Carbide compositions for wear-resistant facings and method of fabrication
Assignee: Individual
•
Filing: 1976-02-17
•
Granted: 1978-01-03
•
Expires: 1996-02-17
Abstract
Abstract Refractory, hard carbide alloys, intended primarily as replacement for the cast eutectic WC + W 2 C tungsten carbides currently used as hard components in wear-resistant facings, consist of fine-grained and hard two-phase mixtures of subcarbide, (Mo,W) 2 C, and hexagonal monocarbide (Mo,W)C, solid solutions, and are formed by solid state decomposition of the pseudocubic, η-(Mo,W) 3 C 2 , or cubic α-(Mo,W)C 1-x solid solutions. The carbide alloys of the invention can be combined with low-melting metal binders to form cemented carbide alloys of at least equivalent wear-resistance to alloys using the eutectic tungsten carbides.
Inventors
- 👤 Erwin Rudy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:39
CPC Classifications
C; C22; C22C; C22C29/00; C22C29/02; C22C29/06
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
180 words
A metal carbide composition (Mo x W.sub. x' Cr.sub. x")C z , in which the relative mole fractions x, x', x" (x + X' + x" = 1) of the metal components assume values of at least 0.20 for x, between 0 and 0.80 for x', and between 0 and 0.18 for x" when x is less than about 0.80 and is 0 when x is greater than about 0.80, and the value of the stoichiometry parameter z, which stands for the number of gramatoms carbon present per gramatom of the metal component in the carbide alloy, lies between 0.60 and 0.73, said metal carbide composition being a two-phase mixture consisting of metal subcarbide, M 2 C and hexagonal monocarbide, MC, solid solution, wherein M represents the metal component, the average spacing between the grains of said subcarbide and said monocarbide phases in the mixture being less than 4 microns, and said two-phased mixture being formed by solid state decomposition of the pseudocubic η -M 3 C 2 , or cubic α -MC 1-x , high temperature carbide solid solutions.
Claim 2
Dependent Claim
180 words
A metal carbide composition (Mo x W.sub. x' Cr.sub. x")C z , in which the relative mole fractions x, x', x" (x + X' + x" = 1) of the metal components assume values of at least 0.20 for x, between 0 and 0.80 for x', and between 0 and 0.18 for x" when x is less than about 0.80 and is 0 when x is greater than about 0.80, and the value of the stoichiometry parameter z, which stands for the number of gramatoms carbon present per gramatom of the metal component in the carbide alloy, lies between 0.60 and 0.73, said metal carbide composition being a two-phase mixture consisting of metal subcarbide, M 2 C and hexagonal monocarbide, MC, solid solution, wherein M represents the metal component, the average spacing between the grains of said subcarbide and said monocarbide phases in the mixture being less than 4 microns, and said two-phased mixture being formed by solid state decomposition of the pseudocubic η -M 3 C 2 , or cubic α -MC 1-x , high temperature carbide solid solutions.
Claim 3
Dependent Claim
40 words
A cemented carbide composition comprising a carbide component according to claim 1, and a low-melting metal binder in which the combined contents of the elements copper, silver, nickel, manganese, and zinc comprise more than 80 atomic percent of said binder.
Claim 4
Dependent Claim
29 words
A wear-resistant composite in which the cemented carbide according to claim 2 is affixed to a metallic substrate for the purpose of increasing the wear life of the substrate.
Claim 5
Dependent Claim
21 words
A cemented carbide-diamond composite, in which the cemented carbide according to claim 2 contains up to about 40 volume percent diamonds.
Claim 6
Dependent Claim
29 words
A wear-resistant composite in which the cemented carbide according to claim 4 is affixed to a metallic substrate for the purpose of increasing the wear life of the substrate.
Claim 7
Dependent Claim
17 words
A welding electrode comprising the metal carbide composition of claim 1 combined with a ferrous metal alloy.
References Cited (Backward Citations)
GB890757A
Cited
US3479155A
Cited
US3677722A
Cited
GB1326769A
Cited
US3842581A
Cited
US3840367A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-02 | 1981-07-04 | 1982-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-02 | 1985-07-04 | 1986-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-02 | 1989-07-04 | 1990-01-03 | $7700.00 | Window Closed / Lapsed |