High temperature flame and heat resistant foamed plastics
Assignee: Label Aire Inc
•
Filing: 1985-12-18
•
Granted: 1987-03-03
•
Expires: 2005-12-18
Abstract
Abstract The heat and flame resistance of foamed plastics is increased by coating the foamed plastic with an inorganic binder composition of colloidal silica, monoaluminum phosphate and aluminum chlorohydrate. The inorganic binder compositions may optionally contain an alkyl tin halide catalyst, a water soluble organic resin, an elastomer or additional inorganic additives. The inorganic binder composition may be employed in combination with dissimilar binders.
Inventors
- 👤 Stephen George
- 👤 Thomas H. George
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:24
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/34; C04B41/00; C04B41/45; C04B41/50; C04B41/5076; C04B41/5092; D; D06; D06M; D06M11/00; D06M11/07; D06M11/11; D06M11/17; D06M11/68; D06M11/70; D06M11/71; D06M11/77; D06M11/79; C04B2111/00; C04B2111/20; C04B2111/28; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249971; Y10T428/249974; Y10T428/249987; Y10T428/24999
Claims Analysis
Total Claims: 69
Claim 1
Independent Claim
62 words
A high temperature and flame resistant foamed plastic composition comprising: (a) a foamed plastic; (b) a first coating formed on the surface of the foamed plastic comprising an elastomer; and (c) a second coating of an inorganic binder composition formed on the surface of the first coating, said inorganic binder composition comprising: (i) colloidal silica, (ii) monoaluminum phosphate, and (iii) aluminum chlorohydrate.
Claim 2
Dependent Claim
62 words
A high temperature and flame resistant foamed plastic composition comprising: (a) a foamed plastic; (b) a first coating formed on the surface of the foamed plastic comprising an elastomer; and (c) a second coating of an inorganic binder composition formed on the surface of the first coating, said inorganic binder composition comprising: (i) colloidal silica, (ii) monoaluminum phosphate, and (iii) aluminum chlorohydrate.
Claim 3
Dependent Claim
36 words
A composition according to claim 1 wherein the inorganic binder composition additionally comprises an amount of an alkyl tin halide catalyst effective to increase the bonding of the inorganic binder composition when applied to a substrate.
Claim 4
Dependent Claim
15 words
A composition according to claim 2 wherein the alkyl tin halide is tri-alkyl tin chloride.
Claim 5
Dependent Claim
15 words
A composition according to claim 3 wherein the tri-alkyl tin chloride is tri-butyl tin chloride.
Claim 6
Dependent Claim
25 words
A composition according to claims 1 or 2 wherein the elastomer is a neoprene, a nitrile, a silicone or a butadiene elastomer or mixtures thereof.
Claim 7
Dependent Claim
36 words
A composition according to claims 1 or 2 wherein the inorganic binder composition additionally comprises graphite, high temperature carbon, carbon fiber, alumina silica fiber, colloidal alumina, colloidal magnesium, alumina fiber, mica, refractory oxides or mixtures thereof.
Claim 8
Dependent Claim
23 words
A composition according to claims 1 or 2 wherein the inorganic binder composition additionally comprises a water soluble organic resin or an elastomer.
Claim 9
Dependent Claim
84 words
A composition according to claim 7 wherein the water soluble organic resin is an acrylic, a styrene butadiene, a vinyl acrylic, a polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, a phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof and the elastomer is a neoprene, a nitrile, a silicone or a butadiene elastomer or mixtures thereof.
Claim 10
Dependent Claim
22 words
A composition according to claims 1 or 2 wherein the second coating additionally comprises a binder dissimilar to the inorganic binder composition.
Claim 11
Dependent Claim
16 words
A composition according to claim 9 wherein the dissimilar binder is a water soluble organic binder.
Claim 12
Dependent Claim
64 words
A composition according to claim 10 wherein the organic binder comprises an acrylic, a styrene butadiene, a vinyl acrylic, a polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof.
Claim 13
Dependent Claim
26 words
A composition according to claim 10 wherein the organic binder comprises a neoprene, a nitrile, a silicone, a urethane or a butadiene elastomer or mixtures thereof.
Claim 14
Dependent Claim
32 words
A composition according to claim 9 wherein the inorganic binder composition is about 1.0 to about 99.9% by weight of the combined weights of the inorganic binder composition and the dissimilar binder.
Claim 15
Dependent Claim
61 words
A composition according to claim 1 wherein the foamed plastic comprises polyamide-imide, polyamide, polyimidimide, polyimide, poly(vinyl-chloride), polyurethane, silicone, phenolic, polycarbonate, polyethylene, polypropylene, polystyrene, ionomer, epoxy, acrylic-butadiene-styrene, acetal or phenylene oxide-based resin foam or syntactic foam comprising: (a) hollow glass spheres, hollow carbon spheres or hollow ceramic spheres, and (b) an inorganic binder composition comprising colloidal silica, monoaluminum phosphate and aluminum chlorohydrate.
Claim 16
Dependent Claim
22 words
A composition according to claim 14 wherein the inorganic binder composition of the syntactic foam additionally comprises an alkyl tin halide catalyst.
Claim 17
Dependent Claim
46 words
A high temperature and flame resistant foamed plastic composition comprising: (a) a foamed plastic, and (b) a coating of an inorganic binder composition formed on the surface of the foamed plastic, said inorganic binder composition comprising: (i) colloidal silica, (ii) monoaluminum phosphate, and (iii) aluminum chlorohydrate.
Claim 18
Dependent Claim
46 words
A high temperature and flame resistant foamed plastic composition comprising: (a) a foamed plastic, and (b) a coating of an inorganic binder composition formed on the surface of the foamed plastic, said inorganic binder composition comprising: (i) colloidal silica, (ii) monoaluminum phosphate, and (iii) aluminum chlorohydrate.
Claim 19
Dependent Claim
36 words
A composition according to claim 16 wherein the inorganic binder composition additionally comprises an amount of an alkyl tin halide catalyst effective to increase the bonding of the inorganic binder composition when applied to a substrate.
Claim 20
Dependent Claim
15 words
A composition according to claim 17 wherein the alkyl tin halide is tri-alkyl tin chloride.
Claim 21
Dependent Claim
15 words
A composition according to claim 18 wherein the tri-alkyl tin chloride is tri-butyl tin chloride.
Claim 22
Dependent Claim
36 words
A composition according to claims 16 or 17 wherein the inorganic binder composition additionally comprises graphite, high temperature carbon, carbon fiber, alumina silica fiber, colloidal alumina, colloidal magnesium, alumina fiber, mica, refractory oxides or mixtures thereof.
Claim 23
Dependent Claim
23 words
A composition according to claims 16 or 17 wherein the inorganic binder composition additionally comprises a water soluble organic resin or an elastomer.
Claim 24
Dependent Claim
83 words
A composition according to claim 21 wherein the water soluble resin binder is an acrylic, a styrene butadiene, a vinyl acrylic, a polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, a phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof and the elastomer is a neoprene, a nitrile, a silicone, a butadiene elastomer or mixtures thereof.
Claim 25
Dependent Claim
21 words
A composition according to claims 16 or 17 wherein the coating additionally comprises a binder dissimilar to the inorganic binder composition.
Claim 26
Dependent Claim
16 words
A composition according to claim 23 wherein the dissimilar binder is a water soluble organic binder.
Claim 27
Dependent Claim
64 words
A composition according to claim 24 wherein the organic binder comprises an acrylic, a styrene butadiene, a vinyl acrylic, a polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof.
Claim 28
Dependent Claim
26 words
A composition according to claim 24 wherein the organic binder comprises a neoprene, a nitrile, a silicone, a urethane or a butadiene elastomer or mixtures thereof.
Claim 29
Dependent Claim
30 words
A composition according to claim 23 wherein the inorganic binder composition is 1.0 to 99.9% by weight of the combined weights of the inorganic binder composition and the dissimilar binder.
Claim 30
Dependent Claim
61 words
A composition according to claim 16 wherein the foamed plastic comprises polyamide-imide, polyamide, polyimidimide, polyimide, poly(vinyl-chloride), polyurethane, silicone, phenolic, polycarbonate, polyethylene, polypropylene, polystyrene, ionomer, epoxy, acrylic-butadiene-styrene, acetal or phenylene oxide-based resin foam or syntactic foam comprising: (a) hollow glass spheres, hollow carbon spheres or hollow ceramic spheres, and (b) an inorganic binder composition comprising colloidal silica, monoaluminum phosphate and aluminum chlorohydrate.
Claim 31
Dependent Claim
22 words
A composition according to claim 28 wherein the inorganic binder composition of the syntactic foam additionally comprises an alkyl tin halide catalyst.
Claim 32
Independent Claim
89 words
A method of preparing a high temperature and flame resistant foamed plastic composition comprising: (a) forming a first coating of an aqueous colloidal suspension of an elastomer on the surface of a foamed plastic; (b) forming a second coating on the surface of the first coating of an inorganic binder composition comprising: (i) colloidal silica (ii) monoaluminum phosphate, and (iii) aluminum chlorohydrate; and (c) heating the coated foamed plastic for a period of time and under heating conditions effective to provide the foamed plastic with a dry coated surface.
Claim 33
Independent Claim
89 words
A method of preparing a high temperature and flame resistant foamed plastic composition comprising: (a) forming a first coating of an aqueous colloidal suspension of an elastomer on the surface of a foamed plastic; (b) forming a second coating on the surface of the first coating of an inorganic binder composition comprising: (i) colloidal silica (ii) monoaluminum phosphate, and (iii) aluminum chlorohydrate; and (c) heating the coated foamed plastic for a period of time and under heating conditions effective to provide the foamed plastic with a dry coated surface.
Claim 34
Dependent Claim
16 words
A method according to claim 30 wherein the second coating additionally comprises an alkyl tin halide.
Claim 35
Dependent Claim
15 words
A method according to claim 31 wherein the alkyl tin halide is tri-butyl tin chloride.
Claim 36
Independent Claim
24 words
A method according to claims 30 or 31 wherein the elastomer is a neoprene, a nitrile, a silicone, a butadiene elastomer or mixtures thereof.
Claim 37
Independent Claim
36 words
A method according to claims 30 or 31 wherein the inorganic binder composition additionally comprises graphite, high temperature carbon, carbon fiber, alumina silica fiber, colloidal alumina, colloidal magnesium, alumina fiber, mica, refractory oxides or mixtures thereof.
Claim 38
Independent Claim
23 words
A method according to claims 30 or 31 wherein the inorganic binder composition additionally comprises a water soluble resin binder or an elastomer.
Claim 39
Dependent Claim
83 words
A method according to claim 35 wherein the water soluble resin binder is an acrylic, a styrene butadiene, a vinyl acrylic, a polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, a phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof and the elastomer is a neoprene, a nitrile, a silicone, a butadiene elastomer or mixtures thereof.
Claim 40
Independent Claim
22 words
A method according to claims 30 or 31 wherein the second coating additionally comprises a binder dissimilar to the inorganic binder composition.
Claim 41
Dependent Claim
16 words
A method according to claim 37 wherein the dissimilar binder is a water soluble organic binder.
Claim 42
Dependent Claim
65 words
A method according to claim 38 wherein the organic binder comprises an acrylic, a styrene butadiene, a vinyl acrylic, a polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, a phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof.
Claim 43
Dependent Claim
26 words
A method according to claim 38 wherein the organic binder comprises a neoprene, a nitrile, a silicone, a urethane or a butadiene elastomer or mixtures thereof.
Claim 44
Dependent Claim
32 words
A method according to claim 37 wherein the inorganic binder composition is about 1.0 to about 99.9% by weight of the combined weights of the inorganic binder composition and the dissimilar binder.
Claim 45
Dependent Claim
61 words
A method according to claim 30 wherein the foamed plastic comprises polyamide-imide, polyamide, polyimidimide, polyimide, poly(vinyl-chloride), polyurethane, silicone, phenolic, polycarbonate, polyethylene, polypropylene, polystyrene, ionomer, epoxy, acrylic-butadiene-styrene, acetal or phenylene oxide-based resin foam or syntactic foam comprising: (a) hollow glass spheres, hollow carbon spheres or hollow ceramic spheres, and (b) an inorganic binder composition comprising colloidal silica, monoaluminum phosphate and aluminum chlorohydrate.
Claim 46
Dependent Claim
22 words
A method according to claim 42 wherein the inorganic binder composition of the syntactic foam additionally comprises an alkyl tin halide catalyst.
Claim 47
Independent Claim
68 words
A method of preparing a high temperature and flame resistant foamed plastic composition comprising: (a) forming a coating on the surface of a foamed plastic of an inorganic binder composition comprising: (i) colloidal silica, (ii) monoaluminum phosphate, and (iii) aluminum chlorohydrate; and (b) heating the coated foamed plastic for a period of time and under heating conditions effective to provide the foamed plastic with a dry coated surface.
Claim 48
Independent Claim
68 words
A method of preparing a high temperature and flame resistant foamed plastic composition comprising: (a) forming a coating on the surface of a foamed plastic of an inorganic binder composition comprising: (i) colloidal silica, (ii) monoaluminum phosphate, and (iii) aluminum chlorohydrate; and (b) heating the coated foamed plastic for a period of time and under heating conditions effective to provide the foamed plastic with a dry coated surface.
Claim 49
Dependent Claim
15 words
A method according to claim 44 wherein the coating additionally comprises an alkyl tin halide.
Claim 50
Dependent Claim
15 words
A method according to claim 45 wherein the alkyl tin halide is tri-butyl tin chloride.
Claim 51
Independent Claim
36 words
A method according to claims 44 or 45 wherein the inorganic binder composition additionally comprises graphite, high temperature carbon, carbon fiber, alumina silica fiber, colloidal alumina, colloidal magnesium, alumina fiber, mica, refractory oxides or mixtures thereof.
Claim 52
Independent Claim
23 words
A method according to claims 44 or 45 wherein the inorganic binder composition additionally comprises a water soluble resin binder or an elastomer.
Claim 53
Dependent Claim
83 words
A method according to claim 48 wherein the water soluble resin binder is an acrylic, a styrene butadiene, a vinyl acrylic, a polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, a phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof and the elastomer is a neoprene, a nitrile, a silicone, a butadiene elastomer or mixtures thereof.
Claim 54
Independent Claim
21 words
A method according to claims 44 or 45 wherein the coating additionally comprises a binder dissimilar to the inorganic binder composition.
Claim 55
Dependent Claim
16 words
A method according to claim 50 wherein the dissimilar binder is a water soluble organic binder.
Claim 56
Dependent Claim
65 words
A method according to claim 51 wherein the organic binder comprises an acrylic, a styrene butadiene, a vinyl acrylic, a polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, a phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof.
Claim 57
Dependent Claim
26 words
A method according to claim 51 wherein the organic binder comprises a neoprene, a nitrile, a silicone, a urethane or a butadiene elastomer or mixtures thereof.
Claim 58
Dependent Claim
30 words
A method according to claim 50 wherein the inorganic binder composition is 1.0 to 99.9% by weight of the combined weights of the inorganic binder composition and the dissimilar binder.
Claim 59
Dependent Claim
61 words
A method according to claim 44 wherein the foamed plastic comprises polyamide-imide, polyamide, polyimidimide, polyimide, poly(vinyl-chloride), polyurethane, silicone, phenolic, polycarbonate, polyethylene, polypropylene, polystyrene, ionomer, epoxy, acrylic-butadiene-styrene, acetal or phenylene oxide-based resin foam or syntactic foam comprising: (a) hollow glass spheres, hollow carbon spheres or hollow ceramic spheres, and (b) an inorganic binder composition comprising colloidal silica, monoaluminum phosphate and aluminum chlorohydrate.
Claim 60
Dependent Claim
22 words
A method according to claim 55 wherein the inorganic binder composition of the syntactic foam additionally comprises an alkyl tin halide catalyst.
Claim 61
Dependent Claim
55 words
A binder composition comprising: (a) about 1.0 to about 99.9 wt. % of an inorganic binder composition comprising: (i) colloidal silica, (ii) monoaluminum phosphate, (iii) aluminum chlorohydrate, and (iv) water; and (b) about 99 to about 0.1 wt. % of a dissimilar binder and water, said dissimilar binder being compatible with the inorganic binder composition.
Claim 62
Dependent Claim
55 words
A binder composition comprising: (a) about 1.0 to about 99.9 wt. % of an inorganic binder composition comprising: (i) colloidal silica, (ii) monoaluminum phosphate, (iii) aluminum chlorohydrate, and (iv) water; and (b) about 99 to about 0.1 wt. % of a dissimilar binder and water, said dissimilar binder being compatible with the inorganic binder composition.
Claim 63
Dependent Claim
36 words
A composition according to claim 57 wherein the inorganic binder composition additionally comprises an amount of an alkyl tin halide catalyst effective to increase the bonding of the inorganic binder composition when applied to a substrate.
Claim 64
Dependent Claim
15 words
A composition according to claim 58 wherein the alkyl tin halide is tri-alkyl tin chloride.
Claim 65
Dependent Claim
15 words
A composition according to claim 59 wherein the tri-alkyl tin chloride is tri-butyl tin chloride.
Claim 66
Dependent Claim
18 words
A composition according to claims 57 or 58 wherein the dissimilar binder is a water soluble organic binder.
Claim 67
Dependent Claim
64 words
A composition according to claim 61 wherein the organic binder comprises an acrylic, a styrene butadiene, a vinyl acrylic, polyvinyl chloride, a polyvinylidene chloride, a vinyl acetate, a styrene, a styrene acrylic, a polyvinyl alcohol, a polyurethane, a silicone polyester, a polyamide, a polyimide, a polyamide-imide, an alkyl, a phenolic, a urea formaldehyde, an epoxy, a fluorocarbon or a polysulfone resin or mixtures thereof.
Claim 68
Dependent Claim
25 words
A composition according to claim 61 wherein the organic binder comprises a neoprene, a nitrile, silicone, a urethane or a butadiene elastomer or mixtures thereof.
Claim 69
Dependent Claim
36 words
A composition according to claims 57 or 58 wherein the inorganic binder composition additionally comprises graphite, high temperature carbon, carbon fiber, alumina silica fiber, colloidal alumina, colloidal magnesium, alumina fiber, mica, refractory oxides or mixtures thereof.
References Cited (Backward Citations)
US4357387A
Cited
US4358500A
Cited
US4375493A
Cited
US4396661A
Cited
US4428999A
Cited
US4507355A
Cited
US4563219A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-02 | 1990-09-01 | 1991-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-02 | 1994-09-01 | 1995-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-02 | 1998-09-01 | 1999-03-03 | $7700.00 | Window Closed / Lapsed |