US4551357A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process of manufacturing ceramic circuit board
Assignee: NGK Insulators Ltd
•
Filing: 1984-10-16
•
Granted: 1985-11-05
•
Expires: 2004-10-16
Abstract
Abstract A process of manufacturing a ceramic circuit board, wherein at least dielectric ceramics and a conductor paste of base metal are co-fired, comprising the steps of preparing the conductor paste containing an organic material which is thermally decomposed at a temperature higher than a decomposition point of an organic binder contained in the dielectric ceramics, and forming a circuit pattern of the conductor paste containing the organic material. Alternatively, the process comprises the steps of forming the circuit pattern of the conductor paste and covering the formed circuit pattern with the organic material. The process further comprises the steps of thermally decomposing the organic binder in an oxidizing atmosphere at a temperature lower than the decomposition point of the organic material, and thermally decomposing the organic material in an atmosphere having a partial oxygen pressure lower than that of the oxidizing atmosphere.
Inventors
- 👤 Yukihisa Takeuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 12:24
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/63404; C04B35/63408; B; B22; B22F; B22F3/00; B22F3/10; B22F3/1017; B22F3/1021; C04B35/63416; C04B35/63424; C04B35/63432; C04B35/638; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/51; C04B41/5144; C04B41/5188; C04B41/52; C23; C23C; C23C24/00; H; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K3/00; H05K3/10; H05K3/12; H05K3/1283; H05K3/1291; B22F2998/00; H05K2203/00; H05K2203/11; H05K2203/1126
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
112 words
A process for manufacturing a ceramic circuit board, wherein at least dielectric ceramics and a conductor paste of base metal are co-fired, comprising the steps of: preparing said conductor paste of base metal containing an organic material which is thermally decomposed at a temperature higher than a decomposition point of an organic binder contained in said dielectric ceramics; forming a circuit pattern of said conductor paste containing said organic material; thermally decomposing said organic binder in an oxidizing atmosphere at a temperature lower than said decomposition point of said organic material; and thermally decomposing said organic material in an atmosphere having a partial oxygen pressure lower than that of said oxidizing atmosphere.
Claim 2
Dependent Claim
112 words
A process for manufacturing a ceramic circuit board, wherein at least dielectric ceramics and a conductor paste of base metal are co-fired, comprising the steps of: preparing said conductor paste of base metal containing an organic material which is thermally decomposed at a temperature higher than a decomposition point of an organic binder contained in said dielectric ceramics; forming a circuit pattern of said conductor paste containing said organic material; thermally decomposing said organic binder in an oxidizing atmosphere at a temperature lower than said decomposition point of said organic material; and thermally decomposing said organic material in an atmosphere having a partial oxygen pressure lower than that of said oxidizing atmosphere.
Claim 3
Dependent Claim
26 words
A process as claimed in claim 1, wherein said conductor paste of base metal comprises copper and/or nickel as a major component or major components thereof.
Claim 4
Dependent Claim
67 words
A process as claimed in claim 1, wherein said organic binder contained in said dielectric ceramics comprises at least one of organic binders selected from the group consisting of acrylic resins, methacrylic resins, and acrylate-methacrylate copolyer resins, and said organic material contained in said conductor paste comprises at least one of organic materials selected from the group consisting of polystyrene resins, polyethylene resins and ethylene-vinyl acetate copolymers.
Claim 5
Dependent Claim
67 words
A process as claimed in claim 2, wherein said organic binder contained in said dielectric ceramics comprises at least one of organic binders selected from the group consisting of acrylic resins, methacrylic resins, and acrylate-methacrylate copolymer resins, and said organic material contained in said conductor paste comprises at least one of organic materials selected from the group consisting of polystyrene resins, polyethylene resins and ethylene-vinyl acetate copolymers.
Claim 6
Dependent Claim
29 words
A process as claimed in claim 1, wherein said circuit pattern is printed on a green sheet of said dielectric ceramics, with said conductor paste containing said organic material.
Claim 7
Dependent Claim
50 words
A process as claimed in claim 5, wherein said circuit pattern is printed on a plurality of green sheets of said dielectric ceramics, and the green sheets with the printed circuit patterns are laminated to form an unfired laminated sheet structure which is subsequently co-fired into said ceramic circuit board.
Claim 8
Dependent Claim
78 words
A process as claimed in claim 1, wherein a dielectric paste is prepared from said dielectric ceramics, and said dielectric paste and said conductor paste are used to print at least one dielectric layer in a predetermined pattern, and at least one conductor layer in the form of said circuit pattern, respectively, said at least one dielectric layer and said at least one conductor layer being alternately superposed one on another to form an unfired printed laminate structure.
Claim 9
Dependent Claim
34 words
A process as claimed in claim 1, said dielectric ceramics include at least one insulating glass selected from the group consisting of silicate glass, and crystallizable glass which is crystallized through heat treatment thereof.
Claim 10
Dependent Claim
38 words
A process as claimed in claim 8, wherein said silicate glass includes at least one of Al 2 O 3 , B 2 O 3 , MgO, PbO, BaO, ZnO, Li 2 O, CaO and ZrO 2 .
Claim 11
Dependent Claim
106 words
A process as claimed in claim 8, wherein said crystallizable glass is selected from the group consisting of: glass composition consisting essentially of SiO 2 , Al 2 O 3 , CaO, ZnO and TiO 2 ; glass composition consisting essentially of SiO 2 , MgO, BaO, B 2 O 3 and ZnO; glass composition consisting essentially of SiO 2 , Al 2 O 3 , PbO and CaO; glass composition consisting essentially of SiO 2 , Al 2 O 3 , CaO, B 2 O 3 and MgO; and glass composition consisting essentially of SiO 2 , B 2 O 3 , PbO and CaO.
Claim 12
Dependent Claim
24 words
A process as claimed in claim 1, wherein said organic material is contained in said conductor paste in an amount of 1-30% by weight.
Claim 13
Dependent Claim
24 words
A process as claimed in claim 11, wherein said organic material is contained in said conductor paste in an amount of 2-7% by weight.
Claim 14
Dependent Claim
28 words
A process as claimed in claim 1, wherein said organic material is applied in the form of a solution to prepare the conductor paste containing the organic material.
Claim 15
Dependent Claim
17 words
A process as claimed in claim 1, wherein said dielectric ceramics includes at least one inorganic peroxide.
Claim 16
Dependent Claim
13 words
A process as claimed in claim 14, wherein said peroxide is strontium peroxide.
Claim 17
Dependent Claim
109 words
A process of manufacturing a ceramic circuit board, werein at least dielectric ceramics and a conductor paste of base metal are co-fired, comprising the steps of: forming a circuit pattern of said conductor paste of base metal; covering the formed circuit pattern with an organic material which is thermally decomposed at a temperature higher than a decomposition point of an organic binder contained in said dielectric ceramics; thermally decomposing said organic binder in an oxidizing atmosphere at a temperature lower than said decomposition point of said organic material; and thermally decomposing said organic material in an atmosphere having a partial oxygen pressure lower than that of said oxidizing atmosphere.
Claim 18
Dependent Claim
109 words
A process of manufacturing a ceramic circuit board, werein at least dielectric ceramics and a conductor paste of base metal are co-fired, comprising the steps of: forming a circuit pattern of said conductor paste of base metal; covering the formed circuit pattern with an organic material which is thermally decomposed at a temperature higher than a decomposition point of an organic binder contained in said dielectric ceramics; thermally decomposing said organic binder in an oxidizing atmosphere at a temperature lower than said decomposition point of said organic material; and thermally decomposing said organic material in an atmosphere having a partial oxygen pressure lower than that of said oxidizing atmosphere.
Claim 19
Dependent Claim
24 words
A process as claimed in claim 16, wherein said organic material is applied in the form of a solution to cover said circuit pattern.
Claim 20
Dependent Claim
26 words
A process as claimed in claim 16, wherein said conductor paste of base metal comprises copper and/or nickel as a major component or major components thereof.
Claim 21
Dependent Claim
67 words
A process as claimed in claim 16, wherein said organic binder contained in said dielectric ceramics comprises at least one of organic binders selected from the group consisting of acrylic resins, methacrylic resins, and acrylate-methacrylate copolymer resins, and said organic material contained in said conductor paste comprises at least one of organic materials selected from the group consisting of polystyrene resins, polyethylene resins and ethylene-vinyl acetate copolymers.
Claim 22
Dependent Claim
67 words
A process as claimed in claim 17, wherein said organic binder contained in said dielectric ceramics comprises at least one of organic binders selected from the group consisting of acrylic resins, methacrylic resins, and acrylate-methacrylate copolyer resins, and said organic material contained in said conductor paste comprises at least one of organic materials selected from the group consisting of polystyrene resins, polyethylene resins and ethylene-vinyl acetate copolymers.
Claim 23
Dependent Claim
29 words
A process as claimed in claim 16, wherein said circuit pattern is printed on a green sheet of said dielectric ceramics, with said conductor paste containing said organic material.
Claim 24
Dependent Claim
46 words
A process as claimed in claim 21, wherein said circuit pattern is printed on a plurality of green sheets, and the green sheets with the printed circuit patterns are laminated to form an unfired laminated sheet structure which is subsequently co-fired into said ceramic circuit board.
Claim 25
Dependent Claim
78 words
A process as claimed in claim 16, wherein a dielectric paste is prepared from said dielectric ceramics, and said dielectric paste and said conductor paste are used to print at least one dielectric layer in a predetermined pattern, and at least one conductor layer in the form of said circuit pattern, respectively, said at least one dielectric layer and said at least one conductor layer being alternately superposed one on another to form an unfired printed laminate structure.
Claim 26
Dependent Claim
34 words
A process as claimed in claim 16, said dielectric ceramics include at least one insulating glass selected from the group consisting of silicate glass, and crystallizable glass which is crystallized through heat treatment thereof.
Claim 27
Dependent Claim
38 words
A process as claimed in claim 24, wherein said silicate glass includes at least one of Al 2 O 3 , B 2 O 3 , MgO, PbO, BaO, ZnO, Li 2 O, CaO and ZrO 2 .
Claim 28
Dependent Claim
106 words
A process as claimed in claim 24, wherein said crystallizable glass is selected from the group consisting of: glass composition consisting essentially of SiO 2 , Al 2 O 3 , CaO, ZnO and TiO 2 ; glass composition consisting essentially of SiO 2 , MgO, BaO, B 2 O 3 and ZnO; glass composition consisting essentially of SiO 2 , Al 2 O 3 , PbO and CaO; glass composition consisting essentially of SiO 2 , Al 2 O 3 , CaO, B 2 O 3 and MgO; and glass composition consisting essentially of SiO 2 , B 2 O 3 , PbO and CaO.
Claim 29
Dependent Claim
23 words
A process as claimed in claim 16, wherein said organic material is contained in said solution in an amount of 1-30% by weight.
Claim 30
Dependent Claim
23 words
A process as claimed in claim 27, wherein said organic material is contained in said solution in an amount of 2-7% by weight.
Claim 31
Dependent Claim
17 words
A process as claimed in claim 16, wherein said dielectric ceramics includes at least one inorganic peroxide.
Claim 32
Dependent Claim
13 words
A process as claimed in claim 27, wherein said peroxide is strontium peroxide.
References Cited (Backward Citations)
US3661615A
Cited
US4079156A
Cited
US4109377A
Cited
US4341820A
Cited
US4409261A
Cited
US4388347A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-04 | 1989-05-06 | 1989-11-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-04 | 1993-05-06 | 1993-11-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-04 | 1997-05-06 | 1997-11-05 | $7700.00 | Window Closed / Lapsed |