Process for producing alpha-olefin polymers
Assignee: JNC Corp
•
Filing: 1983-04-29
•
Granted: 1986-07-29
•
Expires: 2003-04-29
Abstract
Abstract A process for producing α-olefin polymers is proposed wherein the catalyst prepared and used therein is superior in the shelf stability and heat stability. The process comprises reacting TiCl 4 with a reaction product (I) of an organoaluminum compound with an electron donor to obtain a solid product (II), which is then subjected to polymerization treatment with an α-olefin, and further reacted with an electron donor and an electron acceptor to obtain a solid product (III), which is then combined with an organoaluminum compound, to obtain a catalyst, in the presence of which α-olefin(s) are polymerized. The catalyst can be further preactivated with an α-olefin in advance of its use for the polymerization.
Inventors
- 👤 Akihiro Sato
- 👤 Toshihiro Uwai
- 👤 Masami Tachibana
- 👤 Kenji Matsuda
- 👤 Yoshiharu Higuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:22
CPC Classifications
C; C08; C08F; C08F10/00; Y; Y10; Y10S; Y10S526/00; Y10S526/903; Y10S526/904
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
149 words
A process for producing polymers which comprises polymerizing at least one mono-alpha-olefin selected from the group consisting of ethylene, propylene, butene-1, hexene-1 and heptene-1 or styrene, or a mixture thereof, in the presence of a catalyst obtained by reacting a reaction product (I) of at least one organoaluminum compound, selected from the group consisting of trialkylaluminums and dialkylaluminum monohalides with an ether, with TiCl 4 in a molar ratio of said organoaluminum compound used in the preparation of said reaction product (I) to TiCl 4 of 0.06 to 0.3, to form a solid product (II), and during this reaction or after completion of the reaction, subjecting the solid product (II) to a polymerization treatment with a mono-alpha-olefin or styrene; further reacting the thus treated solid products (II) with an ether and TiCl 4 to obtain a solid product (III); and combining this solid product (III) with an organoaluminum compound.
Claim 2
Dependent Claim
149 words
A process for producing polymers which comprises polymerizing at least one mono-alpha-olefin selected from the group consisting of ethylene, propylene, butene-1, hexene-1 and heptene-1 or styrene, or a mixture thereof, in the presence of a catalyst obtained by reacting a reaction product (I) of at least one organoaluminum compound, selected from the group consisting of trialkylaluminums and dialkylaluminum monohalides with an ether, with TiCl 4 in a molar ratio of said organoaluminum compound used in the preparation of said reaction product (I) to TiCl 4 of 0.06 to 0.3, to form a solid product (II), and during this reaction or after completion of the reaction, subjecting the solid product (II) to a polymerization treatment with a mono-alpha-olefin or styrene; further reacting the thus treated solid products (II) with an ether and TiCl 4 to obtain a solid product (III); and combining this solid product (III) with an organoaluminum compound.
Claim 3
Dependent Claim
212 words
A process according to claim 1 which comprises the steps of (a) reacting one mol of an organoaluminum compound with 1 to 4 mols of an ether in a solvent at a temperature of -20° to 200° C., to obtain a reaction product (I); (b) reacting this reaction product (I) with TiCl 4 at a temperature of 0° to 200° C. in a ratio of the number of Al atoms to that of Ti atoms of 0.06 to 0.3 to form a solid product (II), and during this reaction step or after completion of the reaction, subjecting the solid product (II) to a polymerization treatment of contacting the product (II) with 10 to 5,000 g of an alpha-olefin based on 100 g of the solid product (II), under polymerizable conditions, to obtain a solid product (II) subjected to the polymerization treatment; (c) reacting 100 g of this solid product (II) subjected to the polymerization treatment, with 50 to 200 g of an ether electron donor and 20 to 500 g of TiCl 4 at a temperature of 40° to 200° C., to obtain a solid product (III); and (d) polymerizing an alpha-olefin or alpha-olefins in the presence of a catalyst comprising a combination of said solid product (III) with an organoaluminum compound.
Claim 4
Dependent Claim
67 words
A process according to claim 1 wherein during the reaction step of the reaction product (I) with TiCl 4 or after completion of the reaction, said polymerization treament is carried out by passing the mono-alpha-olefin or styrene under the atmospheric pressure or adding it so as to give a pressure of 10 kg/cm 2 G or lower, and at a reaction temperature of 30° to 90° C.
Claim 5
Dependent Claim
72 words
A process according to claim 1 wherein after completion of the reaction of the reaction product (I) with TiCl 4 , said polymerization treatment is carried out by removing the resulting liquid portion, suspending the resulting solid product (II) in a solvent to form a suspension, and adding an organoaluminum compound and a mono-alpha-olefin or styrene under 0 to 10 kg/cm 2 G to the suspension to polymerize the mono-alpha-olefin or styrene.
Claim 6
Dependent Claim
61 words
A process according to claim 4 wherein the amounts of said organoaluminum compound and the added mono-alpha-olefin or styrene is in the range of 5 to 500 g and in the range of 10 to 5,000 g, respectively, each based on 100 g of the solid product (II), and the reaction temperature is in the range of 30° to 90° C.
Claim 7
Dependent Claim
33 words
A process according to claim 2 wherein the reaction product (I) in the form of liquid, obtained by reacting an organoaluminum with an ether is used, as it is, in the subsequent reaction.
Claim 8
Dependent Claim
16 words
A process according to claim 1 wherein said polymerization is carried out by gas phase polymerization.
Claim 9
Dependent Claim
20 words
A process according to claim 1 wherein said polymerization is carried out by slurry polymerization followed by gas phase polymerization.
Claim 10
Dependent Claim
56 words
A process according to claim 1 wherein said organoaluminum compound is expressed by the general formula AlR n R' n ,X 3- (n+n') wherein R and R' each represent alkyl, aryl, alkaryl, cycloalkyl or alkoxy group; X represents fluorine, chlorine, bromine or iodine; and n and n' each represent a number satisfying a relationship of 0<n+n'≦3.
Claim 11
Dependent Claim
20 words
A process according to claim 1 wherein said polymerization is carried out by bulk polymerization followed by gas phase polymerization.
Claim 12
Dependent Claim
13 words
A process according to claim 2 wherein said solvent is an aliphatic hydrocarbon.
Claim 13
Dependent Claim
27 words
A process according to claim 1 wherein said reaction of said solid product (II) with an ether and TiCl 4 is carried out in an aliphatic hydrocarbon.
Claim 14
Dependent Claim
63 words
A process according to claim 1 wherein said reaction of said product (II) with an ether and TiCl 4 is carried out by reacting said ether with TiCl 4 in advance at a temperature of 10° to 100° C. for a time of 30 minutes to 2 hours; cooling the resulting reaction product; and reacting this reaction product with said solid product (II).
Claim 15
Dependent Claim
38 words
A process according to claim 1 wherein said catalyst is preactivated by further reacting an alpha-olefin with said combination of the solid product (III) with an organoaluminum compound and the resulting preactivated catalyst is used for alpha-olefin polymerization.
Claim 16
Dependent Claim
84 words
A process according to claim 14 wherein the preactivation is carried out by using 0.1 to 500 g of an organoaluminum compound, 0 to 50 l of a solvent, 0 to 1,000 ml of hydrogen and 0.05 to 5,000 g of an alpha-olefin, each based on 1 g of the solid product (III), and reacting said alpha-olefin at a temperature of 0° to 100° C. to form 0.01 to 2,000 g of said alpha-olefin reacted, based on 1 g of the solid product (III).
References Cited (Backward Citations)
JPS5512875A
Cited
US4295991A
Cited
US4368304A
Cited
US4309521A
Cited
US4420593A
Cited
US4460757A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-28 | 1990-01-27 | 1990-07-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-28 | 1994-01-27 | 1994-07-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-28 | 1998-01-27 | 1998-07-29 | $7700.00 | Window Closed / Lapsed |