Nickel/indium alloy for use in the manufacture of electrical contact areas electrical devices
Assignee: Honeywell International Inc
•
Filing: 1985-03-26
•
Granted: 1986-12-30
•
Expires: 2005-03-26
Abstract
Abstract This invention relates to electrical devices in which the electrical contact areas are plated with a nickel/indium alloy comprising 0.1-9 percent indium, balance nickel. The nickel/indium alloy layer may be coated with a precious metal such as gold.
Inventors
- 👤 George J. Samuels
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:54
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/02; H05K3/06; H05K3/061; H05K3/062; C; C22; C22C; C22C19/00; C22C19/03; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/562; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0338; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12681; Y10T428/12771; Y10T428/12861; Y10T428/12889; Y10T428/12944
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
127 words
An improved electrical device having improved electrical contact areas, said device of the type having one or more insulating positions and one or more electrical conductive portions, said contact areas in electrical connection with one or more of said conductive portions and adapted to engage and form mating surfaces with one or more electrical contact areas of one or more other electrical devices to provide electrical connection between said one or more conductive portions of said device, and said other devices, the improvement comprising electrical contact areas electroplated with a nickel/indium alloy consisting essentially of from about 0.1 to about 9 weight percent indium based on the total weight of the alloy and from about 99.9 to about 91 percent by weight nickel on the aforementioned basis.
Claim 2
Dependent Claim
127 words
An improved electrical device having improved electrical contact areas, said device of the type having one or more insulating positions and one or more electrical conductive portions, said contact areas in electrical connection with one or more of said conductive portions and adapted to engage and form mating surfaces with one or more electrical contact areas of one or more other electrical devices to provide electrical connection between said one or more conductive portions of said device, and said other devices, the improvement comprising electrical contact areas electroplated with a nickel/indium alloy consisting essentially of from about 0.1 to about 9 weight percent indium based on the total weight of the alloy and from about 99.9 to about 91 percent by weight nickel on the aforementioned basis.
Claim 3
Dependent Claim
91 words
A device according to claim 1 wherein said alloy is electrodeposited from an aqueous bath having a pH equal to or less than about 5, said bath which comprises: (a) at least about 0.5 M nickel cations and at least about 0.001 M indium cations; (b) up to about 2.6 M chloride ions; (c) a buffer material in an amount sufficient to maintain the pH of the bath at a value equal to or less than about 5; (d) an effective amount of one or more chelating agents; and (e) water.
Claim 4
Dependent Claim
80 words
A device according to claim 2 wherein said aqueous plating bath comprises: (a) from about 0.9 M to about 2 M of nickel cations; (b) from about 0.04 M to about 2.5 M chloride ions; (c) from about 0.004 M to about 0.05 M of indium sulfamate; (d) from about 0.25 to about 1.6 M of one or more chelating agents selected from the group consisting of hydroxycarboxylic acids, carboxylic acids and aminocarboxylic acids and salts thereof; and (e) water.
Claim 5
Dependent Claim
16 words
A device according to claim 3 wherein said pH is from about 1.7 to about 3.2.
Claim 6
Dependent Claim
33 words
A device according to claim 2 wherein said nickel and indium cation are derived totally or in part from water-soluble nickel and indium salts of sulfamic acid, carboxylic acids, hydroxycarboxylic or aminocarboxylic acids.
Claim 7
Dependent Claim
19 words
A device according to claim 5 wherein said nickel and indium cations are derived from salts of sulfamic acid.
Claim 8
Dependent Claim
18 words
A device according to claim 6 wherein said chloride ions are derived from nickel chloride or indium chloride.
Claim 9
Dependent Claim
15 words
A device according to claim 7 wherein said chloride ions are derived from nickel chloride.
Claim 10
Dependent Claim
24 words
A device according to claim 2 wherein said chelating agents are selected from the group consisting of dicarboxylic acids, hydroxycarboxylic acids and salts thereof.
Claim 11
Dependent Claim
22 words
A device according to claim 9 wherein said chelating agents are selected from the group consisting of hydroxycarboxylic acids and salts thereof.
Claim 12
Dependent Claim
19 words
A device according to claim 10 wherein said chelating agents are citric acid, malic acid or a salt thereof.
Claim 13
Dependent Claim
30 words
A device according to claim 11 wherein said chelating agents are citric acid and the amount of citric acid in said bath is from about 0.2 M to 1.3 M.
Claim 14
Dependent Claim
23 words
A device according to claim 12 wherein the amount of citric acid in said bath is from about 0.25 M out 0.7 M.
Claim 15
Dependent Claim
14 words
A device according to claim 9 wherein said chelating agents is a carboxylic acid.
Claim 16
Dependent Claim
16 words
A device according to claim 14 wherein said chelating agent is malonic acid or tartaric acid.
Claim 17
Dependent Claim
32 words
A device according to claim 1 which further comprises a material comprising preponderantly a precious metal electroplated onto all or a part of said nickel/indium alloy plated onto said electrical contact area.
Claim 18
Dependent Claim
22 words
A device according to claim 16 wherein said precious metal is selected from the group consisting of gold and gold based alloys.
Claim 19
Dependent Claim
24 words
A device according to claim 16 wherein said thickness of the nickel/indium alloy plated onto said contact area is at least about 0.5 microns.
Claim 20
Dependent Claim
25 words
A device according to claim 1 wherein the thickness of the nickel/indium alloy plated onto said electrical contact area is at least about 1.0 microns.
Claim 21
Dependent Claim
19 words
A device according to claim 19 wherein the thickness of the nickel/indium alloy is at least about 2.5 microns.
Claim 22
Dependent Claim
27 words
A device according to claim 1 wherein the weight percent indium is not greater than 8 weight percent indium based on the total weight of the alloy.
Claim 23
Dependent Claim
32 words
A device according to claim 21 wherein the weight percent indium in said alloy is from about 3.2 to about 5.3 weight percent indium based on the total weight of the alloy.
Claim 24
Dependent Claim
40 words
A device according to claim 22 wherein the weight percent indium in said alloy is from about 4.3 to about 5.3 weight percent indium based on the total weight of the alloy and from about 95.7% to about 94.7% nickel.
Claim 25
Dependent Claim
32 words
A device according to claim 23 wherein the weight percent indium in said alloy is from about 3 to about 7 weight percent indium based on the total weight of the alloy.
Claim 26
Dependent Claim
23 words
A device according to claim 1 wherein said device is adapted to engage and form mating surfaces, and disengage from said mating relationship.
References Cited (Backward Citations)
SU201871A1
Cited
CA449849A
Cited
GB602879A
Cited
US2890314A
Cited
SU145102A1
Cited
CH527911A
Cited
US3857683A
Cited
DE2401342A1
Cited
US4111690A
Cited
JPS53101686A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-29 | 1990-06-30 | 1990-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-29 | 1994-06-30 | 1994-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-29 | 1998-06-30 | 1998-12-30 | $7700.00 | Window Closed / Lapsed |