Method of making MOS VLSI semiconductor device with metal gate and clad source/drain
Assignee: Texas Instruments Inc
•
Filing: 1984-08-07
•
Granted: 1987-04-28
•
Expires: 2004-08-07
Abstract
Abstract Metal-gate transistors with metal silicide cladding of the source/drain regions, as may be used in very high density dynamic RAM devices, are made by a process in which the metal gate is encapsulated in oxide and the cladding is self aligned with the encapsulated gate. A thin coating of a refractory metal is applied to the source/drain areas and heated to react with the exposed silicon. The unreacted metal is removed by an etchant that does not disturb the metal gate or the silicide.
Inventors
- 👤 Robert R. Doering
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:56
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; Y; Y10; Y10S; Y10S438/00; Y10S438/902; Y10T; Y10T156/00; Y10T156/17; Y10T156/1702; Y10T156/1744; Y10T156/1776; Y10T156/1778; Y10T156/178
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
125 words
A method of making a semiconductor device comprising the steps of: forming an electrode on a face of a semiconductor body, covering the top and sides of said electrode with an insulator coating, depositing a reactive material on said face, and subjecting said body to a treatment to cause the material to react with the surface of the semiconductor body to create a conductive compound, and removing the unreacted material from said face with an etchant which does not substantially attack said insulator coating or said conductive compound, said etchant tending to react with the material of said electrode on contact, the electrode being isolated from said etchant by said insulator coating on top and sidewalls to prevent reaction with the material of said electrode.
Claim 2
Independent Claim
125 words
A method of making a semiconductor device comprising the steps of: forming an electrode on a face of a semiconductor body, covering the top and sides of said electrode with an insulator coating, depositing a reactive material on said face, and subjecting said body to a treatment to cause the material to react with the surface of the semiconductor body to create a conductive compound, and removing the unreacted material from said face with an etchant which does not substantially attack said insulator coating or said conductive compound, said etchant tending to react with the material of said electrode on contact, the electrode being isolated from said etchant by said insulator coating on top and sidewalls to prevent reaction with the material of said electrode.
Claim 3
Dependent Claim
30 words
A method according to claim 1 wherein said semiconductor body is silicon, said electrode is a metal, said insulator coating is silicon oxide, and said conductive compound is a silicide.
Claim 4
Dependent Claim
28 words
A method according to claim 2 wherein said metal is a refractory metal, and said conductive compound is a silicide of a refractory metal different from said electrode.
Claim 5
Dependent Claim
22 words
A method according to claim 3 wherein said refractory metal of said electrode is molybdenum and said conductive compound is titanium silicide.
Claim 6
Dependent Claim
19 words
A method according to claim 4 wherein said reactive material is titanium, and said treatment is a heat treatment.
Claim 7
Dependent Claim
13 words
A method according to claim 5 wherein said etchant is an HCl solution.
Claim 8
Dependent Claim
15 words
A method according to claim 6 wherein said HCl solution is about 20% in water.
Claim 9
Dependent Claim
27 words
A method according to claim 5 including the step of implanting an impurity into said face after said step of covering said electrode with an insulator coating.
Claim 10
Dependent Claim
44 words
A method according to claim 8 wherein the step of covering the top and sides of said electrode includes the step of coating the face with a layer of silicon oxide then anisotropically etching to leave silicon oxide on the sidewalls of said electrode.
Claim 11
Dependent Claim
16 words
A method according to claim 9 wherein said electrode is the gate of a field-effect transistor.
Claim 12
Dependent Claim
21 words
A method according to claim 10 wherein said step of removing employs a solution of HCl in water as said etchant.
Claim 13
Dependent Claim
100 words
A method according to claim 1 wherein said step of covering said electrode with insulator coating includes the steps of applying a first insulator coating over a layer of the material of said electrode, then selectively etching both the first insulator coating and the layer of material of the electrode to leave the electrode with a first insulator layer on top of the electrode, then isotropically applying a second insulator coating on said face, then anisotropically etching said second insulator coating to leave sidewall areas of second insulator but to remove the second insulator from flat areas of said face.
Claim 14
Independent Claim
179 words
A method of making a metal gate and clad source/drain structure in a process for manufacture of MOS integrated circuits, comprising the steps of: forming a metal gate on a face of a silicon body by applying a thin layer of molybdenum overlying a thin layer of silicon oxide on said face, and applying a coating of oxide on top of said gate and on the sidewalls of said gate totally encapsulating said gate; forming a titanium silicide layer in the surface of said source/drain regions self-aligned with said oxide on the sidewalls of the metal gate, by depositing a layer of titanium metal on said face, heating the body to react the titanium with silicon, and etching to remove unreacted titanium from the face using a selective etchant which does not attack the titanium silicide, said etchant tending to remove said molybdenum on contact therewith, said metal gate being isolated from said etchant by said coating of oxide on top and on sidewalls of said gate to thereby prevent the etchant from removing material of said metal gate.
Claim 15
Independent Claim
179 words
A method of making a metal gate and clad source/drain structure in a process for manufacture of MOS integrated circuits, comprising the steps of: forming a metal gate on a face of a silicon body by applying a thin layer of molybdenum overlying a thin layer of silicon oxide on said face, and applying a coating of oxide on top of said gate and on the sidewalls of said gate totally encapsulating said gate; forming a titanium silicide layer in the surface of said source/drain regions self-aligned with said oxide on the sidewalls of the metal gate, by depositing a layer of titanium metal on said face, heating the body to react the titanium with silicon, and etching to remove unreacted titanium from the face using a selective etchant which does not attack the titanium silicide, said etchant tending to remove said molybdenum on contact therewith, said metal gate being isolated from said etchant by said coating of oxide on top and on sidewalls of said gate to thereby prevent the etchant from removing material of said metal gate.
Claim 16
Dependent Claim
19 words
A method according to claim 13 wherein said body is P type, and said source/drain regions are N+ type.
Claim 17
Dependent Claim
15 words
A method accordin to claim 14 wherein said etchant is a solution of hydrochloric acid.
Claim 18
Dependent Claim
17 words
A method according to claim 15 wherein said etchant is an aqeuous solution of about 20% HCl.
Claim 19
Dependent Claim
22 words
A method according to claim 16 wherein said step of etching is for about 10 to 15 minutes at about 60° C.
Claim 20
Dependent Claim
105 words
A method according to claim 13 wherein said step of covering said metal gate with said oxide coating includes the steps of applying a first oxide coating over a layer of the metal of said gate, then selectively etching both the first oxide coating and the layer of metal of the gate to leave the metal gate with a first oxide layer on top of the metal gate, then isotropically applying a second oxide coating on said face, then anisotropically etching said second oxide coating to leave sidewall areas of second oxide but to remove the second oxide coating from flat areas of said face.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-27 | 1990-10-27 | 1991-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-27 | 1994-10-27 | 1995-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-27 | 1998-10-27 | 1999-04-28 | $7700.00 | Window Closed / Lapsed |