Process for making molding grade polyethylene terephthalate

Claim 2

An improved process for producing polyethylene terephthalate chip having levels of acetaldehyde content and acetaldehyde generation rate and intrinsic viscosity suitable for molding, said process comprising the steps of: (a) introducing ethylene glycol and terephthalic acid to a reactor in a ratio of from about 1.05 to about 1.35 moles ethylene glycol per mole terephthalic acid and an antimony catalyst in a concentration in the range of from about 325 to about 600 parts antimony per million parts by weight of the product polymer, and heating the resulting mixture at a temperature in the range of about 240° to about 260° C. and a pressure in the range of from about 1 to about 5 atmospheres until said acid is at least about 95 percent esterified to form an esterified monomer mixture; (b) melt polymerizing the antimony-containing esterified monomer mixture of step (a) in at least two stages at progressively higher temperatures in the range of from about 270° to about 285° C. and at a reduced pressure, until it attains an intrinsic viscosity of at least about 0.64 dl/g; (c) extruding the melt of step (b) into a water bath for quenching, then pelletizing the quenched polymer so that the average individual volume chip is in the range of from about 2.3 to about 3.5 mm 3 ; and (d) crystallizing the polymer pellets by heating in air or an inert atmosphere with agitation at a temperature in the range of about 110° to about 160° C. for a time effective to produce a degree of crystallinity in said polymer in the range of from about 10 percent to less than about 30 percent.

Claim 3

A process in accordance with claim 1 wherein the ratio of reactants in step (a) is in the range of from about 1.15 to about 1.25 moles ethylene glycol per mole terephthalic acid.

Claim 4

A process in accordance with claim 1 wherein said antimony catalyst is present in step (a) in an amount in the range of from about 350 to about 450 parts antimony per million parts by weight of said product polymer.

Claim 5

A process in accordance with claim 1 wherein said mixture of step (a) is heated to a temperature in the range of from about 245° to about 255° C., and said pressure is maintained in the range of from about 2 to about 4 atmospheres.

Claim 6

A process in accordance with claim 1 wherein said polymer pellets are crystallized in step (d) to produce a degree of crystallinity in the range of from about 15 to about 25 percent.

Claim 7

A process in accordance with claim 1 wherein the crystallized polymer pellets have levels of residual acetaldehyde of less than about 25 parts per million and an intrinsic viscosity of at least about 0.65 deciliters per gram calculated from measurements made on an 8 weight percent solution in o-chlorophenol at 25° C.

Claim 8

A process in accordance with claim 1 wherein said polymer pellets have a residual acetaldehyde content in the range of from about 15 to about 20 parts per million and an intrinsic viscosity in the range of from about 0.65 to about 0.7 deciliters per gram.

Claim 9

A process in accordance with claim 1 wherein said antimony catalyst is present as elemental antimony or an antimony compound selected from the group consisting of antimony trioxide, antimony oxalate, antimony glucoxide, antimony butoxide, and acetyl antimony dibutoxide.

Claim 10

Crystallized pellets of polyethylene terephthalate prepared in accordance with the process of claim 1.

Claim 11

A process wherein crystallized polyethylene terephthalate chip prepared in accordance with claim 1 is made ready for molding at a molding facility by subjecting the chip to a pre-drying step for a time in the range of from about 1 to about 3 hours at a temperature in the range of from about 145° C. about 165° C. using air having a dew point below about -25° C. flowing at a velocity of about 1 to 2 ft/sec., and then a drying step at a temperature in the range of from about 190° to about 210° C. for a period of time in the range of from about 2 to about 5 hours.

Claim 12

A process in accordance with claim 10 wherein the resulting dried polyethylene terephthalate chip has an acetaldehyde level of less than about 3 parts per million and a rate of generation of acetaldehyde of less than about 4 parts per million per minute, and an intrinsic viscosity of at least about 0.68 deciliters per gram as calculated from measurements made on an 8 weight percent solution in o-chlorophenol at 25° C.

Claim 13

A process for molding a polyethylene terephthalate container from polyethylene terephthalate chip prepared in accordance with the process of claim 10.

Claim 14

Articles molded in accordance with the process of claim 12.

Claim 15

An improved process for producing polyethylene terephthalate suitable for molding, comprising the steps of: (a) esterifying ethylene glycol by heating it in admixture with terephthalic acid and at least about 325 parts antimony catalyst per million parts of the polymer product in a ratio of about 1.05 to about 1.35 moles of said glycol per mole of said acid at a temperature in the range of from about 240° to about 260° C. and a pressure in the range of from about 1 to 5 atmospheres until said acid is at least about 95 percent esterified to form an esterified monomer mixture; (b) melt polymerizing the antimony-containing monomer mixture of step (a) at a temperature in the range of from 270° to 285° C. and at a reduced pressure until it attains an intrinsic viscosity of at least about 0.64; (c) extruding, quenching and pelletizing the melt product of (c) to form chip of an average volume in the range of from about 2.3 to about 3.5 mm 3 ; (d) crystallizing the polymer pellets of (c) by heating with agitation in air or an inert atmosphere at a temperature in the range of from about 110° to about 160° C. to produce a degree of crystallinity within the range of from about 10 to about 25 percent; (e) transporting the pellets to a molding facility; (f) pre-drying said crystallized polymer pellets in the molding facility at a temperature in the range of from about 145° to about 165° C. for a time in the range of about 1 to about 3 hours using air having a dew point below about -25° C. flowing at a velocity of about 1 to 2 ft/sec.; and (g) thereafter drying said polymer pellets in a drier at a temperature in the range of about 180° to about 225° C. for a time in the range of about 2 to about 5 hours using air having a dew point below about -40° C. flowing at a velocity of about 1 to 2 ft/sec., thereby producing a molding resin having a level of residual acetaldehyde less than about 3 parts per million, a generation rate of acetaldehyde less than about 4 parts per million per minute, and an intrinsic viscosity of at least about 0.68 deciliters per gram as calculated from measurements made on an 8 weight percent solution in o-chlorophenol at 25° C.

Claim 16

An improved process for producing polyethylene terephthalate suitable for molding, comprising the steps of: (a) esterifying ethylene glycol by heating it in admixture with terephthalic acid and at least about 325 parts antimony catalyst per million parts of the polymer product in a ratio of about 1.05 to about 1.35 moles of said glycol per mole of said acid at a temperature in the range of from about 240° to about 260° C. and a pressure in the range of from about 1 to 5 atmospheres until said acid is at least about 95 percent esterified to form an esterified monomer mixture; (b) melt polymerizing the antimony-containing monomer mixture of step (a) at a temperature in the range of from 270° to 285° C. and at a reduced pressure until it attains an intrinsic viscosity of at least about 0.64; (c) extruding, quenching and pelletizing the melt product of (c) to form chip of an average volume in the range of from about 2.3 to about 3.5 mm 3 ; (d) crystallizing the polymer pellets of (c) by heating with agitation in air or an inert atmosphere at a temperature in the range of from about 110° to about 160° C. to produce a degree of crystallinity within the range of from about 10 to about 25 percent; (e) transporting the pellets to a molding facility; (f) pre-drying said crystallized polymer pellets in the molding facility at a temperature in the range of from about 145° to about 165° C. for a time in the range of about 1 to about 3 hours using air having a dew point below about -25° C. flowing at a velocity of about 1 to 2 ft/sec.; and (g) thereafter drying said polymer pellets in a drier at a temperature in the range of about 180° to about 225° C. for a time in the range of about 2 to about 5 hours using air having a dew point below about -40° C. flowing at a velocity of about 1 to 2 ft/sec., thereby producing a molding resin having a level of residual acetaldehyde less than about 3 parts per million, a generation rate of acetaldehyde less than about 4 parts per million per minute, and an intrinsic viscosity of at least about 0.68 deciliters per gram as calculated from measurements made on an 8 weight percent solution in o-chlorophenol at 25° C.

Claim 17

A process for molding polyethylene terephthalate comprising the steps of melting a polymer produced by the process of claim 14, forming it into a desired shape, and cooling the molten polymer.