Process for preparing biaxially oriented hollow shaped articles from thermoplastic materials
Assignee: Rhone Poulenc Industries SA
•
Filing: 1980-03-04
•
Granted: 1983-05-24
•
Expires: 2000-03-04
Abstract
Abstract A process for preparing biaxially oriented hollow shaped articles, in particular bottles of thermoplastic material, by biaxial draw- and blow-molding comprises blow-molding a preform and subsequently maintaining the thermoplastic material in close contact with the hot walls of the mold at a temperature which is in the range from about the minimum effective temperature for biaxial orientation of the thermoplastic material to about 40 DEG C. above this temperature for a period of time which is sufficient to partially reduce internal residual stresses in the hollow shaped articles. Following this partial thermo-stabilization, the hollow shaped article preferably is subjected to cooling, whereby the pressure within the article is at least partially maintained or the shaped article is cooled or allowed to shrink and subsequently subjected to a second blow-molding procedure.
Inventors
- 👤 Claude Bonnebat
- 👤 Gilbert Roullet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:07
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/02; B; B29; B29C; B29C49/00; B29C49/18; B29C49/22; B29C49/42; B29C49/64; B29C49/6472; B29C51/00; B29C51/26; B29C51/42; B29C51/426; B29C35/00; B29C35/16; B29C2035/1658; B29C49/78; B29C2049/7879; B29C2949/00; B29C2949/07; B29C2949/081; B29C2949/0811; B29C49/08; B29C49/087; B29C49/6604; B29C49/6605; B29K; B29K2995/00; B29K2995/0012; B29K2995/0017; B29K2995/0037; B29K2995/004; Y; Y10; Y10S; Y10S264/00; Y10S264/90; Y10S264/904; Y10S264/905; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1397
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
269 words
A process for preparing transparent biaxially oriented hollow shaped articles from polyethylene glycol terephthalate by biaxial draw- and blow-molding which comprises the steps of: (a) introducing a thermoplastic material comprising polyethylene glycol terephthalate which is in the shape of a hollow preform into the mold cavity of a mold adapted for blow-molding in the heat; (b) bringing the thermoplastic material to about its temperature of biaxial orientation; (c) bringing the thermoplastic materials into close contact with the walls of the mold by applying an internal pressure to the interior of the hollow preform within the mold cavity by means of a pressure transfer fluid, at least a portion of the material being stretched sufficiently to avoid spherullitic crystallization upon heat treatment; (d) maintaining the thermoplastic material in close contact with the walls of the mold, including those portions of the material which have been stretched sufficiently to avoid spherullitic crystallization upon heat treatment, at a temperature which is suitable for molding and which is in the range from about the minimum effective temperature for biaxial orientation of the thermoplastic material to about 40° C. above the minimum effective temperature for biaxial orientation of the thermoplastic material for a period between about 1 and about 25 seconds to form a partially thermo-stabilized hollow shaped article within the mold, the mold being maintained at a temperature below 130° C., whereby an average temperature of the material of between about 80°-120° C. is reached during the period during which the internal pressure is maintained; (e) allowing the hollow shaped article to cool; and (f) removing the hollow shaped article from the mold.
Claim 2
Dependent Claim
269 words
A process for preparing transparent biaxially oriented hollow shaped articles from polyethylene glycol terephthalate by biaxial draw- and blow-molding which comprises the steps of: (a) introducing a thermoplastic material comprising polyethylene glycol terephthalate which is in the shape of a hollow preform into the mold cavity of a mold adapted for blow-molding in the heat; (b) bringing the thermoplastic material to about its temperature of biaxial orientation; (c) bringing the thermoplastic materials into close contact with the walls of the mold by applying an internal pressure to the interior of the hollow preform within the mold cavity by means of a pressure transfer fluid, at least a portion of the material being stretched sufficiently to avoid spherullitic crystallization upon heat treatment; (d) maintaining the thermoplastic material in close contact with the walls of the mold, including those portions of the material which have been stretched sufficiently to avoid spherullitic crystallization upon heat treatment, at a temperature which is suitable for molding and which is in the range from about the minimum effective temperature for biaxial orientation of the thermoplastic material to about 40° C. above the minimum effective temperature for biaxial orientation of the thermoplastic material for a period between about 1 and about 25 seconds to form a partially thermo-stabilized hollow shaped article within the mold, the mold being maintained at a temperature below 130° C., whereby an average temperature of the material of between about 80°-120° C. is reached during the period during which the internal pressure is maintained; (e) allowing the hollow shaped article to cool; and (f) removing the hollow shaped article from the mold.
Claim 3
Dependent Claim
22 words
The process as defined in claim 1 which comprises the step of cooling the partially thermo-stabilized hollow shaped article within the mold.
Claim 4
Dependent Claim
19 words
The process as defined in claim 2, wherein the internal pressure in the mold is maintained during the cooling.
Claim 5
Dependent Claim
37 words
The process as defined in claim 3, wherein the hollow shaped article is cooled by applying a cold fluid onto the internal walls of the hollow shaped article, while the internal pressure is at least partially maintained.
Claim 6
Dependent Claim
59 words
The process as defined in claim 1, wherein the internal pressure in the interior of the shaped article is at least partially released during the cooling and which further comprises the step of re-applying an internal pressure to the interior of the hollow shaped article in order to bring it into close contact with the walls of a mold.
Claim 7
Dependent Claim
27 words
The process as defined in claim 5, wherein the step of re-applying the internal pressure takes place in a separate mold, the walls of which are cold.
Claim 8
Dependent Claim
20 words
The process as defined in claim 1, wherein the period of contact is between about 1 and about 5 seconds.
Claim 9
Dependent Claim
37 words
The process as defined in claim 1, wherein the hollow shaped article is cooled after removing it from the mold by applying a cold fluid onto its exterior walls, while at least partially maintaining the internal pressure.
Claim 10
Dependent Claim
40 words
The process as defined in claim 1, which comprises the step of, prior to releasing the internal pressure, cooling the hollow shaped article to such a degree that the mean temperature of the material is lowered by about 10°-30° C.
Claim 11
Dependent Claim
62 words
The process as defined in claim 1, which comprises the steps of permitting the material to freely shrink after at least partially evacuating the pressure transfer fluid, reapplying an internal pressure which is sufficient to bring the thermoplastic material in contact with the walls of the mold in the heat, releasing the pressure, and removing the hollow shaped article from the mold.
Claim 12
Dependent Claim
45 words
The process as defined in claim 1, wherein the profile of the temperature of the mold and the distribution of the cooling are adjusted corresponding to at least one of the thickness of the walls of the hollow shaped article and the degree of stretching.
Claim 13
Dependent Claim
19 words
The process as defined in claim 1, wherein the thermoplastic material essentially consists of a homopolymer of ethyleneglycol terephthalate.
Claim 14
Dependent Claim
16 words
The process as defined in claim 1, wherein the thermoplastic material is an ethyleneglycol terephthalate copolymer.
Claim 15
Dependent Claim
44 words
The process as defined in claim 1, which comprises the step of cooling the hollow shaped article after the partially thermo-stabilizing step before finally releasing the internal pressure such that the temperature of the material is lowered by about 10° to about 30° C.
Claim 16
Dependent Claim
15 words
A hollow shaped article which is obtained according to the process defined in claim 1.
Claim 17
Dependent Claim
31 words
The hollow shaped article as defined in claim 15, wherein the drawn portions exhibit a stability at temperatures above 75° C., and which is capable of being filled with hot liquids.
References Cited (Backward Citations)
DE1960129U
Cited
US3733309A
Cited
US3733309B1
Cited
US3888961A
Cited
US3970419A
Cited
US4039641A
Cited
DE2554281A1
Cited
DE2606355A1
Cited
US4233022A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-23 | 1986-11-22 | 1987-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-23 | 1990-11-22 | 1991-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-23 | 1994-11-22 | 1995-05-24 | $7700.00 | Window Closed / Lapsed |