Palladium metal base dental alloy
Assignee: BAKER DENTAL Corp
•
Filing: 1984-09-12
•
Granted: 1986-08-26
•
Expires: 2004-09-12
Abstract
Abstract A palladium alloy for use in making porcelain jacketed dental restorations having the following composition: 60-85 percent by weight palladium, 5-20 percent by weight copper, 3-15 percent by weight gallium, and a modifier metal selected from gold, indium, ruthenium, tin, nickel and mixtures thereof, the sum of the concentrations of the modifier metal percent in the alloy being greater than 5.5 percent by weight.
Inventors
- 👤 Richard D. Lanam
- 👤 Allen R. Robertson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:09
CPC Classifications
C; C22; C22C; C22C5/00; C22C5/04; A; A61; A61K; A61K6/00; A61K6/80; A61K6/84; A61K6/844
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
114 words
A castable dental alloy composition suitable for bonding with dental porcelain consisting essentially of about 60 to 85 percent by weight palladium, about 5 to 20 percent by weight copper, about 3 to about 15 percent by weight gallium, about 0.5 to about 2 percent by weight gold, about 3.2 to about 6 percent by weight indium, about 0.005 to about 0.02 percent by weight ruthenium, 0 to about 2 percent by weight tin and 0 to about 2 percent by weight nickel, wherein the sum of the concentrations of gold, indium, ruthenium, tin and nickel present in the alloy ranges from greater than 5.5 percent by weight to about 8.5 percent by weight.
Claim 2
Dependent Claim
114 words
A castable dental alloy composition suitable for bonding with dental porcelain consisting essentially of about 60 to 85 percent by weight palladium, about 5 to 20 percent by weight copper, about 3 to about 15 percent by weight gallium, about 0.5 to about 2 percent by weight gold, about 3.2 to about 6 percent by weight indium, about 0.005 to about 0.02 percent by weight ruthenium, 0 to about 2 percent by weight tin and 0 to about 2 percent by weight nickel, wherein the sum of the concentrations of gold, indium, ruthenium, tin and nickel present in the alloy ranges from greater than 5.5 percent by weight to about 8.5 percent by weight.
Claim 3
Dependent Claim
27 words
The alloy defined in claim 1 formed as a cast body for use as a dental prosthesis and further comprising a porcelain jacket fired on the body.
Claim 4
Dependent Claim
104 words
A dental composition consisting essentially of about 70 to about 80 percent by weightt palladium, about 8 to 12 percent by weight copper, about 5 to 9 percent by weight gallium, about 1.5 to 1.9 percent by weight gold, about 4.5 to about 5.5 percent by weight indium, 0 to about 2 weight percent tin, 0 to about 2 percent by weight nickel and about 0.006 to about 0.012 percent by weight ruthenium, the sum of the concentrations of gold, indium, ruthenium, tin and nickel present in the alloy composition ranging from greater than 5.5 percent by weight to about 8.5 percent by weight.
Claim 5
Dependent Claim
104 words
A dental composition consisting essentially of about 70 to about 80 percent by weightt palladium, about 8 to 12 percent by weight copper, about 5 to 9 percent by weight gallium, about 1.5 to 1.9 percent by weight gold, about 4.5 to about 5.5 percent by weight indium, 0 to about 2 weight percent tin, 0 to about 2 percent by weight nickel and about 0.006 to about 0.012 percent by weight ruthenium, the sum of the concentrations of gold, indium, ruthenium, tin and nickel present in the alloy composition ranging from greater than 5.5 percent by weight to about 8.5 percent by weight.
Claim 6
Dependent Claim
27 words
The alloy defined in claim 3, formed as a cast body for use as a dental prosthesis and further comprising a porcelain jacket fired on the body.
Claim 7
Dependent Claim
27 words
The alloy defined in claim 4 formed as a cast body for use as a dental prosthesis and further comprising a porcelain jacket fired on the body.
Claim 8
Dependent Claim
107 words
A dental alloy composition consisting essentially of about 70 to about 80 percent by weight palladium, about 8 to about 12 percent by weight copper, about 5 to about 9 percent by weight gallium, about 0.5 to about 2 percent by weight gold, about 3.2 to about 6 percent by weight indium, 0 to about 2 percent by weight tin, 0 to about 2 percent by weight nickel, and about 0.005 to about 0.02 percent by weight ruthenium, wherein the sum of the concentrations of gold, indium and ruthenium in the alloy composition ranges from greater than 5.5 percent by weight to about 8.5 percent by weight.
Claim 9
Dependent Claim
107 words
A dental alloy composition consisting essentially of about 70 to about 80 percent by weight palladium, about 8 to about 12 percent by weight copper, about 5 to about 9 percent by weight gallium, about 0.5 to about 2 percent by weight gold, about 3.2 to about 6 percent by weight indium, 0 to about 2 percent by weight tin, 0 to about 2 percent by weight nickel, and about 0.005 to about 0.02 percent by weight ruthenium, wherein the sum of the concentrations of gold, indium and ruthenium in the alloy composition ranges from greater than 5.5 percent by weight to about 8.5 percent by weight.
References Cited (Backward Citations)
US4387072A
Cited
US4419325A
Cited
US4451639A
Cited
US4400350A
Cited
DE3247398A1
Cited
US4551302A
Cited
US4518564A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-25 | 1990-02-24 | 1990-08-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-25 | 1994-02-24 | 1994-08-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-25 | 1998-02-24 | 1998-08-26 | $7700.00 | Window Closed / Lapsed |