Coating film by ion plating
Assignee: Citizen Watch Co Ltd
•
Filing: 1985-09-30
•
Granted: 1987-02-17
•
Expires: 2005-09-30
Abstract
Abstract A protective and decorative coating film of a beautiful black color which is composed of a mixture of titanium nitride and titanium carbide can be deposited on the surface of various metallic articles of personal ornament use such as watch cases by the techniques of ion plating in which the gaseous atmosphere of low pressure contains argon, nitrogen and an aliphatic hydrocarbon compound such as ethylene in a limited proportion. It is disclosed that the adhesion strength of the coating film to the substrate surface is largely influenced by the oxygen content in the coating film so that it is preferable to decrease the content of oxygen in the atmosphere to such an extent that the oxygen content in the thus formed coating film does not exceed 40% in the atomic ratio.
Inventors
- 👤 Ryo Kurakata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 06:07
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/006; C23C14/00; C23C14/0015; C23C14/06; C23C14/0664; C23C16/22; C23C16/30; C23C16/36
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
186 words
A metal-made article coated with a coating film composed of titanium nitride and titanium carbide in such a proportion that the atomc ratios of titanium, nitrogen and carbon are in the ranges of from 15 to 40%, from 10 to 25% and from 40 to 65%, respectively, and wherein the coating film contains oxygen in an atomic ratio of oxygen to titanium not exceeding 40%; the coating film being formed by a method of ion plating comprising the steps of: (a) holding the metallic substrate article to face an evaporation source of titanium metal in an atmosphere of a gaseous mixture comprising argon, nitrogen and an aliphatic hydrocarbon compound under a pressure in the range from 8×10 -4 to 5×10 -3 Torr; (b) impressing a direct current voltage in the range from 20 to 200 volts between the evaporation source of titanium metal and the metallic substrate article; and (c) heating the titanium metal in the evaporation source to be evaported in the form of metallic ions which deposit on the surface of the metallic substrate article as a mixture of titanium nitride and titanium carbide.
Claim 2
Dependent Claim
186 words
A metal-made article coated with a coating film composed of titanium nitride and titanium carbide in such a proportion that the atomc ratios of titanium, nitrogen and carbon are in the ranges of from 15 to 40%, from 10 to 25% and from 40 to 65%, respectively, and wherein the coating film contains oxygen in an atomic ratio of oxygen to titanium not exceeding 40%; the coating film being formed by a method of ion plating comprising the steps of: (a) holding the metallic substrate article to face an evaporation source of titanium metal in an atmosphere of a gaseous mixture comprising argon, nitrogen and an aliphatic hydrocarbon compound under a pressure in the range from 8×10 -4 to 5×10 -3 Torr; (b) impressing a direct current voltage in the range from 20 to 200 volts between the evaporation source of titanium metal and the metallic substrate article; and (c) heating the titanium metal in the evaporation source to be evaported in the form of metallic ions which deposit on the surface of the metallic substrate article as a mixture of titanium nitride and titanium carbide.
Claim 3
Dependent Claim
40 words
The metal-made article coated with a coating film composed of titanium nitride and titanium carbide as claimed in claim 1 wherein the coating film contains oxygen in an atomic ratio of oxygen to titanium from about 2 to about 40%.
References Cited (Backward Citations)
US4480010A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-16 | 1990-08-18 | 1991-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-16 | 1994-08-18 | 1995-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-16 | 1998-08-18 | 1999-02-17 | $7700.00 | Window Closed / Lapsed |