Hard alloy containing molybdenum
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1985-12-13
•
Granted: 1987-01-27
•
Expires: 2005-12-13
Abstract
Abstract This invention relates to a hard alloy comprising two phases: a hard phase consisting of at least one compound having a crystal structure of simple hexagonal MC type (M: metal; C: carbon) selected from the group consisting of mixed carbides, carbonitrides and carboxynitrides of molybdenum and tungsten, and a binder phase consisting of at least one element selected from the group consisting of iron, cobalt and nickel. The hard phase is prepared by carburizing an (Mo, W) alloy obtained by reducing oxides of molybdenum and tungsten with a particle size of at most 1 micron, is composed of coarse particles with a mean particle size of at least 3 microns, and has a uniform molybdenum to tungsten ratio in the particles. The hard alloy has a gross composition within the range of the shaded portion ABCDEA in FIG. 1.
Inventors
- 👤 Mitsuo Kodama
- 👤 Masaya Miyake
- 👤 Minol Nakano
- 👤 Tsuyoshi Asai
- 👤 Akio Hara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:56
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/04; C22C1/05; C22C1/051; C01; C01B; C01B32/00; C01B32/90; C01B32/907; C01B32/914; C01B32/949; C22C29/00; C22C29/02; C01P; C01P2004/00; C01P2004/80; C01P2006/00; C01P2006/10; C01P2006/80; C01P2006/90
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
219 words
A process for preparing a hard alloy having a gross composition within the range of the shaded portion ABCDEA in FIG. 1, comprising the following two phases: (1) a hard phase comprising at least one compound having a simple hexagonal MC type crystal structure selected from the group consisting of mixed carbides, carbonitrides and carboxynitrides of molybdenum and tungsten, and (2) a binder phase comprising at least one element selected from the group consisting of iron, cobalt, and nickel, which process comprises reducing a mixture of oxides of molydenum and tungsten having a particle size of at most 1 micron to produce an (Mo,W) alloy; heat treating said (Mo,W) alloy at a temperature of 1100° to 1400° C. in a stream of nitrogen or hydrogen; carburizing the heat-treated alloy at a controlled temperature which is as high as possible but lower than the decomposition temperature of (Mo,W)C into (Mo,W) 2 C, to produce said hard phase composed of coarse particles having a mean particle size of at least 3 microns and having a uniform molybdenum to tungsten ratio in said coarse particles; mixing said hard phase with said binder phase; and sintering the resultant mixture to produce said hard alloy, said process being conducted in a manner to hold the quantity of M 2 C precipitated to a minimum.
Claim 2
Dependent Claim
219 words
A process for preparing a hard alloy having a gross composition within the range of the shaded portion ABCDEA in FIG. 1, comprising the following two phases: (1) a hard phase comprising at least one compound having a simple hexagonal MC type crystal structure selected from the group consisting of mixed carbides, carbonitrides and carboxynitrides of molybdenum and tungsten, and (2) a binder phase comprising at least one element selected from the group consisting of iron, cobalt, and nickel, which process comprises reducing a mixture of oxides of molydenum and tungsten having a particle size of at most 1 micron to produce an (Mo,W) alloy; heat treating said (Mo,W) alloy at a temperature of 1100° to 1400° C. in a stream of nitrogen or hydrogen; carburizing the heat-treated alloy at a controlled temperature which is as high as possible but lower than the decomposition temperature of (Mo,W)C into (Mo,W) 2 C, to produce said hard phase composed of coarse particles having a mean particle size of at least 3 microns and having a uniform molybdenum to tungsten ratio in said coarse particles; mixing said hard phase with said binder phase; and sintering the resultant mixture to produce said hard alloy, said process being conducted in a manner to hold the quantity of M 2 C precipitated to a minimum.
Claim 3
Dependent Claim
42 words
The process of claim 1, wherein a part of the compound of crystal structure is replaced by at least one hard B1 type compound selected from the group consisting of compounds containing Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, and W.
Claim 4
Dependent Claim
19 words
The process of claim 2, wherein the quantity of the B1 type compound is at most 30% by weight.
Claim 5
Dependent Claim
21 words
The process of claim 1, wherein at least one of the mixed carbides is a solid solution of (Mo, W, Cr)C.
Claim 6
Dependent Claim
16 words
The process of claim 4, wherein the quantity of Cr is 0.3 to 10% by weight.
Claim 7
Dependent Claim
28 words
The process of claim 1, wherein a part of the carbon in the carbides forming the hard phases is replaced by at least one of nitrogen and oxygen.
Claim 8
Dependent Claim
25 words
The process of claim 6, wherein the quantities of nitrogen and oxygen are defined, in connection with the alloy composition, by the relationship of: ##EQU6##
Claim 9
Dependent Claim
31 words
The process of claim 1, wherein at least one element selected from the group consisting of Be, Mg, Ca, B, Si, P, Mn, Fe and Re is incorporated in the alloy.
Claim 10
Dependent Claim
22 words
The process of claim 1, wherein the hard phase comprises two or three simple hexagonal phases differing in the ratio of Mo/W.
Claim 11
Dependent Claim
22 words
The process of claim 1, wherein the mean particle size of the particles in the hard phase is at least 4 microns.
Claim 12
Dependent Claim
22 words
The process of claim 1, wherein the mean particle size of the particles in the hard phase is at least 5 microns.
Claim 13
Dependent Claim
34 words
The process of claim 1, wherein at least one element selected from the group consising of Mn, Re, Cu, Ag, Zn, and Au is incorporated in the binder phase to make the alloy non-magnetic.
References Cited (Backward Citations)
GB635221A
Cited
US4049876A
Cited
US4049380A
Cited
US4066451A
Cited
US4212671A
Cited
GB1593326A
Cited
US4216009A
Cited
WO1979000089A1
Cited
GB2011949A
Cited
US4265662A
Cited
GB2015572A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-26 | 1990-07-28 | 1991-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-26 | 1994-07-28 | 1995-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-26 | 1998-07-28 | 1999-01-27 | $7700.00 | Window Closed / Lapsed |