherein said silicide is selected from the group consisting of titanium silicide, tungsten silicide, molybdenum silicide and tantalum silicide.
Claim 13
Dependent Claim
18 words
The method of claim 1, wherein said diffused region has a thickness of less than about 300 Å.
Claim 14
Dependent Claim
31 words
The method of claim 1, wherein said silicide layer is formed by applying a metal layer on said substrate and annealing the substrate and metal layer to form said silicide layer.
Claim 15
Dependent Claim
36 words
The method of claim 13, wherein said annealing occurs during said step of heating said device to cause said silicide layer to be formed and said impurities to be diffused through the silicide layer being formed.
Claim 16
Independent Claim
130 words
A method for forming a semiconductor device comprising: providing a silicon substrate; forming a first diffusion layer on said silicon substrate; providing an insulating layer on said first diffusion layer; forming a contact hole through said insulating layer, to extend to said first diffusion layer; forming a contact layer comprised of one of a metal or a silicide on said insulating layer and through said contact hole to contact said first diffusion layer; depositing an impurity layer including an impurity onto said contact layer to yield a device; and heating said device for a period of less than about 100 seconds at a temperature sufficient to cause said impurity to diffuse through said contact layer and into said substrate to form a second diffusion layer adjacent to the contact hole.
Claim 17
Independent Claim
130 words
A method for forming a semiconductor device comprising: providing a silicon substrate; forming a first diffusion layer on said silicon substrate; providing an insulating layer on said first diffusion layer; forming a contact hole through said insulating layer, to extend to said first diffusion layer; forming a contact layer comprised of one of a metal or a silicide on said insulating layer and through said contact hole to contact said first diffusion layer; depositing an impurity layer including an impurity onto said contact layer to yield a device; and heating said device for a period of less than about 100 seconds at a temperature sufficient to cause said impurity to diffuse through said contact layer and into said substrate to form a second diffusion layer adjacent to the contact hole.
Claim 18
Dependent Claim
14 words
The method of claim 15, wherein said impurity is one of phosphorus and boron.
Claim 19
Dependent Claim
23 words
The method of claim 15, wherein said step of depositing onto said contact layer comprises coating said contact layer with a phosphosilicate glass.
Claim 20
Dependent Claim
17 words
The method of claim 17, wherein the step of depositing onto said contact layer comprises spin coating.
Claim 21
Dependent Claim
18 words
The method of claim 15, wherein said step of heating comprises exposing said device to a halogen lamp.
Claim 22
Dependent Claim
31 words
The method of claim 15, wherein said step of heating is performed at a temperature of greater than about 900° C. for a period of between about one and 100 seconds.
Claim 23
Dependent Claim
18 words
The method of claim 15, wherein said step of heating is performed in an atmosphere of inactive gas.
Claim 24
Dependent Claim
15 words
The method of claim 21, wherein the inactive gas is nitrogen or an inert gas.
Claim 25
Dependent Claim
26 words
The method of claim 15, further comprising baking at a temperature of less than about 500° C. after depositing the impurity layer onto the silicide layer.
Claim 26
Dependent Claim
17 words
The method of claim 15, wherein said silicide layer is comprised of a high melting point silicide.
Claim 27
Dependent Claim
24 words
The method of claim 24, wherein said silicide is selected from the group consisting of titanium silicide, tungsten silicide, molybdenum silicide and tantalum silicide.
Claim 28
Dependent Claim
21 words
The method of claim 15, wherein said second diffusion layer has a thickness less than that of said first diffusion layer.
Claim 29
Dependent Claim
19 words
The method of claim 15, wherein said contact layer is a metal and said metal is applied by sputtering.
Claim 30
Independent Claim
118 words
A method for forming a semiconductor device on a silicon semiconductor substrate having diffused regions doped with impurities beneath the surface of the substrate, comprising: providing a silicon substrate; forming a gate insulating film on the substrate; providing a gate electrode on the gate insulating film; forming a silicide layer on the gate electrode; depositing an impurity layer including an impurity to be diffused on the silicide layer to yield a device; and heat treating the device for a period of less than about 100 seconds at a temperature sufficient to cause the impurity to be diffused through the silicide layer into the substrate in regions adjacent the gate for forming source and drain regions of the device.
Claim 31
Independent Claim
118 words
A method for forming a semiconductor device on a silicon semiconductor substrate having diffused regions doped with impurities beneath the surface of the substrate, comprising: providing a silicon substrate; forming a gate insulating film on the substrate; providing a gate electrode on the gate insulating film; forming a silicide layer on the gate electrode; depositing an impurity layer including an impurity to be diffused on the silicide layer to yield a device; and heat treating the device for a period of less than about 100 seconds at a temperature sufficient to cause the impurity to be diffused through the silicide layer into the substrate in regions adjacent the gate for forming source and drain regions of the device.
Claim 32
Dependent Claim
13 words
The method of claim 28, wherein said gate insulating film is silicon dioxide.
Claim 33
Dependent Claim
14 words
The method of claim 28, wherein said impurity is one of phosphorus and boron.
Claim 34
Dependent Claim
26 words
The method of claim 28, wherein said step of depositing an impurity layer on said silicide layer comprises coating said silicide layer with a phosphosilicate glass.
Claim 35
Dependent Claim
20 words
The method of claim 31, wherein said step of depositing the impurity layer onto said silicide layer comprises spin coating.
Claim 36
Dependent Claim
19 words
The method of claim 28, wherein said step of heat treating comprises exposing said device to a halogen lamp.
Claim 37
Dependent Claim
32 words
The method of claim 28 wherein said step of heat treating is performed at a temperature of greater than about 900° C. for a period of between about one and 100 seconds.
Claim 38
Dependent Claim
18 words
The method of claim 28, wherein said step of heattreating is performed in an atmosphere of inactive gas.
Claim 39
Dependent Claim
15 words
The method of claim 35, wherein the inactive gas is nitrogen or an inert gas.
Claim 40
Dependent Claim
27 words
The method of claim 28, further comprising the step of baking the device at a temperature of less than 500° C. prior to heat treating the device.
Claim 41
Dependent Claim
17 words
The method of claim 28, wherein said silicide layer is comprised of a high melting point silicide.
Claim 42
Dependent Claim
25 words
The method of claim 38, wherein said silicide layer is selected from the group consisting of titanium silicide, tungsten silicide, molybdenum silicide and tantalum silicide.
Claim 43
Dependent Claim
19 words
The method of claim 28, wherein said source and drain regions have thicknesses of less than about 300 Å.
Claim 44
Dependent Claim
31 words
The method of claim 28, wherein said silicide layer is formed by applying a metal layer on said substrate and annealing said substrate and metal layer to form said silicide layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-01 | 1990-12-01 | 1991-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-01 | 1994-12-01 | 1995-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-01 | 1998-12-01 | 1999-06-02 | $7700.00 | Window Closed / Lapsed |