Conductive coating treatment of glass sheet bending process
Assignee: Magna Donnelly Corp
•
Filing: 1985-12-23
•
Granted: 1987-04-07
•
Expires: 2005-12-23
Abstract
Abstract The specification discloses a method for producing a curved glass member having a transparent, electroconductive coating by first coating the glass flat with indium-tin oxide, followed by coating that film with a layer of carbonaceous material and covering that layer with a mating piece of glass while the two pieces of glass are bent in a bending oven.
Inventors
- 👤 Lowell E. Bitter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 07:37
CPC Classifications
B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10165; B32B17/10174; B32B17/10009; B32B17/10018; C; C03; C03B; C03B23/00; C03B23/02; C03B23/023; C03B23/025; C03B23/0252; C03B23/027; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3429; C03C17/3441
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
59 words
A method for forming a curved, electrically conductive glass member comprising: coating a flat piece of glass with an indium-tin oxide coating; applying a layer of carbonaceous material on top of said indium-tin oxide coating; bending said glass member with heat while minimizing exposure of said carbonaceous layer to oxygen, whereby crazing of said indium-tin oxide coating is minimized.
Claim 2
Independent Claim
59 words
A method for forming a curved, electrically conductive glass member comprising: coating a flat piece of glass with an indium-tin oxide coating; applying a layer of carbonaceous material on top of said indium-tin oxide coating; bending said glass member with heat while minimizing exposure of said carbonaceous layer to oxygen, whereby crazing of said indium-tin oxide coating is minimized.
Claim 3
Dependent Claim
61 words
The method of claim 1 in which said step of minimizing exposure of said carbonaceous layer to oxygen during bending is conducted by covering said carbonaceous layer with a second sheet of glass and bending said first and second sheets of glass together with heat with said indium-tin oxide and carbonaceous layers sandwiched between said first and second sheets of glass.
Claim 4
Dependent Claim
24 words
The method of claim 2 in which said carbonaceous material is applied to a density of approximately 0.6 of a gram per square foot.
Claim 5
Dependent Claim
27 words
The method of claim 3 in which said carbonaceous material is selected from the group consisting of powdered activated charcoal, powdered charcoal, powdered graphite and carbon black.
Claim 6
Dependent Claim
26 words
The method of claim 4 in which said carbonaceous material is incorporated into a paint and is applied to said indium-tin oxide layer in paint form.
Claim 7
Dependent Claim
17 words
The method of claim 4 in which said carbonaceous layer is dusted onto said indium-tin oxide layer.
Claim 8
Dependent Claim
50 words
The method of claim 4 in which said indium-tin oxide layer is applied to an initial light transmittance (T o ) of greater than about 40, said bending step being conducted without any firing of said indium-tin oxide layer in oxygen between said initial application step and said bending step.
Claim 9
Dependent Claim
45 words
The method of claim 4 in which said indium-tin oxide layer is applied on said glass to an initial light transmittance (T o ) of less than about 40; said indium-tin oxide layer being fired in an atmosphere containing oxygen prior to said bending step.
Claim 10
Dependent Claim
20 words
The method of claim 4 in which said curved, electroconductive glass member is made without using a reduction cure step.
Claim 11
Dependent Claim
50 words
The method of claim 3 in which said indium-tin oxide layer is applied to an initial light transmittance (T o ) of greater than about 40, said bending step being conducted without any firing of said indium-tin oxide layer in oxygen between said initial application step and said bending step.
Claim 12
Dependent Claim
45 words
The method of claim 3 in which said indium-tin oxide layer is applied on said glass to an initial light transmittance (T o ) of less than about 40; said indium-tin oxide layer being fired in an atmosphere containing oxygen prior to said bending step.
Claim 13
Dependent Claim
20 words
The method of claim 3 in which said curved, electroconductive glass member is made without using a reduction cure step.
Claim 14
Dependent Claim
50 words
The method of claim 2 in which said indium-tin oxide layer is applied to an initial light transmittance (T o ) of greater than about 40, said bending step being conducted without any firing of said indium-tin oxide layer in oxygen between said initial application step and said bending step.
Claim 15
Dependent Claim
45 words
The method of claim 2 in which said indium-tin oxide layer is applied on said glass to an initial light transmittance (T o ) of less than about 40; said indium-tin oxide layer being fired in an atmosphere containing oxygen prior to said bending step.
Claim 16
Dependent Claim
20 words
The method of claim 2 in which said curved, electroconductive glass member is made without using a reduction cure step.
Claim 17
Dependent Claim
50 words
The method of claim 1 in which said indium-tin oxide layer is applied to an initial light transmittance (T o ) of greater than about 40, said bending step being conducted without any firing of said indium-tin oxide layer in oxygen between said initial application step and said bending step.
Claim 18
Dependent Claim
45 words
The method of claim 1 in which said indium-tin oxide layer is applied on said glass to an initial light transmittance (T o ) of less than about 40; said indium-tin oxide layer being fired in an atmosphere containing oxygen prior to said bending step.
Claim 19
Dependent Claim
20 words
The method of claim 1 in which said curved, electroconductive glass member is made without using a reduction cure step.
References Cited (Backward Citations)
CA566773A
Cited
CA733062A
Cited
USRE25711E
Cited
US25711A
Cited
CA555403A
Cited
US1077357A
Cited
US2447379A
Cited
US2511472A
Cited
US2628927A
Cited
GB739565A
Cited
US2954454A
Cited
US2871623A
Cited
US2927042A
Cited
US3001901A
Cited
US3108019A
Cited
US3282815A
Cited
US3260584A
Cited
US3506556A
Cited
US3655545A
Cited
US4065600A
Cited
US3907660A
Cited
US4094763A
Cited
US4102768A
Cited
GB1446849A
Cited
DE2441862A1
Cited
US4102722A
Cited
US4109044A
Cited
US4119425A
Cited
JPS53118417A
Cited
US4113599A
Cited
US4202917A
Cited
US4277517A
Cited
US4201649A
Cited
DE2854213A1
Cited
US4387134A
Cited
EP0040076A2
Cited
GB2094355A
Cited
US4399015A
Cited
GB2116590A
Cited
US4414281A
Cited
US4490227A
Cited
US4503090A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-06 | 1990-10-06 | 1991-04-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-06 | 1994-10-06 | 1995-04-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-06 | 1998-10-06 | 1999-04-07 | $7700.00 | Window Closed / Lapsed |