Material for sliding surface bearings
Assignee: Kolbenschmidt AG
•
Filing: 1986-02-06
•
Granted: 1986-11-25
•
Expires: 2006-02-06
Abstract
Abstract A sheet material for sliding surface bearings comprises an expanded metal mesh which consists of a wrought aluminum alloy and is coated with a mixture of polytetrafluoroethylene, filler and glass fibers. The bond strength is increased by coating the surface of the expanded metal mesh with a primer layer.
Inventors
- 👤 Wolfgang Bickle
- 👤 Rolf Pfoh
- 👤 Karl Becker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 11:26
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/20; F16C33/201; F16C33/28; Y; Y10; Y10S; Y10S384/00; Y10S384/90; Y10S384/907; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/29; Y10T428/2982; Y10T428/31504; Y10T428/3154; Y10T428/31544; Y10T442/00; Y10T442/10; Y10T442/102; Y10T442/109; Y10T442/131
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
97 words
A sheet material for sliding surface bearings comprising an expanded metal mesh composed of a wrought aluminum alloy having an elongation at break δ 5 =8 to 20% and a Brinell Hardness Number HB of 35 to 65; a primer layer coating the surface of the expanded metal mesh and having a thickness of 2 to 10 micrometers; and on the primer layer and composed of 10 to 30 wt. % of a filler for improving the thermal conductivity and wear resistance, 10 to 30 wt. % glass fibers and 40 to 80 wt. % polytetrafluoroethylene (PTFE).
Claim 2
Dependent Claim
97 words
A sheet material for sliding surface bearings comprising an expanded metal mesh composed of a wrought aluminum alloy having an elongation at break δ 5 =8 to 20% and a Brinell Hardness Number HB of 35 to 65; a primer layer coating the surface of the expanded metal mesh and having a thickness of 2 to 10 micrometers; and on the primer layer and composed of 10 to 30 wt. % of a filler for improving the thermal conductivity and wear resistance, 10 to 30 wt. % glass fibers and 40 to 80 wt. % polytetrafluoroethylene (PTFE).
Claim 3
Dependent Claim
47 words
The material for sliding surface bearings according to claim 1, wherein the primer layer comprises embedded particles of PTFE, and wherein the coating is sintered and the embedded particles of PTFE are sintered to adjacent PTFE particles of the coating composes of PTFE, filler and glass fibers.
Claim 4
Dependent Claim
45 words
The material for sliding surface bearings according to claim 2, wherein the primer layer comprises of 90 to 110 parts by weight of a PTFE dispersion, 10 to 30 parts by weight of chromium phosphate and 20 to 50 parts by weight of distilled water.
Claim 5
Independent Claim
100 words
A method of making sheet material for sliding surface bearings comprising the steps of providing an expanded metal mesh of a wrought aluminum alloy having an elongation at break δ 5 =8 to 20% and a Brinell Hardness Number HB of 35 to 65; coating the surface of the mesh with a primer layer having a thickness of 2 to 10 micrometers coating the mesh and primer layer with 10 to 30 wt. % of a filler for improving the thermal conductivity and wear resistance, 10 to 30 wt. % glass fibers and 40 to 80 wt. % polytetrafluoroethylene (PTFE).
Claim 6
Independent Claim
100 words
A method of making sheet material for sliding surface bearings comprising the steps of providing an expanded metal mesh of a wrought aluminum alloy having an elongation at break δ 5 =8 to 20% and a Brinell Hardness Number HB of 35 to 65; coating the surface of the mesh with a primer layer having a thickness of 2 to 10 micrometers coating the mesh and primer layer with 10 to 30 wt. % of a filler for improving the thermal conductivity and wear resistance, 10 to 30 wt. % glass fibers and 40 to 80 wt. % polytetrafluoroethylene (PTFE).
Claim 7
Dependent Claim
45 words
The method according to claim 4, wherein the primer layer comprises embedded particles of PTFE, and wherein the steps of coating the primer layer with PTFE, filler and glass fibers includes sintering to sinter adjacent PTFE particles of the primer layer and the coating thereon.
Claim 8
Dependent Claim
82 words
The method according to claim 5, wherein the step of coating with the primer layer comprises providing a mixture of 90 to 110 parts by weight of a PTFE dispersion, 10 to 30 parts by weight of chromium phosphates and 20 to 50 parts by weight of distilled water, and subsequently dried the mixture at a temperature of 230° to 300° C. for 3 to 8 minutes and sintered at a temperature of 380° to 410° C. for 4 to 10 minutes.
References Cited (Backward Citations)
US3950599A
Cited
US4156049A
Cited
JPS541395A
Cited
US4208472A
Cited
US4238137A
Cited
US4439484A
Cited
US4559248A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-24 | 1990-05-26 | 1990-11-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-24 | 1994-05-26 | 1994-11-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-24 | 1998-05-26 | 1998-11-25 | $7700.00 | Window Closed / Lapsed |