Plastic article containing electrically conductive fibers

Claim 2

A plastic article in the form of a plate or sheet, which is electrically conductive at least in certain predetermined parts, comprising a plastic material including electrically conductive fibers said fibers having a specific conductivity of at least 0.5% of the copper standard which are substantially evenly distributed in said parts, said fibers having a length L and an equivalent diameter D varying between about 0.002 mm and about 0.015 mm so that the ratio D/L varies from about 0.0005 to about 0.008 for a major part of said fibers and wherein the volume concentration (C%) of said fibers in said parts varies between about 0.05% and about 0.5% so that the specific resistance of the article is less than about 3.1 ohm-cm, wherein said plastic material is a thermoplastic resin and said article is formed by injection moulding.

Claim 3

An article according to claim 1 wherein when the thickness of said plate or sheet is less than about 3 mm, the volume concentration C of conductive fibers in the plate or sheet meets the relationship C≧1.4 D/L-0.00082 and when the thickness of said plate or sheet is between about 3 mm and about 6 mm the volume concentration (C) meets the relationship C≧D/L-0.0013.

Claim 4

An article according to claim 2, whereby C≧3.34 D/L-0.00041.

Claim 5

An article according to claim 1, wherein the conductive fibers have relatively smooth surfaces.

Claim 6

An article according to claim 1 or 4, wherein the conductive fibers are stainless steel fibers.

Claim 7

An article according to claim 1, wherein the plastic is a thermosetting resin.

Claim 8

An article according to claim 6, wherein it is a foamed resin.

Claim 9

An article according to claim 6, wherein the plastic is an elastomer.

Claim 10

An article according to claim 7 wherein the plastic is an elastomer.

Claim 11

An article according to claim 1, wherein it comprises still other fibers.

Claim 12

An article according to claim 10, wherein at least part of the other fibers are reinforcing fibers.

Claim 13

A plastic grain having a length between about 0.4 cm and 1.2 cm including a pure plastic and a low molecular weight plastic material and electrically conductive fibers which have been subjected to shear forces so that they are dispersed therein, whereby the conductive fiber content therein has a concentration of said conductive fibers that ranges from about 0.5% to about 2.0%.

Claim 14

A plastic grain having a length between about 0.4 cm and 1.2 cm including a pure plastic and a low molecular weight plastic material and electrically conductive fibers which have been subjected to shear forces so that they are dispersed therein, whereby the conductive fiber content therein has a concentration of said conductive fibers that ranges from about 0.5% to about 2.0%.

Claim 15

A plastic grain according to claim 12 whereby they further include other fibers.

Claim 16

A thread comprising a bundle of between 1000 and 35000 adjacent conductive fibers embedded in plastic, wherein the fiber content therein is between about 30 volume percent and about 70 volume percent, the fiber conductivity is at least 0.5% of the copper standard, the fiber diameter is a most 0.015 mm and the plastic includes a thermoplastic polymer of relatively low molecular weight.

Claim 17

A thread comprising a bundle of between 1000 and 35000 adjacent conductive fibers embedded in plastic, wherein the fiber content therein is between about 30 volume percent and about 70 volume percent, the fiber conductivity is at least 0.5% of the copper standard, the fiber diameter is a most 0.015 mm and the plastic includes a thermoplastic polymer of relatively low molecular weight.

Claim 18

A thread as in claim 14 further including an outer sheath comprised of an additional plastic material.

Claim 19

A plastic composite article in the form of a plate or sheet comprised of a plastic material in which the volume concentration (C%) of electrically conductive fibers varies from about 0.03 to about 0.5%, said conductive fibers have an effective diameter (D) ranging from about 0.002 mm to about 0.015 mm and an average length (L) varying from about 0.5 mm to about 5.0 mm with a resulting D/L ratio ranging from about 0.0005 to about 0.008 for a major part of the fibers and which are substantially uniformly distributed throughout the composite article so that the article has a predetermined level of conductivity so that the resistance of the composite article is less than about 3.1 ohm-cm wherein the conductive fibers have a specific conductivity of at least 0.5% of the copper standard.

Claim 20

A plastic composite article in the form of a plate or sheet comprised of a plastic material in which the volume concentration (C%) of electrically conductive fibers varies from about 0.03 to about 0.5%, said conductive fibers have an effective diameter (D) ranging from about 0.002 mm to about 0.015 mm and an average length (L) varying from about 0.5 mm to about 5.0 mm with a resulting D/L ratio ranging from about 0.0005 to about 0.008 for a major part of the fibers and which are substantially uniformly distributed throughout the composite article so that the article has a predetermined level of conductivity so that the resistance of the composite article is less than about 3.1 ohm-cm wherein the conductive fibers have a specific conductivity of at least 0.5% of the copper standard.

Claim 21

A plastic composite as in claim 16 wherein the thickness of the plate or sheet is less than 3 mm and C≧1.4 D/L-0.12.

Claim 22

A plastic composite as in claim 16 wherein the thickness of the plate or sheet varies from 3 mm to about 6 mm and C≧D/L-0.18.

Claim 23

A plastic plate or sheet formed from a plastic material having a predetermined portions through which conductive fibers are substantially uniformly distributed, said conductive fibers being present in said predetermined portions at a concentration (C %) ranging between about 0.05% to about 0.5% volume, with a major part of the individual fibers in said predetermined portions having a D/L ratio which varies from about 0.0005 to about 0.008 so that in said predetermined portions the resistance of the plate or sheet is less than about 3.1 ohm-cm wherein the conductive fibers have a specific conductivity of at least 0.5% of the copper standard.

Claim 24

A plastic plate or sheet formed from a plastic material having a predetermined portions through which conductive fibers are substantially uniformly distributed, said conductive fibers being present in said predetermined portions at a concentration (C %) ranging between about 0.05% to about 0.5% volume, with a major part of the individual fibers in said predetermined portions having a D/L ratio which varies from about 0.0005 to about 0.008 so that in said predetermined portions the resistance of the plate or sheet is less than about 3.1 ohm-cm wherein the conductive fibers have a specific conductivity of at least 0.5% of the copper standard.

Claim 25

A plastic article in the form of a plate or sheet according to any one of claims 1, 16 or 19 wherein the article exhibits a shielding effectiveness (SE) against electromagnetic radiation of at least about 25 dB.

Claim 26

A plastic article according to claim 20, wherein the shielding effectiveness occurs at a frequency of about 1 GHz.

Claim 27

A plastic article according to claim 20, wherein the shielding effectiveness occurs over a frequency range of about 0.4 GHz to about 5 GHz.

Claim 28

A process for forming plastic articles having at least predetermined electrically conductive portions therein including the steps of admixing a predetermined volume of substantially pure plastic material with another predetermined volume of fiber/plastic composite granules, said granules being comprised of at least a plastic material with a relatively low molecular weight which is compatible with said pure plastic material and conductive fibers, embedded in the low molecular weight material, having a substantially parallel fiber arrangement within the granule, said granule being sheathed with an additional plastic material and having between 1000 and 35000 conductive fibers in a bundled arrangement with a fiber diameter of less than about 0.015 mm, heating the admixture and working the heated admixture while maintaining a low shear conditions to avoid excessive breakage of the fibers, but with sufficient shear to substantially evenly disperse the fibers within the heated admixture, forwarding the hot worked admixture through at least one orifice and forming it to a certain shape and cooling the thus shaped admixture.

Claim 29

A process for forming plastic articles having at least predetermined electrically conductive portions therein including the steps of admixing a predetermined volume of substantially pure plastic material with another predetermined volume of fiber/plastic composite granules, said granules being comprised of at least a plastic material with a relatively low molecular weight which is compatible with said pure plastic material and conductive fibers, embedded in the low molecular weight material, having a substantially parallel fiber arrangement within the granule, said granule being sheathed with an additional plastic material and having between 1000 and 35000 conductive fibers in a bundled arrangement with a fiber diameter of less than about 0.015 mm, heating the admixture and working the heated admixture while maintaining a low shear conditions to avoid excessive breakage of the fibers, but with sufficient shear to substantially evenly disperse the fibers within the heated admixture, forwarding the hot worked admixture through at least one orifice and forming it to a certain shape and cooling the thus shaped admixture.

Claim 30

A process according to claim 23, wherein the pure plastic material of step (a) is comprised of plastic pellets.

Claim 31

A process according to claim 23 including the further step of forming the article by injection molding the worked mixture.

Claim 32

A process as set forth in claim 23, wherein the volume concentration (C%) of said conductive fibers in said conductive portions is between about 0.05 and about 0.5%.

Claim 33

A process as set forth in claim 23, wherein the volume concentration (C%) of said conductive fibers in said conductive portions ranges from about 0.5% to about 1.0%.

Claim 34

The process of claim 23 wherein the granule has a flattened cross-sectional surface.

Claim 35

The process of claim 23 wherein the length of the granule ranges from about 0.4 cm to 1.5 cm.

Claim 36

The process of claim 23, wherein the fiber content in said bundle is between about 30% and about 70% of the volume of the granule.

Claim 37

The process of claim 23 further including other fibers in the bundled arrangement.

Claim 38

A process according to claim 23, wherein the worked mixture is extruded in thread shape form with a dispersed conductive fiber content ranging between about 0.5% vol. and about 2% vol.

Claim 39

A process as in claim 32 including the further step of chopping the extruded thread into grains having a length from about 0.4 cm to about 1.2 cm.

Claim 40

A process according to claim 33 including the further steps of admixing the grains with a predetermined volume of substantially pure plastic material so as to provide a mixture wherein from about 0.05% to about 0.5% vol. of fibers are substantially evenly distributed, and forming the worked mixture into a plastic article wherein the D/L ratio varies from about 0.0005 to 0.008 for a major part of the fibers.

Claim 41

A process as in claim 34 wherein the plastic in the grains has a softening and melting point, respectively, at most equal to that of the plastic material with which they are admixed.

Claim 42

A process as in claim 34 wherein the article is formed by extrusion through a die.

Claim 43

A process as in claim 34 wherein the article is formed by injection molding.

Claim 44

A process according to claim 23 including the further step of forming the article by extrusion through a die.

Claim 45

A process according to claim 38 wherein the admixture is extruded to a thread with a conductive fiber content between about 0.5% volume and about 2% volume.

Claim 46

A process according to claim 32 or 39 including the further step of chopping the extruded thread into grains having a length from about 0.4 cm to about 1.2 cm.

Claim 47

A process for forming plastic articles having at least predetermined conductive portions including the steps of (a) admixing the grains obtained according to the process of claim 40 with a predetermined volume of substantially pure plastic material; (b) heating and working the plastic admixture to provide a random dispersion of the fibers at least within the predetermined conductive portions and (c) forwarding the hot worked admixture through at least one orifice in view of forming it to a certain shape and (d) cooling the thus shaped admixture.

Claim 48

A process according to claim 34 or 41 wherein the pure plastic material is comprised of plastic pellets.

Claim 49

The process of claim 41 wherein the process includes the additional step of dry mixing the pellets and the grains prior to step (b).

Claim 50

A process for forming a plastic article having at least predetermined conductive portions including the steps of (a) heating and working the grains obtained by the process of claim 33 to provide a substantially even distribution of the fibers in the worked plastic and (b) forwarding the hot worked plastic through at least one orifice in view of forming it to a certain shape and (c) cooling the thus shaped plastic.

Claim 51

A process according to claim 41 or 44 whereby the heated plastic is worked while maintaining low shear conditions to avoid excessive breakage of the fibers, but with sufficient shear to substantially evenly distribute the fibers within the admixture.

Claim 52

A process according to claim 41 or 44 wherein the article is formed by injection molding.

Claim 53

A process according to claim 41 or 44 wherein the article is formed by extrusion.

Claim 54

A process for forming plastic articles having at least predetermined electrically conductive portions therein including the steps of admixing a predetermined volume of substantially pure plastic material with another predetermined volume of fiber/plastic composite granules, said granules, being comprised of at least a plastic material with a relatively low molecular weight which is compatible with said pure plastic material and conductive fibers having a substantially parallel fiber arrangement within the granule, heating the admixture and working the heated admixture while maintaining low shear conditions to avoid excessive breakage of the fibers, but with sufficient shear to substantially evenly disperse the fibers within the heated admixture, forwarding the hot worked admixture through at least one orifice and forming it to a certain shape with a conductive fiber content between about 0.5% volume and about 2% volume, cooling the thus shaped mixture and the further step of chopping the extruded shape into grains having a length from about 0.4 centimeters to about 1.2 centimeters.

Claim 55

A process for forming plastic articles having at least predetermined electrically conductive portions therein including the steps of admixing a predetermined volume of substantially pure plastic material with another predetermined volume of fiber/plastic composite granules, said granules, being comprised of at least a plastic material with a relatively low molecular weight which is compatible with said pure plastic material and conductive fibers having a substantially parallel fiber arrangement within the granule, heating the admixture and working the heated admixture while maintaining low shear conditions to avoid excessive breakage of the fibers, but with sufficient shear to substantially evenly disperse the fibers within the heated admixture, forwarding the hot worked admixture through at least one orifice and forming it to a certain shape with a conductive fiber content between about 0.5% volume and about 2% volume, cooling the thus shaped mixture and the further step of chopping the extruded shape into grains having a length from about 0.4 centimeters to about 1.2 centimeters.

Claim 56

The process as in claim 48 wherein the certain shape is that of a thread.