Anisotropically pressure-sensitive electroconductive composite sheets and method for the preparation thereof
Assignee: Shin-Etsu Polymer Co Ltd
•
Filing: 1978-06-01
•
Granted: 1980-04-22
•
Expires: 1998-06-01
Abstract
Abstract Anisotropically pressure-sensitive electroconductive composite sheets are provided which have a very low electric conductive resistance in the direction perpendicular to the plane of the sheet when compressed with an adequate pressure in the direction but a high insulating resistance in all directions within the plane of the sheet. The composite sheets are constructed so that electrically conductive fibers are uniformly dispersed in the matrix of an electrically insulating substance, the average length of the fibers ranging from 20 to 80% of the thickness of the sheet, and are aligned in the direction substantially perpendicular to the plane. They are useful as a switching material in various miniaturized electronic circuits.
Inventors
- 👤 Ryoichi Sado
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 10:07
CPC Classifications
H; H01; H01H; H01H13/00; H01H13/70; H01H13/78; H01H13/785; B; B29; B29C; B29C48/00; B29C48/022; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/12; B29C70/14; B29C70/88; B29C70/882; H01B; H01B5/00; H01B5/16; H01R; H01R13/00; H01R13/02; H01R13/22; H01R13/24; H01R13/2407; H01R13/2414; H01R31/00; H01R43/00; H01R43/007; B29C48/03; B29C48/07; B29C48/08; B29K; B29K2105/00; B29K2105/06; H01H2201/00; H01H2201/022; H01H2201/032; H01H2201/036; Y; Y10; Y10T; Y10T428/00; Y10T428/14; Y10T428/1405; Y10T428/1438; Y10T428/24; Y10T428/24174; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/249942; Y10T428/249945; Y10T428/29; Y10T428/2913; Y10T428/2929; Y10T428/2931; Y10T428/2933; Y10T428/2938; Y10T428/294; Y10T428/2973; Y10T428/2978; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
85 words
An anisotropically electroconductive thin composite sheet having a plane top surface and a plane bottom surface substantially parallel to said top surface, and composed of an electrically insulating material and a plurality of electrically conductive fibers dispersed through said sheet in alignment in a direction substantially perpendicular to said plane top surface and said plane bottom surface, the average length of said electrically conductive fibers ranging from 20 to 80% of the thickness of said sheet and at least some extending completely through said sheet.
Claim 2
Dependent Claim
85 words
An anisotropically electroconductive thin composite sheet having a plane top surface and a plane bottom surface substantially parallel to said top surface, and composed of an electrically insulating material and a plurality of electrically conductive fibers dispersed through said sheet in alignment in a direction substantially perpendicular to said plane top surface and said plane bottom surface, the average length of said electrically conductive fibers ranging from 20 to 80% of the thickness of said sheet and at least some extending completely through said sheet.
Claim 3
Dependent Claim
19 words
The anisotropically electroconductive composite sheet, as claimed in claim 1, wherein said electrically conductive fiber is a carbon fiber.
Claim 4
Dependent Claim
19 words
The anisotropically electroconductive composite sheet, as claimed in claim 1, wherein said electrically conductive fiber is a metal fiber.
Claim 5
Dependent Claim
23 words
The anisotropically electroconductive composite sheet, as claimed in claim 1, wherein the diameter of said electrically conductive fiber is less than 0.2 mm.
Claim 6
Dependent Claim
37 words
The anisotropically electroconductive composite sheet, as claimed in claim 1, wherein the volume of said electrically conductive fibers is in the range of from about 0.1 to about 20% of the total volume of said composite sheet.
Claim 7
Dependent Claim
19 words
The anisotropically electroconductive composite sheet, as claimed in claim 1, wherein said electrically insulating material is a polymeric substance.
Claim 8
Dependent Claim
17 words
The anisotropically electroconductive composite sheet, as claimed in claim 6, wherein said polymeric substance is an elastomer.
Claim 9
Dependent Claim
17 words
The anisotropically electroconductive composite sheet, as claimed in claim 7, wherein said elastomer is a cured organopolysiloxane.
Claim 10
Dependent Claim
171 words
An anisotropically pressure sensitive electroconductive composite sheet comprising a sheet matrix having substantially parallel first and second planar surfaces on each side and being of a compressible polymeric insulating material, a multiplicity of electrically conductive fibers disposed substantially perpendicular to each of said first and second planar surfaces and being uniformly distributed within said matrix but separated from each other by insulating material of said sheet matrix, at least some of said fibers extending from one of said first surfaces to said second surface, and completely through said sheet and at least some of said fibers being shorter than the space in between said first and second surfaces, said short fibers contributing little to the conductivity of said sheet in the uncompressed state but adding to the conductivity thereof when said sheet is compressed, the number of fibers extending completely through said sheet being such that an average of the lengths of all of the fibers is within the range of 20 to 80% of the thickness of the sheet material.
Claim 11
Dependent Claim
171 words
An anisotropically pressure sensitive electroconductive composite sheet comprising a sheet matrix having substantially parallel first and second planar surfaces on each side and being of a compressible polymeric insulating material, a multiplicity of electrically conductive fibers disposed substantially perpendicular to each of said first and second planar surfaces and being uniformly distributed within said matrix but separated from each other by insulating material of said sheet matrix, at least some of said fibers extending from one of said first surfaces to said second surface, and completely through said sheet and at least some of said fibers being shorter than the space in between said first and second surfaces, said short fibers contributing little to the conductivity of said sheet in the uncompressed state but adding to the conductivity thereof when said sheet is compressed, the number of fibers extending completely through said sheet being such that an average of the lengths of all of the fibers is within the range of 20 to 80% of the thickness of the sheet material.
Claim 12
Independent Claim
218 words
A method of preparing an anisotropically conductive sheet comprising mixing an electrically insulating substance while soft but being capable of hardening with electrically conductive fibers, some of which are of a length which will be equal to the width of the sheet and extend completely through said sheet so as to render said sheet electrically conductive, and some of which are shorter than the width of the sheet, subjecting the mixture to a shearing deformation in one direction in a manner to align the electrically conductive fibers in a direction parallel to the shearing deformation and parallel to the surface of the sheet to form a composite of electrical insulating substance and electrically conductive fibers which are separated from each other by the insulating substance to obtain a composite, subjecting the composite to hardening, and slicing the hardened composite into a sheet having top and bottom surfaces substantially perpendicular to the direction of the alignment of the electrically conductive layers and in a manner such that some of the fibers extend from one surface to the other and others do not, the number of fibers extending completely through said sheet being such that an average of the lengths of all of the fibers is within the range of 20 to 80% of the thickness of the sheet material.
Claim 13
Independent Claim
218 words
A method of preparing an anisotropically conductive sheet comprising mixing an electrically insulating substance while soft but being capable of hardening with electrically conductive fibers, some of which are of a length which will be equal to the width of the sheet and extend completely through said sheet so as to render said sheet electrically conductive, and some of which are shorter than the width of the sheet, subjecting the mixture to a shearing deformation in one direction in a manner to align the electrically conductive fibers in a direction parallel to the shearing deformation and parallel to the surface of the sheet to form a composite of electrical insulating substance and electrically conductive fibers which are separated from each other by the insulating substance to obtain a composite, subjecting the composite to hardening, and slicing the hardened composite into a sheet having top and bottom surfaces substantially perpendicular to the direction of the alignment of the electrically conductive layers and in a manner such that some of the fibers extend from one surface to the other and others do not, the number of fibers extending completely through said sheet being such that an average of the lengths of all of the fibers is within the range of 20 to 80% of the thickness of the sheet material.
References Cited (Backward Citations)
US2744981A
Cited
US2885459A
Cited
US3324445A
Cited
US3795037A
Cited
US3962531A
Cited
US3983265A
Cited
US3979356A
Cited
US3949141A
Cited
US3998513A
Cited
US4003621A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-22 | 1983-10-22 | 1984-04-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-22 | 1987-10-22 | 1988-04-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-22 | 1991-10-22 | 1992-04-22 | $7700.00 | Window Closed / Lapsed |