Method of forming an indium phosphide-boron phosphide heterojunction bipolar transistor
Assignee: Honeywell International Inc
•
Filing: 1985-04-15
•
Granted: 1986-09-16
•
Expires: 2005-04-15
Abstract
Abstract A heterojunction bipolar transistor having an n- type epitaxial indium phosphide collector layer grown on a semi-insulating indium phosphide substrate with an n+ buried layer, a p- type indium phosphide base and an epitaxial, n- type boron phosphide wide gap emitter. The p- type base region is formed by ion implantation of magnesium ions into the collector layer. The transistor is applicable to millimeter wave applications due to the high electron mobility in the indium phosphide base. The wide gaps of both the boron phosphide (2.2 eV) and indium phosphide (1.34 eV) permit operation up to 350° C. The transistor is easily processed using metal organic-chemical vapor deposition (MO-CVD) and standard microelectronic techniques.
Inventors
- 👤 Krishna P. Pande
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:25
CPC Classifications
H; H10; H10D; H10D10/00; H10D10/01; H10D10/021; H10D62/00; H10D62/80; H10D62/82; H10D62/824; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2909; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418; Y; Y10; Y10S; Y10S148/00; Y10S148/065; Y10S148/072; Y10S148/076; Y10S148/084; Y10S148/11; Y10S148/119
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
123 words
A method for forming a bipolar heterojunction indium phosphide transistor comprising the steps of: epitaxially growing a buried n+ indium phosphide layer on a selectively etched semi-insulating indium phosphide substrate; epitaxially growing an n- type indium phosphide collector layer over said buried n+ layer; implanting silicon ions into said collector layer to form an n+ collector contact region about the perimeter of said collector layer; implanting metal ions into the central region of said collector layer to form a p- type base region and a p+ base contact region; epitaxially growing an n- type boron phosphide layer over said base region to form an emitter; and epitaxially growing an n+ type boron phosphide layer over said emitter to form an emitter contact region.
Claim 2
Independent Claim
123 words
A method for forming a bipolar heterojunction indium phosphide transistor comprising the steps of: epitaxially growing a buried n+ indium phosphide layer on a selectively etched semi-insulating indium phosphide substrate; epitaxially growing an n- type indium phosphide collector layer over said buried n+ layer; implanting silicon ions into said collector layer to form an n+ collector contact region about the perimeter of said collector layer; implanting metal ions into the central region of said collector layer to form a p- type base region and a p+ base contact region; epitaxially growing an n- type boron phosphide layer over said base region to form an emitter; and epitaxially growing an n+ type boron phosphide layer over said emitter to form an emitter contact region.
Claim 3
Dependent Claim
66 words
The method of claim 1 wherein said steps of growing said n- type and n+ type boron phosphide layers includes the steps of: depositing an insulating layer over said collector layer; etching an opening in said insulator layer exposing a portion of said base region; and epitaxially growing said n- type boron phosphide and n+ boron phosphide layers over said exposed portion of said base region.
Claim 4
Dependent Claim
69 words
The method of claim 2 further including the steps of: etching openings in said insulating layer to expose said collector and base contact regions; and depositing individual metallic electrodes on the surface of said insulating layer and said collector, base, and emitter contact regions, said electrodes electrically isolated from one another and each electrode making electrical contact with a different one of said collector, base and emitter contact regions.
Claim 5
Dependent Claim
39 words
The method of claim 3 wherein said step of depositing electrodes comprises the steps of: thermal evaporating individual gold-germanium-nickel alloy electrodes on said collector and emitter contact regions; and evaporating a gold-zinc-platinum alloy electrode on said base contact regions.
Claim 6
Dependent Claim
40 words
The method of claim 1 wherein said step of growing a buried n+ layer grows said buried n+ layer to a thickness between 1 to 2 micrometers having a carrier concentration of approximately 2 to 5×10 18 cm -3 .
Claim 7
Dependent Claim
52 words
The method of claim 5 wherein said step of growing a buried n+ layer includes the step of chemical vapor depositing said buried n+ layer by reacting phosphine with trietylindium and using sulfer chloride as the dopant source to adjust the carrier concentration to approximately 2 to 5×10 18 cm -3 .
Claim 8
Dependent Claim
41 words
The method of claim 1 wherein said step of growing an n- type collector layer gorws said n- type collector layer to a thickness between 0.5 and 1.0 micrometers and having a carrier concentration of approximately 2×10 15 cm -3 .
Claim 9
Dependent Claim
47 words
The method of claim 7 wherein said step of growing an n- type collector layer includes the step of chemical vapor depositing said n- type collector layer by reacting phosphine with triethylindium and using sulfer chloride to adjust the carrier concentration to 2×10 15 cm -3 .
Claim 10
Dependent Claim
73 words
The method of claim 1 wherein said step of implanting silicon ions to form an n+ collector contact region comprises the steps of: depositing an insulating layer on the surface of said collector layer; etching said insulating layer to expose a surface area defining said collector contact region; and implanting silicon ions in said exposed surface to form said collector contact region having a carrier concentration of approximately 2×10 18 cm -3 .
Claim 11
Dependent Claim
147 words
The method of claim 1 wherein said step of implanting metal ions to form a p- type base region and a p+ base contact region comprises the steps of: depositing an insulating layer on the surface of collector layer; etching said insulating layer to expose a surface area of said collector layer defining said base contact region; implanting said base region and said base contact region with metal ions having sufficient energy to penetrate said insulator layer to form said p- type base region in said collector layer underlying said insulator region having a carrier concentration of approximately 6 to 8×10 17 cm -3 ; and reducing the energy of said implanting ions to a level insufficient to penetrate said insulating layer to form said base contact region having a carrier concentration of greater than 10 18 cm -3 in the exposed portion of said collector layer.
Claim 12
Dependent Claim
18 words
The method of claim 1 wherein said metal ions are selected from a group comprising magnesium and beryllium.
Claim 13
Dependent Claim
32 words
The method of claim 1 further including the step of electrically isolating said transistor by implanting boron ions in the area surrounding said collector, base and emitter regions to render it non-conductive.
Claim 14
Dependent Claim
40 words
The method of claim 1 further including the step of electrically isolating said transistor by etching away the portion of the collector layer and buried n+ layer surrounding said collector, base and emitter regions to produce a mesa type structure.
References Cited (Backward Citations)
US3321682A
Cited
US3877060A
Cited
US3922553A
Cited
US4214926A
Cited
US4220488A
Cited
US4481523A
Cited
JPH109581A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-15 | 1990-03-17 | 1990-09-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-15 | 1994-03-17 | 1994-09-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-15 | 1998-03-17 | 1998-09-16 | $7700.00 | Window Closed / Lapsed |