Abstract
Abstract By use of an ion plating apparatus having an ionizing means which can be operated independently of the electric potential of a substrate, at the initial and final stages of the process of ion plating, a negative potential relative to that of a vapor source is applied to the substrate in order to facilitate the bombardment effect and at the intermediate stage of the process, the potential of the substrate is left floating while the ionization means is being driven in order to control the bombardment effect. In a preferred example, the apparatus has thermoelectron emitting filaments located near the substrate and a pair of anodes located on the side of the vapor source with respect to the substrate and on the opposite side of the substrate. This process permits producing relatively thick and adherent coatings.
Inventors
- 👤 Yasutomo Sasanuma
- 👤 Masao Koshi
- 👤 Teruaki Takahashi
- 👤 Shotaro Shimizu
- 👤 Mitsugu Enomoto
- 👤 Youji Yoshikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 09:26
CPC Classifications
H; H01; H01J; H01J37/00; H01J37/32; H01J37/32009; H01J37/32422; C; C23; C23C; C23C14/00; C23C14/22; C23C14/24; C23C14/32; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
230 words
A method for coating materials by ion plating comprising the steps of: providing an ion plating apparatus comprising: a vapor source at ground potential; a substrate holder located above said vapor source; a pair of anodes located on the side of said vapor source with respect to said substrate holder and the opposite side of said substrate holder; one or more thermoelectron emitting filaments located between said anodes; a vacuum chamber for accomodating said elements, said vacuum chamber having a gas inlet and an evacuation system; means for applying a negative potential relative to that of said vapor source to a substrate supported by said substrate holder; and means for removing said negative potential to leave the potential of said substrate floating; at an initial stage, ionizing a gas introduced from said gas inlet and a vapor of an evaporation material from said vapor source, and ion plating a surface of said substrate with a film of said evaporation material or a compound of said evaporation material and said introduced gas, said substrate being cathodically biased relative to said vapor source; at an intermediate stage, while driving said ionizing means, continuing ion plating with the potential of said substrate left floating; and at a final stage, while driving said ionizing means, continuing ion plating with the potential of said substrate again made negative relative to that of said vapor source.
Claim 2
Independent Claim
230 words
A method for coating materials by ion plating comprising the steps of: providing an ion plating apparatus comprising: a vapor source at ground potential; a substrate holder located above said vapor source; a pair of anodes located on the side of said vapor source with respect to said substrate holder and the opposite side of said substrate holder; one or more thermoelectron emitting filaments located between said anodes; a vacuum chamber for accomodating said elements, said vacuum chamber having a gas inlet and an evacuation system; means for applying a negative potential relative to that of said vapor source to a substrate supported by said substrate holder; and means for removing said negative potential to leave the potential of said substrate floating; at an initial stage, ionizing a gas introduced from said gas inlet and a vapor of an evaporation material from said vapor source, and ion plating a surface of said substrate with a film of said evaporation material or a compound of said evaporation material and said introduced gas, said substrate being cathodically biased relative to said vapor source; at an intermediate stage, while driving said ionizing means, continuing ion plating with the potential of said substrate left floating; and at a final stage, while driving said ionizing means, continuing ion plating with the potential of said substrate again made negative relative to that of said vapor source.
Claim 3
Dependent Claim
25 words
A method for coating materials by ion plating according to claim 1 wherein said film comprises a hard material apt to accumulate a residual stress.
Claim 4
Dependent Claim
19 words
A method for coating materials by ion plating according to claim 2 wherein said hard material is titanium nitride.
Claim 5
Dependent Claim
19 words
A method for coating materials by ion plating according to claim 2 wherein said hard material is titanium carbonitride.
Claim 6
Dependent Claim
18 words
A method for coating materials by ion plating according to claim 2 wherein said hard material is chromium.
Claim 7
Independent Claim
269 words
A method for coating materials by ion plating comprising the steps of: providing an ion plating appartus an ionizing means operated independently of a potential of comprising: a vapor source at ground potential; a substrate holder located above said vapor source; a pair of anodes located on the side of said vapor source with respect to said substrate holder and the opposite side of said substrate holder; one or more thermoelectron emitting filaments located between said anodes; a vacuum chamber for accommodating said elements, said vacuum chamber having a gas inlet and an evacuation system; means for applying a negative potential relative to that of said vapor source to a substrate supported by said substrate holder; and means for removing said negative potential to leave the potential of said substrate floating; at an initial stage, ionizing a gas introduced from said gas inlet and a vapor of an evaporation material from said vapor source, and ion plating a surface of said substrate with a film of said evaporation material or a compound of said evaporation material and said introduced gas, said substrate being cathodically biased relative to that of said vapor source; at an intermediate stage, while driving said ionizing means, repeating alternately the ion plating step with the potential of said substrate left floating and the ion plating step with the potential of said substrate made negative relative to that of said vapor source so as to stack films; and at a final stage, while driving said ionizing means, continuing ion plating with the potential of said substrate again made negative relative to that of said vapor source.
Claim 8
Independent Claim
269 words
A method for coating materials by ion plating comprising the steps of: providing an ion plating appartus an ionizing means operated independently of a potential of comprising: a vapor source at ground potential; a substrate holder located above said vapor source; a pair of anodes located on the side of said vapor source with respect to said substrate holder and the opposite side of said substrate holder; one or more thermoelectron emitting filaments located between said anodes; a vacuum chamber for accommodating said elements, said vacuum chamber having a gas inlet and an evacuation system; means for applying a negative potential relative to that of said vapor source to a substrate supported by said substrate holder; and means for removing said negative potential to leave the potential of said substrate floating; at an initial stage, ionizing a gas introduced from said gas inlet and a vapor of an evaporation material from said vapor source, and ion plating a surface of said substrate with a film of said evaporation material or a compound of said evaporation material and said introduced gas, said substrate being cathodically biased relative to that of said vapor source; at an intermediate stage, while driving said ionizing means, repeating alternately the ion plating step with the potential of said substrate left floating and the ion plating step with the potential of said substrate made negative relative to that of said vapor source so as to stack films; and at a final stage, while driving said ionizing means, continuing ion plating with the potential of said substrate again made negative relative to that of said vapor source.
Claim 9
Dependent Claim
25 words
A method for coating materials by ion plating according to claim 6 wherein said film comprises a hard material apt to accumulate a residual stress.
Claim 10
Dependent Claim
19 words
A method for coating materials by ion plating according to claim 7 wherein said hard material is titanium nitride.
Claim 11
Dependent Claim
19 words
A method for coating materials by ion plating according to claim 7 wherein said hard material is titanium carbonitride.
Claim 12
Dependent Claim
18 words
A method for coating materials by ion plating according to claim 7 wherein said hard material is chromium.
Claim 13
Dependent Claim
10 words
A coated substrate made by the method of claim 1.
References Cited (Backward Citations)
US4152478A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |