Method of manufacturing MIS capacitors for semiconductor IC devices
Assignee: Oki Electric Industry Co Ltd
•
Filing: 1985-01-15
•
Granted: 1986-07-29
•
Expires: 2005-01-15
Abstract
Abstract A method of manufacturing MIS capacitors for semiconductor IC devices, which have a three-ply dielectric layer formed of a first oxide film, a nitride film, and a second oxide film, thereby having high dielectric constants, stable electric characteristics, and high dielectric strength. First, the first oxide film is formed on a semiconductor substrate, on which film is then formed the nitride film, followed by thermal treatment of the nitride film in an oxiding atmosphere to form the thin second oxide film on the nitride film, to obtain the three-ply dielectric layer. The dielectric layer is further thermally treated in an inert gas atmosphere to eliminate a boundary level, etc. developed between the nitride film and the second oxide film at the time of formation of the second oxide film, for electrical stability of the dielectric layer.
Inventors
- 👤 Fumio Kiyosumi
- 👤 Masayoshi Ino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:37
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10D; H10D1/00; H10D1/60; H10D1/62; H10D1/66; H10D84/00; H10D84/01
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
132 words
A method of manufacturing a MIS capacitor for use in a dynamic MOS memory IC device, comprising the steps of: (1) forming a thermally-grown silicon oxide on a silicon substrate; (2) forming a silicon nitride film on said silicon oxide film by chemical vapor deposition; (3) forming a thin silicon oxide film on said silicon nitride film by heating said silicon nitride film in an oxidizing atmosphere, to provide on to said silicon substrate a laminated dielectric layer comprising sequentially said silicon oxide film, said silicon nitride film and said thin silicon oxide film; (4) thermally treating said silicon substrate having said laminated dielectric layer in an inert gas atmosphere at a high temperature; and (5) forming a conductive film as a capacitor plate on the surface of said laminated dielectric layer.
Claim 2
Independent Claim
132 words
A method of manufacturing a MIS capacitor for use in a dynamic MOS memory IC device, comprising the steps of: (1) forming a thermally-grown silicon oxide on a silicon substrate; (2) forming a silicon nitride film on said silicon oxide film by chemical vapor deposition; (3) forming a thin silicon oxide film on said silicon nitride film by heating said silicon nitride film in an oxidizing atmosphere, to provide on to said silicon substrate a laminated dielectric layer comprising sequentially said silicon oxide film, said silicon nitride film and said thin silicon oxide film; (4) thermally treating said silicon substrate having said laminated dielectric layer in an inert gas atmosphere at a high temperature; and (5) forming a conductive film as a capacitor plate on the surface of said laminated dielectric layer.
Claim 3
Dependent Claim
53 words
The method of claim 1, wherein said first silicon oxide film is 50 to 500 Å thick, and said step (1) is carried out in a dry oxygen atmosphere at about 1000° C. for 20 to 50 minutes, or in a wet oxygen atmosphere at about 800° C. for 5 to 50 minutes.
Claim 4
Dependent Claim
46 words
The method of claim 1, wherein said silicon nitride film is 50 to 500 Å thick, and said step (2) is carried out by deposition from a gaseous mixture of dichlorosilane and ammonia at a temperature of 700° to 800° C. for 5 to 50 minutes.
Claim 5
Dependent Claim
51 words
The method of claim 1, wherein said thin silicon oxide film is 20 to 50 Å thick, and said step (3) is carried out in a dry oxygen atmosphere at 900° C. for 30 to 100 minutes, or in a wet oxygen atmosphere at 950° C. for 20 to 60 minutes.
Claim 6
Dependent Claim
39 words
The method of claim 1, wherein said step (4) is carried out in an inert gas selected from the group consisting of N 2 , Ar, and H 2 at 900° to 1000° C. for 10 to 120 minutes.
Claim 7
Dependent Claim
39 words
The method of claim 1, wherein said first silicon oxide film is 50 to 500 < thick, said silicon nitride film is 50 to 500 Å thick and said thin silicon oxide film is 20 to 50 Å thick.
Claim 8
Dependent Claim
39 words
The method of claim 6, wherein said step (4) is carried out in an inert gas selected from the group consisting of N 2 , Ar, and H 2 at 900° to 1000° C. for 10 to 120 minutes.
Claim 9
Dependent Claim
104 words
The method of claim 7, wherein said step (1) is carried out in a dry oxygen atmosphere at about 1000° C. for 20 to 50 minutes, or in a wet oxygen atmosphere at about 800° C. for 5 to 50 minutes; said step (2) is carried out by deposition from a gaseous mixture of dichlorosilane and ammonia at a temperature of 700° to 800° C. for 5 to 50 minutes and said step (3) is carried out in a dry oxygen atmosphere at 900° C. for 30 to 100 minutes, or in a wet oxygen atmosphere at 950° C. for 20 to 60 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-07-28 | 1990-01-27 | 1990-07-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-07-28 | 1994-01-27 | 1994-07-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-07-28 | 1998-01-27 | 1998-07-29 | $7700.00 | Window Closed / Lapsed |