Method of manufacturing a layer of an oxide of an element from group IVa
Assignee: US Philips Corp
•
Filing: 1984-08-30
•
Granted: 1986-10-14
•
Expires: 2004-08-30
Abstract
Abstract Providing a transparent layer of an oxide of an element from group IVa of the Periodic Table, notably TiO 2 , by providing a substrate with a solution of a compound of the element which upon heating is converted into the relevant oxide, drying the film and heating the dried film so as to form the transparent layer of the oxide. The oxide thus obtained is a form having a comparatively low refractive index. By heating the product, after providing the film, rapidly to a temperature of above 700° C., preferably above 1,000° C., keeping it at this temperature for some time and then rapidly cooling it again, a modification having a higher refractive index (for example, for TiO 2 rutile) is obtained.
Inventors
- 👤 Jan Haisma
- 👤 Petrus Heller
- 👤 Johannes M. M. Pasmans
- 👤 Udo K. P. Biermann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:41
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; C03C17/256; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/212; C03C2217/22; C03C2217/228; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/111; C03C2218/116; C03C2218/30; C03C2218/32
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
146 words
A method of manufacturing a member consisting of a substrate bearing a transparent layer of an oxide of an element from group IVa of the Periodic Table by providing the substrate with a film of a solution of a compound of the element which upon heating is converted into the relevant oxide, drying the film and heating the dried film so as to form the transparent layer of the oxide, wherein the substrate bearing the dried film is heated to a temperature above 700° C. at a rate of at least 30° C./sec in the range between 300° C. and the temperature above 700° C., is kept at the temperature above 700° C. for at least 45 seconds and is cooled to room temperature at a rate of at least 30° C./sec, at least in the range of the temperature above 700° C. and 300° C.
Claim 2
Independent Claim
146 words
A method of manufacturing a member consisting of a substrate bearing a transparent layer of an oxide of an element from group IVa of the Periodic Table by providing the substrate with a film of a solution of a compound of the element which upon heating is converted into the relevant oxide, drying the film and heating the dried film so as to form the transparent layer of the oxide, wherein the substrate bearing the dried film is heated to a temperature above 700° C. at a rate of at least 30° C./sec in the range between 300° C. and the temperature above 700° C., is kept at the temperature above 700° C. for at least 45 seconds and is cooled to room temperature at a rate of at least 30° C./sec, at least in the range of the temperature above 700° C. and 300° C.
Claim 3
Dependent Claim
90 words
A method as claimed in claim 1, characterized in that after providing the dried film the member is heated to a temperature above 1,000° C. at a rate of at least 30° C./sec at least in the range between 300° C. and the temperature above 1000° C., is kept at the temperature above 1000° C. for at least 45 seconds and is then cooled to room temperature also at a rate of at least 30° C./sec. at least in the range between the temperature above 1000° C. and 300° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-13 | 1990-04-14 | 1990-10-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-13 | 1994-04-14 | 1994-10-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-13 | 1998-04-14 | 1998-10-14 | $7700.00 | Window Closed / Lapsed |