Liquid-phase epitaxial growth method of a IIIb-Vb group compound
Assignee: Mitsubishi Chemical Corp
•
Filing: 1985-01-25
•
Granted: 1986-09-02
•
Expires: 2005-01-25
Abstract
Abstract The reproducibility of Te doping in III-V group compounds is improved by using as the dopant a III-V group compound containing Te at a concentration of at least 1×10 17 cm -3 .
Inventors
- 👤 Yasuji Kohashi
- 👤 Toshio Ishiwatari
- 👤 Hisanori Fujita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 03:16
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/10; C30B29/40; C30B19/00; C30B19/02; C30B19/04; C30B19/10; C30B19/106; C30B29/42; C30B29/44; Y; Y10; Y10S; Y10S438/00; Y10S438/914; Y10S438/925
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
79 words
A method for epitaxially growing a single crystalline film of a Te-doped III-V group inorganic compound consisting of a IIIb group element and a Vb group element of the Periodic Table on a single crystalline substrate by means of liquid-phase epitaxial growth, characterized in that a Te source for doping consists of a single crystalline or polycrystalline III-V compound of said single crystalline film and which contains Te at a concentration of at least 1×10 17 cm -3 .
Claim 2
Independent Claim
79 words
A method for epitaxially growing a single crystalline film of a Te-doped III-V group inorganic compound consisting of a IIIb group element and a Vb group element of the Periodic Table on a single crystalline substrate by means of liquid-phase epitaxial growth, characterized in that a Te source for doping consists of a single crystalline or polycrystalline III-V compound of said single crystalline film and which contains Te at a concentration of at least 1×10 17 cm -3 .
Claim 3
Dependent Claim
52 words
A method according to claim 1, wherein said Te source consists of polycrystalline GaAs containing at least 1×10 17 cm -3 of Te and said III-V group inorganic compound is at least one member selected from the group consisting of GaAs, GaAs 1-x P x (1>x>0), and Ga 1-x Al x As(1>x>0).
Claim 4
Dependent Claim
16 words
A method according to claim 1 or 2, wherein said single crystalline substrate consists of GaAs.
Claim 5
Dependent Claim
47 words
A method according to claim 1, wherein said Te source consists of polycrystalline GaAs containing at least 1×10 17 cm -3 of Te and said III-V group inorganic compound is at least one member selected from the group consisting of GaP and GaAs 1-x P x (1>x>0).
Claim 6
Dependent Claim
14 words
A method according to claim 4, wherein said single crystalline substrate consists of GaP.
Claim 7
Independent Claim
209 words
A method for epitaxially growing a single crystalline film of a Te-doped III-V group inorganic compound which consists of a IIIb group element and a Vb group element of the Periodic Table on a single crystalline substrate by means of liquid-phase epitaxial growth, comprising the steps of: preparing, by means of a boat growth method, a Te source for doping, said Te source consisting of a single crystalline or polycrystalline III-V compound which comprises at least one component of said single crystalline film and which contains Te at a concentration of at least 1×10 17 cm -3 ; preparing a solution for epitaxially growing said III-V group compound; preparing a liquid-phase epitaxial growth apparatus comprising at least one melt reservoir and a holding part of said single crystalline substrate; placing said single crystalline substrate in said holding part of the liquid-phase epitaxial growth apparatus; loading into said melt reservoir said solution and said Te source in a predetermined amount for obtaining an n-type carrier concentration; and cooling, at a predetermined cooling rate, said solution containing said Te source while said solution is in contact with said single crystalline substrate, thereby forming an n-type layer of said III-V group compound having a uniform n-type carrier concentration along a depth thereof.
Claim 8
Independent Claim
209 words
A method for epitaxially growing a single crystalline film of a Te-doped III-V group inorganic compound which consists of a IIIb group element and a Vb group element of the Periodic Table on a single crystalline substrate by means of liquid-phase epitaxial growth, comprising the steps of: preparing, by means of a boat growth method, a Te source for doping, said Te source consisting of a single crystalline or polycrystalline III-V compound which comprises at least one component of said single crystalline film and which contains Te at a concentration of at least 1×10 17 cm -3 ; preparing a solution for epitaxially growing said III-V group compound; preparing a liquid-phase epitaxial growth apparatus comprising at least one melt reservoir and a holding part of said single crystalline substrate; placing said single crystalline substrate in said holding part of the liquid-phase epitaxial growth apparatus; loading into said melt reservoir said solution and said Te source in a predetermined amount for obtaining an n-type carrier concentration; and cooling, at a predetermined cooling rate, said solution containing said Te source while said solution is in contact with said single crystalline substrate, thereby forming an n-type layer of said III-V group compound having a uniform n-type carrier concentration along a depth thereof.
Claim 9
Dependent Claim
43 words
A method according to claim 6, wherein said steps are repeated while maintaining the process conditions, including the predetermined amount of the Te source and the cooling rate, identical, thereby obtaining an n-type carrier concentration which is essentially the same at each repetition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-09-01 | 1990-03-03 | 1990-09-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-09-01 | 1994-03-03 | 1994-09-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-09-01 | 1998-03-03 | 1998-09-02 | $7700.00 | Window Closed / Lapsed |