Abstract
Abstract In a composite bearing material including a metal strip, a porous sintered metal matrix layer bonded to a surface of said metal strip and a resin composition impregnated into and substantially filling the voids in said porous metal layer and forming a continuous surface layer thereon, the resin composition consists essentially of a blend of 60 to 95 percent by weight of polytetrafluoroethylene and 40 to 5 percent by weight of a copolymer of tetrafluoroethylene and hexafluoropropylene, and mostly all of the copolymer in the composition is included in the surface layer in the form of a fibrillated network.
Inventors
- 👤 Hideo Cho
- 👤 Yukinori Takenoshita
- 👤 Saisuke Sugimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:19
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/20; F16C33/201; F16C33/208; Y; Y10; Y10S; Y10S384/00; Y10S384/90; Y10S384/902; Y10T; Y10T29/00; Y10T29/49; Y10T29/49636; Y10T29/49643; Y10T29/49647; Y10T29/49668; Y10T29/49677; Y10T29/49705; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12042; Y10T428/24; Y10T428/24479; Y10T428/24496; Y10T428/25; Y10T428/254; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/269; Y10T428/31504; Y10T428/3154; Y10T428/31544
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
103 words
In a composite bearing material including a metal strip, a porous sintered metal matrix layer bonded to a surface of said metal strip and a resin composition impregnated into and substantially filling the voids in said porous metal layer and forming a continuous surface layer thereon; the improvement which comprises: said resin composition consists essentially of a blend of 60 to 95 percent by weight of polytetrafluoroethylene and 40 to 5 percent by weight of a copolymer of tetrafluoroethylene and hexafluoropropylene, and mostly all of the copolymer in said composition is included in the surface layer in the form of a fibrillated network.
Claim 2
Dependent Claim
103 words
In a composite bearing material including a metal strip, a porous sintered metal matrix layer bonded to a surface of said metal strip and a resin composition impregnated into and substantially filling the voids in said porous metal layer and forming a continuous surface layer thereon; the improvement which comprises: said resin composition consists essentially of a blend of 60 to 95 percent by weight of polytetrafluoroethylene and 40 to 5 percent by weight of a copolymer of tetrafluoroethylene and hexafluoropropylene, and mostly all of the copolymer in said composition is included in the surface layer in the form of a fibrillated network.
Claim 3
Dependent Claim
42 words
The composite bearing material as recited in claim 1 in which said resin composition consists essentially of a blend of 70 to 90 percent by weight of polytetrafluoroethylene and 30 to 10 percent by weight of a copolymer of tetrafluoroethylene and hexafluoropropylene.
Claim 4
Dependent Claim
39 words
The composite bearing material as recited in claim 1 or 2 in which the continuous surface resin layer formed on the surface of said porous metal layer has a thickness of 10 to 100μ, preferably, of 20 to 50μ.
Claim 5
Dependent Claim
55 words
The composite bearing material as recited in any one of claims 1 to 3 in which said porous metal layer has a thickness of 0.15 to 0.40 mm, preferably, of 0.20 to 0.30 mm and a porosity of more than 10 percent by volume, preferably, of from about 15 to about 40 percent by volume.
Claim 6
Dependent Claim
126 words
In a composite bearing material including a metal strip, a porous sintered metal matrix layer bonded to a surface of said metal strip and a thin resin layer formed by impregnating and pressing a resin composition into the pores of said porous metal layer and followed by sintering the thus pressed resin composition in a heating furnace; the improvement which comprises: said resin composition comprises a uniform blend of 60 to 95 percent by weight of a polytetrafluoroethylene having an average particle size less than the average pore size of the voids in said porous metal layer and complementally therewith 40 to 5 percent by weight of a hexafluoropropylene-tetrafluoroethylene copolymer having an average particle size more than the average pore size in said porous metal layer.
Claim 7
Dependent Claim
126 words
In a composite bearing material including a metal strip, a porous sintered metal matrix layer bonded to a surface of said metal strip and a thin resin layer formed by impregnating and pressing a resin composition into the pores of said porous metal layer and followed by sintering the thus pressed resin composition in a heating furnace; the improvement which comprises: said resin composition comprises a uniform blend of 60 to 95 percent by weight of a polytetrafluoroethylene having an average particle size less than the average pore size of the voids in said porous metal layer and complementally therewith 40 to 5 percent by weight of a hexafluoropropylene-tetrafluoroethylene copolymer having an average particle size more than the average pore size in said porous metal layer.
Claim 8
Dependent Claim
29 words
The composite bearing material as recited in claim 5 in which the average pore size in said metal layer is in the range of about 10 to about 70μ.
Claim 9
Dependent Claim
30 words
The composite bearing material as recited in claim 5 or 6 in which the particle sizes of the copolymer in the blend is in the range of 70 to 150μ.
Claim 10
Dependent Claim
45 words
The composite bearing material as recited in any one of claims 5 to 7 in which said resin composition comprises a umiform blend of 70 to 90 percent by weight of polytetrafluoroethylene and complementally therewith 30 to 10 percent by weight of the hexafluoropropylene-tetrafluoroethylene copolymer.
Claim 11
Dependent Claim
42 words
The composite bearing material as recited in any one of claims 5 to 8 in which the continuous surface resin layer formed on the surface of said porous metal layer has a thickness of 10 to 100μ, preferably of 20 to 50μ.
Claim 12
Dependent Claim
55 words
The composite bearing material as recited in any one of claims 5 to 9 in which said porous metal layer has a thickness of 0.15 to 0.40 mm, preferably, of 0.20 to 0.30 mm and a porosity of more than 10 percent by volume, preferably, of from about 15 to about 40 percent by volume.
Claim 13
Dependent Claim
107 words
The composite bearing material as recited in any one of claims 5 to 10 in which said resin composition consists essentially of a uniform blend of 42 to 78 percent by weight of polytetrafluoroethylene fine powder having an average particle size less than 6μ, 5 to 40 percent by weight of powder of hexafluoropropylene-tetrafluoroethylene copolymer having an average particle size of 70 to 150μ, 10 to 30 percent by weight of aqueous dispersion of colloidal polytetrafluoroethylene (solid content; 35 to 60 percent by weight), 6 to 21 percent by weight of organic solvent, and 1 to 5 percent by weight of anionic and/or non-ionic surface active agent.
Claim 14
Dependent Claim
32 words
The composite bearing material as recited in claim 11 in which said resin composition contains 2 to 3 percent by weight of the surface active agent having more than 12 carbon atoms.
References Cited (Backward Citations)
US2813041A
Cited
US2995462A
Cited
US3136680A
Cited
US3198691A
Cited
US3416941A
Cited
US3419414A
Cited
US4000982A
Cited
US4152474A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-06-17 | 1983-12-17 | 1984-06-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-06-17 | 1987-12-17 | 1988-06-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-06-17 | 1991-12-17 | 1992-06-17 | $7700.00 | Window Closed / Lapsed |