Glass fiber reinforced thermoplastic composition and process for its preparation

Claim 2

A blending concentrate of glass filaments uniformly predisposed in highly oriented relationship in a thermoplastic resin and having the form of generally rod-shaped granules of at least 1/8 inch in length said granules being combinable by simple mixing with substantial quantities of unreinforced thermoplastic resin pellets to form dry free-flowing compositions which, on hot molding or shaping, yield superior reinforced articles, said concentrate consisting essentially of about 70 to 90% by weight of glass filaments and about 30 to 10% by weight of a thermoplastic resin chosen from the group consisting of polystyrene, styrene-acrylonitrile copolymer, polyethylene, polypropylene, polycarbonate, polyamide and polyester with a multiplicity of glass filaments extending in essentially parallel alignment throughout the length of each individual granule of said concentrate.

Claim 3

A blending concentrate as in claim 1 wherein said granules are generally at least 1/4 inch in length.

Claim 4

A free flowing thermoplastic resin based composition readily thermoformable into a finished article of high strength comprising a dry blend of the concentrate of claim 1 with a sufficient quantity of pellets of the same unreinforced thermoplastic resin contained in said concentrate to bring the glass filament content of said composition into the range of about 20 to about 35% by weight.

Claim 5

The composition of claim 3 wherein the granules of which said concentrate is composed are largely between 1/4 and 1/2 inch in length.

Claim 6

A composition according to claim 3 wherein the thermoplastic resin is polystyrene.

Claim 7

A composition according to claim 3 wherein the thermoplastic resin is styrene-acrylonitrile copolymer.

Claim 8

A composition according to claim 3 wherein the thermoplastic resin is polyethylene or polypropylene.

Claim 9

A process for preparing a superior, granular, blending concentrate containing an unusually high level of reinforcing glass filaments arranged in a highly oriented disposition in a thermoplastic resin matrix comprising: a. continuously passing a plurality of longitudinally aligned glass filaments through a zone containing a liquid pool of thermoplastic resin chosen from the group consisting of polystyrene, styrene-acrylonitrile copolymer, polyethylene, polypropylene, polycarbonate, polyamide and polyester, b. continuously impregnating said glass filaments with the thermoplastic resin in said zone at a resin to glass ratio of between about 1 to 9 and about 3 to 7 by weight, c. continuously withdrawing the resin impregnated glass filaments from said zone and forming same into a unitary elongate solid mass wherein said glass filaments extend in substantially parallel alignment with the longitudinal dimension of said elongate solid mass, and d. passing the unitary continuous elongate solid mass to a cutting zone and maintaining said mass at a somewhat elevated temperature of at least 80° F. while cutting same transversely into short lengths of at least 1/8 inch so that neat free-flowing rod-shaped granules are formed without substantial longitudinal splitting.

Claim 10

A process for preparing a superior, granular, blending concentrate containing an unusually high level of reinforcing glass filaments arranged in a highly oriented disposition in a thermoplastic resin matrix comprising: a. continuously passing a plurality of longitudinally aligned glass filaments through a zone containing a liquid pool of thermoplastic resin chosen from the group consisting of polystyrene, styrene-acrylonitrile copolymer, polyethylene, polypropylene, polycarbonate, polyamide and polyester, b. continuously impregnating said glass filaments with the thermoplastic resin in said zone at a resin to glass ratio of between about 1 to 9 and about 3 to 7 by weight, c. continuously withdrawing the resin impregnated glass filaments from said zone and forming same into a unitary elongate solid mass wherein said glass filaments extend in substantially parallel alignment with the longitudinal dimension of said elongate solid mass, and d. passing the unitary continuous elongate solid mass to a cutting zone and maintaining said mass at a somewhat elevated temperature of at least 80° F. while cutting same transversely into short lengths of at least 1/8 inch so that neat free-flowing rod-shaped granules are formed without substantial longitudinal splitting.

Claim 11

The process of claim 8 wherein said thermoplastic resin is polystyrene and the elevated temperature in step (d) is at least 100° F.

Claim 12

The process of claim 8 wherein said thermoplastic resin is polypropylene and the elevated temperature in step (d) is at least 100° F.

Claim 13

The process of claim 8 wherein said thermoplastic resin is polyethylene and the elevated temperature in step (d) is at least 90° F.

Claim 14

A process according to claim 8 wherein said solid mass is maintained at a temperature of at least 90° F. while being cut during step (d).

Claim 15

A process according to claim 8 wherein said liquid pool in step (a) comprises an aqueous emulsion or suspension of said thermoplastic resin.