Method for removal of carbonaceous residues from ceramic structures having internal metallurgy
Assignee: International Business Machines Corp
•
Filing: 1985-08-02
•
Granted: 1986-12-09
•
Expires: 2005-08-02
Abstract
Abstract A process for removing organic materials from an article formed from a slurry of glass and/or ceramic particles, resin binder, and a solvent for the resin binder, the process involving including in the slurry a particulate catalyst selected from the group consisting of Cu, Cu2O, CuO, Cu2SO4, CuCl2, Cu organometallic compounds, and mixtures thereof, the catalyst promoting a rapid and complete removal from the shaped article when heated of the organic materials of the slurry.
Inventors
- 👤 Lester W. Herron
- 👤 Ananda H. Kumar
- 👤 Raj N. Master
- 👤 Robert W. Nufer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:10
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/01; H10W70/05; C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/638; C04B35/64; H10W99/00; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49126; Y10T29/49155; Y10T29/49163; Y10T29/49165
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
179 words
In a method of forming a glass-ceramic composite substrate wherein a slurry is prepared which includes sinterable particles of a crystallizable glass, an organic resin binder, and a solvent for the binder, forming the slurry into green ceramic sheets, forming via holes in the sheets, depositing electrically conductive material in the via holes and in line patterns on the surface of the sheets, assembling the sheets, and heating the assembly in an environment to oxidize and remove the resin binder, and subsequently heating the assembly at a higher temperature to fuse the glass particles, the improvement comprising, incorporating a catalyst to accelerate the binder oxidation of said slurry and eliminate carbonaceous binder residue, said catalyst selected from the group consisting of fine particles of Cu, Cu 2 O, CuO, Cu 2 SO 4 , CuCl 2 , Cu- organometallic compounds and mixtures thereof, in an amount in the range of 0.01 to 3.0% by weight of the said crystallizable glass, said catalyst capable of accelerating the oxidation and removal of said binder during said heating in the oxidizing environment.
Claim 2
Dependent Claim
179 words
In a method of forming a glass-ceramic composite substrate wherein a slurry is prepared which includes sinterable particles of a crystallizable glass, an organic resin binder, and a solvent for the binder, forming the slurry into green ceramic sheets, forming via holes in the sheets, depositing electrically conductive material in the via holes and in line patterns on the surface of the sheets, assembling the sheets, and heating the assembly in an environment to oxidize and remove the resin binder, and subsequently heating the assembly at a higher temperature to fuse the glass particles, the improvement comprising, incorporating a catalyst to accelerate the binder oxidation of said slurry and eliminate carbonaceous binder residue, said catalyst selected from the group consisting of fine particles of Cu, Cu 2 O, CuO, Cu 2 SO 4 , CuCl 2 , Cu- organometallic compounds and mixtures thereof, in an amount in the range of 0.01 to 3.0% by weight of the said crystallizable glass, said catalyst capable of accelerating the oxidation and removal of said binder during said heating in the oxidizing environment.
Claim 3
Dependent Claim
10 words
The method of claim 1 wherein said catalyst is Cu.
Claim 4
Dependent Claim
10 words
The method of claim 1 wherein said catalyst is CuO.
Claim 5
Dependent Claim
12 words
The method of claim 1 wherein said catalyst is Cu 2 O.
Claim 6
Dependent Claim
14 words
The method of claim 1 wherein said catalyst is Cu 2 SO 4 .
Claim 7
Dependent Claim
12 words
The method of claim 1 wherein said catalyst is CuCl 2 .
Claim 8
Dependent Claim
12 words
The method of claim 1 wherein said catalyst is Cu organometallic compounds.
Claim 9
Dependent Claim
12 words
The method of claim 1 wherein said electrically conductive material is Cu.
Claim 10
Dependent Claim
21 words
The method of claim 1 wherein said composite substrate is a multilayer ceramic substrate adapted for use in an electronic package.
Claim 11
Dependent Claim
25 words
The method of claim 1 wherein the initial heating of the assembly is controlled to oxidize the resin binder but not the electrically conductive material.
Claim 12
Dependent Claim
34 words
The method of claim 1 wherein the initial heating of the composite substrate is done in a steam and H2 atmosphere at a temperature less than the melting point of said electrically conductive material.
Claim 13
Dependent Claim
16 words
The method of claim 11 wherein said electrically conductive material is Cu or an alloy thereof.
Claim 14
Dependent Claim
24 words
The method of claim 12 wherein the hydrogen to H 2 O ratio is in the range of 10 -4 to 10 -6 .5.
Claim 15
Dependent Claim
22 words
The method of claim 13 wherein the temperature range of said initial heating is in the range of 720° to 85° C.
Claim 16
Dependent Claim
148 words
In a method of forming a composite substrate wherein a slurry is prepared which includes sinterable particles of a particulate inorganic material, an organic resin binder, and a solvent for the binder, forming the slurry into green sheets, forming via holes in the sheets, depositing electrically conductive material in the via holes and in line patterns on the surface of the sheets, assembling the sheets, and heating the assembly to oxidize and remove the resin binder and to fuse the particles of inorganic material, the improvement comprising, incorporating a catalyst to accelerate the binder oxidation of said slurry and eliminate carbonaceous binder residue, said catalyst selected from the group consisting of fine particles of Cu, Cu 2 O, CuO, Cu 2 SO 4 , CuCl 2 , Cu organometallic compounds and mixtures thereof, said catalyst capable of accelerating the oxidation and removal of said binder during said heating.
Claim 17
Dependent Claim
148 words
In a method of forming a composite substrate wherein a slurry is prepared which includes sinterable particles of a particulate inorganic material, an organic resin binder, and a solvent for the binder, forming the slurry into green sheets, forming via holes in the sheets, depositing electrically conductive material in the via holes and in line patterns on the surface of the sheets, assembling the sheets, and heating the assembly to oxidize and remove the resin binder and to fuse the particles of inorganic material, the improvement comprising, incorporating a catalyst to accelerate the binder oxidation of said slurry and eliminate carbonaceous binder residue, said catalyst selected from the group consisting of fine particles of Cu, Cu 2 O, CuO, Cu 2 SO 4 , CuCl 2 , Cu organometallic compounds and mixtures thereof, said catalyst capable of accelerating the oxidation and removal of said binder during said heating.
Claim 18
Dependent Claim
27 words
The method of claim 15 wherein said catalyst is present in an amount in the range of 0.01 to 3.0% by weight of said particulate organic material.
Claim 19
Dependent Claim
39 words
The method of claim 15 wherein said assembly of sheets is initially heated in an environment to oxidize and remove the resin binder, and subsequently heated at a higher temperature to fuse the particles of said particulate inorganic material.
References Cited (Backward Citations)
US2993815A
Cited
US4104345A
Cited
US4234367A
Cited
US4504339A
Cited
US4547625A
Cited
US4474731A
Cited
US4551357A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-08 | 1990-06-09 | 1990-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-08 | 1994-06-09 | 1994-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-08 | 1998-06-09 | 1998-12-09 | $7700.00 | Window Closed / Lapsed |