US4620987A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Surface treatment method for magnetic particles
Assignee: Ricoh Co Ltd
•
Filing: 1984-05-25
•
Granted: 1986-11-04
•
Expires: 2004-05-25
Abstract
Abstract A surface treatment method for magnetic particles is disclosed, which comprises the steps of activating magnetic particles by application of heat thereto, treating the surface of the magnetic particles with a reactive silane coupling agent, bringing the treated magnetic particles into contact with at least one polymerizable vinyl-type monomer, polymerizing the monomer to form a polymer, and coating the surface of the magnetic particles with the polymer.
Inventors
- 👤 Hiroshi Yamashita
- 👤 Kenkichi Muto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:07
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/087; G03G9/08784; G03G9/08791; G03G9/083; G03G9/0839; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70647; G11B5/712; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/06; H01F1/061
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
76 words
A surface treatment method for uncoated magnetic particles consisting of magnetic material comprising the steps of activating by heating said uncoated magnetic particles to a temperature of 100° C. to 500° C., treating the surfaces of said magnetic particles with a reactive silane coupling agent, mixing the silane-treated magnetic particles with at least one polymerizable vinyl monomer, polymerizing said monomer to form a polymer, and thereby coating the surfaces of said magnetic particles with said polymer.
Claim 2
Dependent Claim
76 words
A surface treatment method for uncoated magnetic particles consisting of magnetic material comprising the steps of activating by heating said uncoated magnetic particles to a temperature of 100° C. to 500° C., treating the surfaces of said magnetic particles with a reactive silane coupling agent, mixing the silane-treated magnetic particles with at least one polymerizable vinyl monomer, polymerizing said monomer to form a polymer, and thereby coating the surfaces of said magnetic particles with said polymer.
Claim 3
Dependent Claim
102 words
A surface treatment method for magnetic particles as claimed in claim 1, wherein the treating of said magnetic particles with said reactive silane coupling agent is performed by the steps comprising (a) adding said silane coupling agent to an organic solvent, in an amount ranging from 0.1 wt. % to 5 wt. %, based on the weight of said magnetic particles, (b) adjusting the pH of said solution of said silane coupling agent and said organic solvent to a pH at which said silane coupling agent is hydrolyzed, (c) immersing said magnetic particles in said solution, and (d) recovering said magnetic particles.
Claim 4
Dependent Claim
32 words
A surface treatment method for magnetic particles as claimed in claim 2, wherein said recovered magnetic particles are further subjected to heat treatment at temperature ranging from 100° C. to 120° C.
Claim 5
Dependent Claim
37 words
A surface treatment method for magnetic particles as claimed in claim 1, wherein the coating of said magnetic particles with said polymer is performed by vapor-phase polymerization of said monomer in the presence of said magnetic particles.
Claim 6
Dependent Claim
38 words
A surface treatment method for magnetic particles as claimed in claim 1, wherein the coating of said magnetic particles with said polymer is performed by polymerizing said monomer in a solvent in the presence of said magnetic particles.
Claim 7
Dependent Claim
37 words
A surface treatment method for magnetic particles as claimed in claim 1, wherein the coating of said magnetic particles with said polymer is performed by bulk polymerization of said monomer in the presence of said magnetic particles.
Claim 8
Dependent Claim
38 words
A surface treatment method for magnetic particles as claimed in claim 1, wherein said reactive silane coupling agent is selected from the group consisting of: γ-chloropropyltrimethoxysilane, vinyltrichlorosilane, vinyltriethoxysilane, vinyltrimethoxysilane, vinyl.tris(β-methoxyethoxy)silane, γ-methacryloxypropyltrimethoxysilane, β-3,4-epoxycyclohexyl)ethyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, N-β-(aminoethyl)-γ-aminopropyltrimethoxysilane, and γ-ureidopropyltriethoxysilane.
Claim 9
Independent Claim
191 words
A method for treating the surfaces of magnetic particles to improve their dispersibility and their surface affinity with respect to polymerizable monomers, which consists essentially of the steps of: heating magnetic particles to a temperature of from 100° to 500° C. effective to remove adsorbed water from said magnetic particles whereby to activate said magnetic particles, said magnetic particles having a particle size of from about 0.01 to about 1 micrometers and consisting of a magnetic material selected from the group consisting of magnetic metals, magnetic metal alloys, magnetic metal oxides and ferromagnetic materials; then coating said magnetic particles with from 0.1 to 5 wt. %, based on the weight of said magnetic particles, of a reactive silane coupling agent and heating same at 100° to 120° C. whereby to bond said silane coupling agent to the surfaces of said magnetic particles; then mixing said magnetic particles with a polymerizable vinyl monomer component which can be polymerized by radical polymerization and polymerizing said monomer component whereby to form a polymer coating on each of said magnetic particles, which coating is firmly bonded to its magnetic particle by said silane coupling agent.
Claim 10
Independent Claim
191 words
A method for treating the surfaces of magnetic particles to improve their dispersibility and their surface affinity with respect to polymerizable monomers, which consists essentially of the steps of: heating magnetic particles to a temperature of from 100° to 500° C. effective to remove adsorbed water from said magnetic particles whereby to activate said magnetic particles, said magnetic particles having a particle size of from about 0.01 to about 1 micrometers and consisting of a magnetic material selected from the group consisting of magnetic metals, magnetic metal alloys, magnetic metal oxides and ferromagnetic materials; then coating said magnetic particles with from 0.1 to 5 wt. %, based on the weight of said magnetic particles, of a reactive silane coupling agent and heating same at 100° to 120° C. whereby to bond said silane coupling agent to the surfaces of said magnetic particles; then mixing said magnetic particles with a polymerizable vinyl monomer component which can be polymerized by radical polymerization and polymerizing said monomer component whereby to form a polymer coating on each of said magnetic particles, which coating is firmly bonded to its magnetic particle by said silane coupling agent.
References Cited (Backward Citations)
US2876133A
Cited
US3505100A
Cited
US3837892A
Cited
US4264700A
Cited
JPS56121050A
Cited
US4314931A
Cited
JPS57168254A
Cited
JPS587648A
Cited
JPS587646A
Cited
JPS58158650A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-03 | 1990-05-05 | 1990-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-03 | 1994-05-05 | 1994-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-03 | 1998-05-05 | 1998-11-04 | $7700.00 | Window Closed / Lapsed |